Preparation method of liquid propyl silicon resin blend for personal care

The technology of a blend and propyl triethoxy silane is applied in the directions of skin care preparations, hair care, cosmetic preparations, etc. The effect of avoiding pollution, preventing skin aging, and increasing process costs

Pending Publication Date: 2022-05-27
陈才虎
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the preparation of silicone resin with chlorosilane as raw material will produce a large amount of hydrochloric acid (HCl), which will corrode the production equipment and have certain harm to the environment. The waste water produced also needs special treatment, which further increases the production cost of the process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of liquid propyl silicon resin blend for personal care
  • Preparation method of liquid propyl silicon resin blend for personal care
  • Preparation method of liquid propyl silicon resin blend for personal care

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A preparation method of liquid propyl silicone resin blend for personal care, the steps are:

[0039]At room temperature, add 11.66 mol of deionized water, 7.49 mol of cyclohexane, and 1.52 mol of absolute ethanol into a three-port reactor equipped with a thermometer, turn on mechanical stirring, and stir until the mixture is evenly mixed; Add 3 mol of oxysilane into the container, continue to stir, then add 0.056 mol of trifluoromethanesulfonic acid dropwise, set the stirring speed to 280 rpm, turn on the circulating water, heat to 60 ° C, and react under this condition for 50 min; continue to heat up to 85 ° C , continue to react for 6h after the solvent is evaporated, wash with a large amount of deionized water after the reaction, until the washing solution PH>5 (measured by a pH meter), separate liquid, after short-path distillation (120 ~ 160 ℃, 9 ~ 20Pa) That is, the propyl silicone resin (285.4 g) is obtained, and the resin viscosity can reach 20000 mPas (25° C.)...

Embodiment 2

[0044] A preparation method of liquid propyl silicone resin blend for personal care, the steps are:

[0045] At room temperature, add 11.66 mol of deionized water, 7.49 mol of cyclohexane, and 1.52 mol of absolute ethanol into a three-port reactor equipped with a thermometer, turn on mechanical stirring, and stir until the mixture is evenly mixed; Add 3 mol of oxysilane into the container, continue to stir, then add 0.056 mol of trifluoromethanesulfonic acid dropwise, set the stirring speed to 280 rpm, turn on the circulating water, heat to 60 ° C, and react under this condition for 50 min; continue to heat up to 85 ° C , continue to react for 6h after the solvent is evaporated, wash with a large amount of deionized water after the reaction, until the washing solution PH>5 (measured by a pH meter), separate liquid, after short-path distillation (120 ~ 160 ℃, 9 ~ 20Pa) That is, a propyl silicone resin (283.2 g) is obtained, and the resin viscosity can reach 20,000 mPas (25° C.)...

Embodiment 3

[0048] A preparation method of liquid propyl silicone resin blend for personal care, the steps are:

[0049] At room temperature, add 11.66 mol of deionized water, 7.49 mol of toluene, and 1.52 mol of absolute ethanol into a three-port reactor equipped with a thermometer, turn on mechanical stirring, and stir until the mixture is mixed; Add 3 mol of silane into the container, continue to stir, then add 0.064 mol of trifluoromethanesulfonic acid dropwise, set the stirring speed to 275 rpm, turn on the circulating water, heat to 55 ° C, and react under this condition for 40 min; continue to heat up to 85 ° C, wait for After the solvent is evaporated, the reaction is continued for 6 hours. After the reaction is completed, it is washed with a large amount of deionized water until the pH of the washing solution is > 5 (measured by a pH meter), and the liquid is separated. The propyl silicone resin (283.9g) was obtained, the resin viscosity could reach 22000mPas (25°C), the refracti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a liquid propyl silicone resin blend for personal care. The propyl silicon resin provided by the invention is prepared by the following method: carrying out hydrolytic polymerization reaction on n-propyltriethoxysilane serving as a raw material in the presence of water, an organic solvent and an acid catalyst, thereby obtaining the propyl silicon resin. The propyl silicon resin developed and produced by the invention has the excellent characteristics of high viscosity, good thermal stability, water resistance, moisture resistance and the like, and is environment-friendly and non-toxic. The film formed by the resin is still smooth and intact even after being stretched and washed. Propyl groups on a silane chain can be freely bent and rotated and can be blended with D5 or flexible paraffin, so that the product can be endowed with better lubricity, elasticity and flexibility. Besides, the production and emission of highly corrosive and toxic substances in the production process can be reduced by utilizing the process route, the production cost is reduced by recycling the recovered solvent, and the pollution to the environment is avoided.

Description

technical field [0001] The invention belongs to the field of preparation of cosmetic intermediates, in particular to a preparation method of a liquid propyl silicone resin blend for personal care. Background technique [0002] Heart of beauty in everyone. Today's society is an era of "looking at face", people pay more attention to their own appearance, and believe that "face value is justice", thus giving birth to the "face value economy". The arrival of the "face value economy" also means the awakening of consumers' awareness of skin care. The society's ability to accept cosmetics has improved, and the "appearance economy" has exploded, especially the audience of skin care products has become wider and wider, which has brought more market opportunities to my country's cosmetics market. At present, the United States, Japan and South Korea occupy most of the global cosmetics market share, while the Chinese market accounts for no more than 50%. Although the market size of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G77/06A61K8/891A61Q1/00A61Q5/00A61Q17/00A61Q17/04A61Q19/08
CPCC08G77/06A61K8/891A61Q19/08A61Q17/00A61Q1/00A61Q17/04A61Q5/00
Inventor 陈才虎蒲阳周鹏刘敏文全东任沂杨梅
Owner 陈才虎
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com