Rubber automobile synchronous belt and its producing method

A manufacturing method and technology of timing belts, which are applied to belts, other household appliances, household appliances, etc., can solve the problems of complex manufacturing process, poor performance of timing belts, and short service life, and achieve simple manufacturing process, stable performance, and cost of use. low effect

Inactive Publication Date: 2004-04-28
朱国有 +3
View PDF0 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The synchronous belt manufactured by the above formula and its process is poor in performance, not stable enough, low in strength, easy to age, short in service life, high in use cost and complicated in manufacturing process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber automobile synchronous belt and its producing method
  • Rubber automobile synchronous belt and its producing method
  • Rubber automobile synchronous belt and its producing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] The invention adopts high-strength elastic nylon cloth as the synchronous belt tooth bread cloth. As a synchronous toothed belt covering cloth, in addition to high strength, it also has good wear resistance and latitudinal elongation and good tooth filling ability, and also requires good bonding force with the belt body, so it must be Elastic nylon cloth for surface treatment.

[0041] 1. Treatment of high elastic nylon cloth:

[0042] Firstly, the nylon cloth is impregnated with hydrogenated nitrile rubber thin glue (the glue concentration is 15-17%), so that the impregnated glue can fully penetrate into the fabric fibers, and an appropriate amount of M300 isocyanate is added to the above treatment solution (thin glue) Tackifier. Then carry out thick glue coating treatment (concentration is 24-26%), make the surface of the fabric attach a certain amount of glue layer, then carry out heating and drying treatment to the nylon cloth with glue layer, and its temperature ...

Embodiment 2

[0059] Embodiment 2: main raw material rubber and compounding agent, its composition ratio (calculated by weight percentage).

[0060] In this embodiment, firstly, the high elastic nylon cloth is subjected to surface treatment, using the treatment method in Example 1. The main raw materials, compounding agents and their formula ratios selected in the rubber mixing process are as follows: the main raw material rubber is hydrogenated nitrile rubber: 55, zinc oxide: 2.7, stearic acid 0.55, anti-aging agent: 2.2, semi-reinforced carbon Black: 30.2, Softener: 5.5, Sulfur: 0.42, Accelerator: 2.7. The above-mentioned rubber and compounding agent also adopt the process steps in Example 1 in the rubber mixing process. According to the process conditions of hydrogenated nitrile rubber and compounding agent which are difficult to disperse during mixing, a staged mixing method is designed in which the compounding agent is gradually added in batches, thus forming a colloidal sheet and the...

Embodiment 3

[0062] In the embodiment of the present invention, the treatment method of the high-stretch elastic nylon cloth is also carried out by using the treatment method in Examples 1 and 2.

[0063] Main raw material rubber and compounding agent, their composition ratio (by weight percentage).

[0064] Get hydrogenated nitrile rubber: 53, zinc oxide: 2.18, stearic acid: 0.57, high temperature resistance, ozone resistance anti-aging agent: 2.3, semi-reinforcing carbon black: 31.8, softener: 5.6, sulfur: 0.45, accelerator: 2.8. Process steps and process conditions thereof such as rubber mixing (two-stage mixing) adopted in embodiment 1.2, calendering with colloid, molding, vulcanization, demoulding, grinding, cutting, inspection (sampling physical property inspection) and the like. Made to meet the quality and performance indicators achieved by the performance of the finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The rubber holding belt is key part of automobile engine, and used for the timing ignition and gas distribution of cam shaft automobile engine. The materials including elastic nylon cloth as toothed coating cloth, hydrogenated butadiene-acrylonitrile rubber and auxiliary materials are produced through mixing to form the rubber belt, calendering to form sheet, shaping, sulfurizing, demolding, grinding, cutting, packing and other steps into the rubber holding belt. The product s high strength, high wear resistance, high ozone resistance, high rebound elasticity, less deformation, low cost, simple production process, long service life and capacity of operation in 130 deg.c environment.

Description

Technical field: [0001] The invention relates to a rubber automobile synchronous belt and a manufacturing method thereof, which is applied to the timing ignition and gas distribution of a camshaft gasoline engine, is a key accessory of an automobile engine, and belongs to the technical field of rubber products. Background technique: [0002] Before the present invention was made, the main raw materials of the automobile synchronous belt used on the automobile engine were nylon cloth, glass fiber rope, neoprene and compounding agents (Oxime, stearic acid, anti-aging agent, polyethylene, semi-reinforced carbon black, aromatic oil, zinc oxide, etc.). Its production process is as follows: 1. Firstly, the high elastic nylon cloth is processed. First, the nylon cloth is impregnated with dilute glue, and isocyanate compounds are added to the treatment solution to improve the oil resistance, abrasion resistance and adhesion of the nylon cloth to the colloid. Then carry out one-sid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29D29/00C08L9/02
Inventor 朱国有尤建平蔡伟薛建江
Owner 朱国有
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap