Prepn of solid phosphoric acid catalyst for oligomerization of propylene

A technology of phosphoric acid catalyst and polyphosphoric acid, which is applied in chemical instruments and methods, organic chemistry, hydrocarbons, etc., can solve the problems of poor catalyst stability and low crushing strength, and achieve improved extrusion, long service life, The effect of improving catalyst activity

Inactive Publication Date: 2003-02-26
CHINA PETROLEUM & CHEM CORP +1
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The catalyst is at a reaction temperature of 130-230°C, and the space velocity of the reaction raw material is 2.5-5.0hr -1 , under the condition of reaction pressure 2.0-6.0MPa, the highest conversion rate of olefin superposition reaction is 72.44%, and the crushing strength is low, only 170 N / cm 2 , poor catalyst stability
This document does not involve equipment material issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 3

[0031] Raw material polyphosphoric acid preparation:

[0032] According to the preparation condition of example 2, difference: the reactor material is electrolytic copper, makes 100 kilograms of polyphosphoric acid, contains phosphorus pentoxide 80% by weight.

[0033] Preparation of solid phosphoric acid catalyst:

[0034] Add zirconia and 22.0 kg of boric acid to the polyphosphoric acid prepared above under electric stirring, and control the reaction temperature at 170-200°C to make a polyphosphate mixture. At the same time, add 26.5 kg of dry diatomaceous earth into the kneader, add Polyphosphate mixture, kneaded for 4 minutes to obtain a viscous lump material, extruded, dried at 200°C for 1 hour, roasted at 500°C for 2 hours; activated with a mixture of water vapor and air, activation process conditions: activation temperature 250 °C, the activation time was 4 hours, and the molar ratio of air:water vapor was 1.4:1, and the finished catalyst was obtained. The obtained so...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Crushing strengthaaaaaaaaaa
Login to view more

Abstract

A preparation process of solid phosphoric acid catalyst for oligomerization of propylene includes preparing polyphosphate in 72-88 wt% at 120-180 deg.C in a copper reactor, preparing phosphate at 150-230 deg.C, mixing with diatomite, extruding into strips, drying by roasting, and activating. The molar ratio expression of the catalyst is SiAaBb(P2O5)c.(H2O)d. where A is at least one selected from B, Al and In; B is at least one selected from Ti, Zr, V, Nb, Cr, Mn, Mg and W; a=0.2-1.5; b=0.01-0.2; c=1.0-2.0; and d=0.6-1.2. The reactor is strongly resistant to corrosion of polyphosphate, the method has low production cost and the catalyst has high activity and high crushing strength.

Description

technical field [0001] The invention relates to a preparation method for propylene oligomerization solid phosphoric acid catalyst. Background technique [0002] Solid phosphoric acid catalyst (SPAC) is one of the catalysts widely used in the petrochemical industry. For the typical example of olefin oligomerization to prepare trimers and tetramers, nonene and dodecene are prepared from propylene by acidic catalyst oligomerization. It is characterized by relatively simple process and mature technology, and the main difference in the synthesis method is the use of different catalysts. According to relevant literature reports, so far, most of the industrial catalysts for the preparation of trimers and tetramers from propylene still use phosphoric acid series catalysts, including the liquid phosphoric acid catalyst of California Research Company, the copper pyrophosphate catalyst of Kellogg Company, Standard Oil's phosphoric acid-quartz catalyst, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C07C2/18
CPCY02P20/52
Inventor 陈永福姚亚平袁梅卿黄尔峰徐菁
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap