Composition for forming transparent polysiloxane coating and solidification thereof

A technology of polysiloxane and curing method, applied in the direction of coating, etc., can solve the problems of unstable catalyst action, unsatisfactory adjustment of hardness, etc.

Inactive Publication Date: 2003-04-02
泽村聪
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the current catalysts do not have stable catalytic action, so the curing time varies, and the adjustment of hardness is not satisfactory

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific example

[0041] Specific examples are: 2-hydroxy-4-methoxybenzophenone, 2,4-dihydroxybenzophenone, 2,2',4,4'-tetrahydroxybenzophenone, 2-hydroxy-4- Methoxybenzone-5-sulfonic acid, etc.

[0042] If it is not necessary to have alkali releasability, benzophenone-based or benzotriazole-based ultraviolet absorbers other than the above-mentioned ones can be used.

[0043] The infrared shielding agent may be an inorganic substance or an organic substance. As an infrared shielding agent, there are two types of infrared reflection type and infrared absorption type.

[0044] When it is an infrared reflective type, it is a perylene (perylene)-based black pigment (manufactured by BASF Co.), etc., and when it is an infrared-absorbing type, when it is an organic substance, it is aniline or polyaniline-based (manufactured by Japan Ka-ritto Co., Ltd. ) or organic pigments such as cyanine or phthalocyanine (manufactured by Nippon Shokubai Co., Ltd.). -02, ULA-01 produced by Kureha Chemicals—in this ...

Embodiment 1～3

[0073] Embodiment 1~3 (embodiment 1)

[0074] Mix 85g of γ-glycidoxypropyltrimethoxysilane, 80g of γ-aminopropyltriethoxysilane and 50g of methyltrimethoxysilane, stir for 1 hour, and place it in a constant temperature room at 25°C for 14 day, let it ripen, and prepare the reaction product.

[0075] 5 g of 2,4-dihydroxybenzophenone were dissolved in 20 g of propylene glycol monoethyl ether acetate.

[0076] Dissolve 0.2 g of boron trifluoride piperidine in 10 g of dipropylene glycol monomethyl ether propanol. (4) What disperse|distributed 0.5g of ITO (indium tin oxide: Fuji titanium company make) whose particle diameter is 25nm in 5g of propylene glycol monoethyl ether acetate was prepared. (5) After mixing the liquids (3) and (4) in the liquid (2), 20 g of the liquid (1) was further uniformly mixed to prepare a composition 1 for forming a transparent polysiloxane coating film. (comparison 1)

[0077] Except not adding liquid (4), the same operation as Example 1 was perfor...

Embodiment 6

[0082] Embodiment 6 (19) in the gamma-glycidoxypropyl trimethoxysilane of 40g and 70g gamma-aminopropyl triethoxysilane, mix the trimethoxymethylsilane of 20g, stir after 1 hour, in In a constant temperature room at 25° C., it was left to age for 14 days to prepare a reaction product. Furthermore, 0.92 g of methoxysilane was mixed, and it left to stand in the thermostatic room of 25 degreeC for 3 days. (20) Dissolve 0.05g 2,4-dihydroxybenzophenone, 0.01g nickel dibutyl dithiocarbamate and 0.03g 2,6-di-tert-butyl 4-methylphenol in 20g propylene glycol monoethyl ether in acetate. (21) 0.2 g of boron trifluoride piperidine was dissolved in 10 g of a mixed solution consisting of 2 g of N-methyl-2-pyrrolidone and 8 g of dipropylene glycol monomethyl ether propanol.

[0083] After mixing the liquids (21) and (14) in the liquid (20), 20 g of the perylene-based black pigment and the liquid (19) were further uniformly mixed to prepare a composition 6 for forming a transparent polysil...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
sizeaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

There is provided a transparent silicone film-forming composition which forms a ultraviolet absorbing and infrared screening film exhibiting film hardness of 6H to 9H or more after curing on a transparent substrate such as glass and plastic. A transparent silicone film-forming composition comprises (a) a reaction product of alkoxysilane (A) having an epoxy group and alkoxylsilane (B) having an amino group with active hydrogen, (b) an acid catalyst, (c) a finely ground ITO cocatalyst and (d) at least one solvent selected from organic solvents. A transparent silicone film-forming composition comprising a reaction product of alkoxysilane (A) having an epoxy group and alkoxylsilane (B) having an amino group with active hydrogen as well as tri- or dialkoxysilane (C) mixed with monoalkoxysilane (D) and / or glycidsilane (E), (b) an acid catalyst, (c) a finely ground ITO cocatalyst and (d) at least one solvent selected from organic solvents.

Description

technical field [0001] The present invention relates to a hard transparent coating film that does not have staining and is bright in color by being coated on transparent substrates such as glass and plastic used in windows of buildings, trains, and automobiles, or Transparent and opaque polysiloxane coating film-forming composition for forming a colored transparent coating film and curing method thereof. [0002] More specifically, the present invention relates to the formation of a hard coat protective film on the window glass of buildings and automobile window glass, and further on the surface of metals such as acrylic and polycarbonate and plastic or aluminum, or the formation of a coating with rich popularity. Coating film, polysiloxane coating film-forming composition and curing method thereof functioning simultaneously for protection against ultraviolet rays and infrared rays. Background technique [0003] Conventionally, for the main purpose of preventing ultraviolet...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/08C08K5/01C08K5/57C09D183/00C09D183/04C09D183/06
CPCC08K5/57C09D183/04C09D183/14C08K5/01C03C17/008C03C17/009C03C17/30C03C2217/445C03C2217/476C03C2217/485C03C2217/944C03C2217/948C09D183/00C09D183/08
Inventor 吉原千智泽村聪
Owner 泽村聪
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com