Non-crimping polyester monofilament and process for producing same

A single fiber and polyester single technology, applied in the field of polyester single fiber, can solve the problems of reducing physical properties and functions, reducing single fiber inhibition, low compatibility, etc.

Inactive Publication Date: 2001-11-07
TEIJIN LTD
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the thickness of the sheath portion of the monofilament is too small, the core of the monofilament is partially exposed, and at the same time, since the compatibility between the polyester copolymer of the sheath portion and the polyester homopolymer of the core is low, Therefore, at the interface between the two, the separation of the shell part from the core part is unavoidable
This phenomenon reduces the scum suppression of the individual fibers and reduces their physical properties and functionality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-crimping polyester monofilament and process for producing same
  • Non-crimping polyester monofilament and process for producing same
  • Non-crimping polyester monofilament and process for producing same

Examples

Experimental program
Comparison scheme
Effect test

reference example 1

[0120] As shown in Table 1, polyester (polyethylene terephthalate) resin is heat-treated in a nitrogen environment (oxygen-free environment) at 280-300°C for 5-15 minutes, and each heated sample is Intrinsic viscosity measurement. Table 1 shows the reduction in intrinsic viscosity under each heat treatment condition.

[0121] Table 1

[0122] Table 1 shows that the higher the heating temperature and the longer the heating time, the greater the decrease in the intrinsic viscosity of the polyester resin. That is to say, the decrease in intrinsic viscosity after heat treatment at 300°C for 10 minutes is 0.071 larger than the decrease in intrinsic viscosity at 280°C for 5 minutes.

[0123] When the polyester resin heat-treated at 300°C for 10 minutes is melted and sprayed at a coiling speed of 1200m / min at an extrusion speed of 4.27g / min, and the unstretched finished product is drawn at a stretch ratio of 3.8 In the case of filaments, the ultimate elo...

reference example 2

[0128] A polyethylene terephthalate resin having an intrinsic viscosity [η] of 0.90 was melted in a melt extruder, and the melting temperature of the resin was controlled at 290°C. The melt was passed through a heating box heated to 300° C. with a heating medium, and then extruded through a metering gear pump at 0.3 ml / rev (milliliter / rev). The measured temperature of the melt extruded through the metering pump was 300°C. During the melting of the above melt and the extrusion of the gear pump, the extrusion rate of the gear pump is shown in Table 2, and the intrinsic viscosity of the extruded molten sample was measured. Its measured values ​​are shown in Table 2,

[0129] No.

[0130] Table 2 shows that: the greater the extrusion speed of the gear pump, the shorter the residence time of the melt in the gear pump, the higher the intrinsic viscosity of the extruded melt, and the lower the intrinsic viscosity of the extruded melt The smaller the amount. The absolute ...

example 1

[0135]The polyethylene terephthalate resin with an intrinsic viscosity of 0.8 is melted at 300°C, and enters through the metering gear pump 14 at a speed of 5ml / min. Figure 3(a) and 3(b) The melt spinneret shown. Figure 3(a) and 3(b) The melt spinneret 12 shown has a total internal volume of 12 ml, the central channel 16 of the distribution disc 18 has a diameter of 5 mm, and 24 peripheral channels 17 are arranged concentrically around the central channel 16 . The diameters of the surrounding channels are shown in Table 4. The mixed flow in the melt chamber 19 was extruded through the melt orifice 23 at an extrusion speed of 5 ml / min. The extruded single fiber flow passed through a heating zone with a temperature of 350° C. and a length of 100 mm, and then was cooled and solidified under the operation of pulling out and coiling at a speed of 1000 m / min. The undrawn finished monofilament enters heated drawing rolls heated to 100°C and 140°C respectively, and is stretched ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
widthaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

A non-crimping polyester monofilament having an excellent resistance to abrasion and satisfactory mechanical strength and modulus has an intrinsic viscosity distribution such that the farther the location of a part of the monofilament from the longitudinal axis of the monofilament, the lower the intrinsic viscosity of a portion of polyester resin located in the part of the monofilament, wherein a peripheral part of the monofilament formed from a portion of the polyester resin having a lowest average intrinsic viscosity of 0.6 to 1.1 and concentrically surrounds a center part of the monofilament formed from another portion of the polyester resin having a highest average intrinsic viscosity, and the intrinsic viscosities the polyester resin portions for the peripheral and center parts of the monofilament is controlled by controlling the heat history of each of the portions of the polyester resin in a melt spinneret for producing the monofilament.

Description

technical field [0001] The present invention relates to a non-crimped polyester monofilament and a method for producing such a monofilament. In particular, the present invention relates to a non-crimped polyester monofilament which has a high surface property and can be used as a material monofilament, for example, as a rope, net, artificial gut, tarpaulin, tent, wire mesh, Material for gliding parachutes and canvas, and used to produce mesh fabrics for screen printing, especially, in the production of printed circuit boards, for the production of high mesh and high modulus required for high-precision screen printing Plain gaze. Background technique [0002] Polyester monofilament may be called "single fiber" or "raw material thread", which is widely used in the fields of clothing and industrial raw materials. In particular, in the field of industrial raw materials, polyester monofilaments are used as raw material threads for tire cords, ropes, nets, guts, oilcloths, tents...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01D5/34D01F6/62D01F8/14H05K3/12
CPCD01F6/62D01F8/14D01D5/34H05K3/1225Y10T428/2913Y10T428/2969
Inventor 赤松哲也田代智秋
Owner TEIJIN LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap