Antirust pigment for improving antirust property of antirust paint

A technology of anti-rust performance and anti-rust pigments, which is applied in the direction of anti-corrosion coatings, fibrous fillers, etc., can solve the problems of high price, and achieve the effect of reasonable price, convenient construction and large usage

Inactive Publication Date: 2004-06-16
万达科技(无锡)有限公司
View PDF0 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

According to the survey, at present, in the research of anti-rust pigments at home and abroad, it is mainly modified on the basis of phosphate. The direction of modification is to form polymetallic polyphosphate double salt, modified polyphosphate (three) metal salts The antirust performance of red lead can be slightly higher than that of red lead, but its price is expensive, such as the zinc calcium phosphomolybdate we bought in the test, the price is as high as 300 yuan / kg

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0069] Embodiment 1: get particle diameter and be 200 purpose carrier powder Fe 3 o 4 99.9 grams, take Nano Y 2 o 3 0.1 g of Nano Y 2 o 3 Surface treatment with coupling agent, and then with carrier powder Fe 3 o 4 Mix until completely uniform, promptly make 100 grams of composite iron-titanium powder of the present invention.

Embodiment 2

[0070] Embodiment 2: getting particle diameter is 400 purpose carrier powder Fe 3 o 4 98 grams, take nano SiO 2 1 gram, nano-TiO 2 1 g of nano-SiO 2 、TiO 2 Surface treatment with coupling agent, and then with carrier powder Fe 3 o 4 Mix until completely uniform, promptly make 100 grams of composite iron-titanium powder of the present invention.

Embodiment 3

[0071] Embodiment 3: get particle diameter and be 600 purpose carrier powder Fe 3 o 4 95.5 grams, take nano CaCO 3 1.5 grams, Nano Y 2 o 3 0.5 g, nano Fe 3 o 4 2.5 g nano-CaCO 3 , Y 2 o 3 , Fe 3 o 4 Surface treatment with coupling agent, and then with carrier powder Fe 3 o 4 Mix until completely uniform, promptly make 100 grams of composite iron-titanium powder of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite ferrum-titanium powder, a rust-preventive pigment for improving the tarnish proofness for anti-corrosive paint, characterized in that, the composite ferrum-titanium powder uses natural or artificially synthesized ferriferrous oxide having a fineness of 200-1200 sieve number as carrying agent, to be added by nano silicon oxide, titanium oxide, vanadium oxide, yttrium oxide, zinc oxide, ferric oxide and calcium carbonate.

Description

technical field [0001] The invention relates to an antirust pigment, in particular to a composite iron-titanium powder used for improving the antirust performance of an antirust paint. Background technique [0002] Coating is the most economical and convenient anti-corrosion material. Due to its excellent antirust performance, Hongdan antirust paint has been king in the field of antirust paint for nearly a hundred years. According to the introduction of the National Coatings Industry Information Center, my country's current annual consumption of anti-corrosion paint is more than 350,000 tons, not including the export of anti-corrosion paint, and the growth rate in 2001 reached 13%. In 1990, the national consumption of red lead reached 80,000 tons. In the past two years, the consumption of red lead has been declining, and the development trend is to gradually reduce and prohibit its use. Due to its excellent anti-rust performance and the lack of sound industrial hygiene and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09C1/24C09D5/08
Inventor 金广泉李家权
Owner 万达科技(无锡)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com