Water-dispersed resin and paint for automobile coating

A dispersive, resin-based technology, applied in coatings, polyester coatings, latex paints, etc., can solve the problems of molecular weight limitation, low water resistance of coating films, poor water dispersibility, etc., to overcome the decline of water resistance and poor water dispersibility , Excellent impact resistance effect

Inactive Publication Date: 2002-07-10
CNOOC CHANGZHOU PAINT & COATINGS IND RES INST
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The method of dispersing this resin in water includes: adopting the method of adding an emulsifier, but this will lead to low water resistance of the coating film; it is also possible to make the polyester resin Emulsification in water, however, this emulsification effect is limited, so that the molecular weight of the polyester resin is limited, the molecular weight is too large, the water dispersibility is poor, affecting the storage stability of the coating; the molecular weight is too small, although it can be stably dispersed in water, but the coating Membrane flexibility is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] The first step to synthesize resin A 1 and resin B 1 , and the formulations of the resins are listed in Table 1.

[0012] raw material name

Resin A 1

Resin A 2

Resin B 1

Resin B 2

Polyol

Neopentyl glycol

Trimethylolpropane

Neopentyl Glycol Hydroxypivalate

1,4 cyclohexyl dimethanol

Glycidyl tertiary carbonate

Polyether 204

13.5

26.1

55.2

13.6

-

-

27.0

14.3

10.2

11.8

8.8

-

16.1

33.2

122.4

21.6

-

-

43.0

20.1

29.5

20.0

-

40.0

Polyacid

Isophthalic acid

tetrahydrophthalic anhydride

Adipic acid

trimellitic anhydride

41.9

24.0

32.3

12.1

27.6

22.9

22.0

11.0

83.1

45.7

43.9

-

60.0

27.1

49.0

...

Embodiment 2

[0024] The first step to synthesize resin A 2 and resin B 2

[0025] Resin A in Table 1 is used instead of the formula 2 and resin B 2 Except that all the other synthetic techniques are the same as in Example 1. The obtained resin A 2 The hydroxyl value is 67, the acid value is 41, the number average molecular weight is 2600, and the solid content is 80%; the obtained resin B 2 The hydroxyl value is 65, the acid value is 3, the number average molecular weight is 4370, and the solid content is 80% for later use.

[0026] The second step resin A 2 and resin B 2 Polycondensation

[0027] Remove Resin A 2 281.4 parts, resin B 2 140.7 parts (resin A 2 : Resin B 2 =2:1) ​​to replace the resin A in the second step of Example 1 1 and resin B 1 Except, all the other polycondensation processes are with the second step of embodiment 1. The resulting polycondensate has an acid value of 21, a hydroxyl value of 60, and a number average molecular weight of 4000 for future use. ...

Embodiment 3

[0031] The preparation of embodiment 3 water-based automotive intermediate coatings

[0032]

raw material name

Specification

Dosage

The actual amount

convert to solid

Film-forming substance

Water-dispersed resin of the present invention

(Embodiment 1 or Embodiment 2)

Solid content 40%

100

40(44.97％)

water

distilled or deionized water

22

0

Pigments

Titanium dioxide

carbon black

Talc powder

Precipitated Barium Sulfate

Kaolin

DuPont, Type R

Tegoza Corporation, SP-4

1250 mesh

1250 mesh

1250 mesh

20

0.3

8

8

4

40.3(45.31％)

crosslinking agent

amino resin

blocked isocyanate

Cyanoamide 1130, 98% solids

Bayer AG 2016, 40% solids

4.1

10.0

8(9％)

catalyst

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention relates to water dispersed resin and paint for the intermediate coat of vehicle. The resin is water dispersed matter produced through condensation polymerizing hydrophilic polyester resin with acid value of 20-60 and hybrophobic polyester resin with acid value below 5 and obtained via ring-opening polymerization of epsilon-caprolactone in the weight ratio of 1-3 and has acid value of 10-25, hydroxyl value of 50-100 and number average molecular weight of 3000-5000. The paint with the water dispersed resin as filming agent contains water dispersed amino resin and water enclosed polyisocyanate mixed crosslinking agent. The paint has organic volatile matter less than 8 % and can form smooth coat with high adhesive force, good water resistance and flexibility and excellent high shock resistance.

Description

technical field [0001] The invention relates to a water-dispersed resin for coating in automobiles and its coating. Background technique [0002] In automotive painting, in addition to the beautiful appearance of the coating film, the requirements for the durability of the coating film are also getting higher and higher. Therefore, the importance of the middle coat between the primer coat and the top coat is gradually being valued by people, because it can not only buffer the impact of the gravel on the road on the surface of the car, but also protect the primer coat and the substrate. Without damage, the durability of the primer coating film can be greatly improved, and the mid-coat can adjust the flatness of the substrate to form a smooth and meticulous mid-coat surface, which can make the top coat have a better decorative effect. The resin used for coating in automobiles is currently still commonly used in China as solvent-based polyester, which has a high organic solven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/02C09D167/00
Inventor 夏范武董观秀胡中付强严俊
Owner CNOOC CHANGZHOU PAINT & COATINGS IND RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More