Ultraviolet aluminium-silver size coating with light curing

A technology of aluminum silver paste and ultraviolet light, applied in the direction of coating, etc., can solve the problems of low addition amount of aluminum paste, poor adhesion between layers, and unfavorable application.

Inactive Publication Date: 2006-03-15
CHINA LUCKY FILM CORP +1
View PDF7 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The coating has the following disadvantages: (1) the interlayer adhesion is poor; (2) titanium dioxide must be added to the aluminum powder paint with silver flash metal effect, so that there are more grinding processes in the preparation process of the coating; (3) ) The amount of aluminum paste added is low (limited to 2%-8%), which is not conducive to the application of special occasions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Aliphatic urethane acrylate CN9006 20.7%

[0044] Propoxylated Trimethylolpropane Triacrylate 20%

[0045] TPO 6%

[0046] 907 4%

[0047] ZX8081 15%

[0048] CAB-381-20 4%

[0049] DP-983 0.05%

[0050] BYK361 0.05%

[0051] SH350 0.25%

[0052] Butyl acetate 15%

[0053] Xylene 15%

[0054] After soaking the aluminum silver paste with a solvent, stir it evenly; mix the remaining solvent with the aluminum silver paste orientation agent, and stir until the aluminum silver paste orientation agent is fully dissolved; mix the acrylate resin and the acrylate monomer according to the proportion in the formula, Heat to 60°C, stir until completely dissolved, then add photoinitiator, dispersant, and leveling agent, and stir until uniformly mixed; mix the above components, and disperse uniformly; cool down and filter to obtain UV-curable aluminum-silver paste coating .

Embodiment 2

[0056] Aliphatic urethane acrylate CN9002 25%

[0057] Ethoxylated Trimethylolpropane Triacrylate 6%

[0058] Dipentaerythritol pentaacrylate 7%

[0059] 1,6-Hexanediol diacrylate 10%

[0060] TPO 3%

[0061] 184 3%

[0062] HS9007 10%

[0063] CAB-381-2 6%

[0064] EFKA5065 0.2%

[0065] EFKA3777 0.8%

[0066] DEUCHEM229 1.0%

[0067] Butyl acetate 14%

[0068] Toluene 14%

[0069] After soaking the aluminum silver paste with a solvent, stir it evenly; mix the remaining solvent with the aluminum silver paste orientation agent, and stir until the aluminum silver paste orientation agent is fully dissolved; mix the acrylate resin and the acrylate monomer according to the proportion in the formula, Heat to 55°C, stir until completely dissolved, then add photoinitiator, dispersant, and leveling agent, and stir until uniformly mixed; mix the above components, and disperse uniformly; cool down and filter to obtain UV-curable aluminum-silver paste coating .

Embodiment 3

[0071] Aromatic urethane acrylate CN978 27.4%

[0072] Bisphenol A Epoxy Acrylate CN104 18%

[0073] Dipentaerythritol pentaacrylate 5%

[0074] 1,6-Hexanediol diacrylate 5%

[0075] Darocur 1173 2%

[0076] Irgacure 184 3%

[0077] ZX1755 6%

[0078]CAB-381-0.5 5%

[0079] CAB-381-2 10%

[0080] EFKA4010 0.2%

[0081] BYK388 0.2%

[0082] SH290 1.2%

[0083] Butyl acetate 10%

[0084] Toluene 7%

[0085] After soaking the aluminum silver paste with solvent, stir evenly; use the remaining solvent to mix with the aluminum silver paste directional agent, and stir until the aluminum silver paste directional agent is fully dissolved; mix the acrylate resin and acrylate monomer according to the proportion in the formula, Heat to 65°C, stir until completely dissolved, then add photoinitiator, dispersant, and leveling agent, stir until evenly mixed; mix the above components, and disperse evenly; cool down and filter to obtain UV-curable aluminum-silver paste coating .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A ultraviolet light solidified aluminium silver slurry coating consists of acrylic resin 20-50wt%, acrylic ester monomer 10-50wt%, light initiating agent 3-10wt%, aluminium silver slurry 2-15wt%, aluminium silver slurry orienting agent 4-15wt%, assistants 0.3-2.5wt% and solvent 15-30wt%. It achieves fast curing speed, less organic volatile substances, higher production efficiency, better adhesion, hardness and abrasive-resistant performance.

Description

technical field [0001] The invention relates to a UV-curable coating, in particular to a UV-curable aluminum-silver paste coating with excellent interlayer adhesion and metallic silver flash texture. Background technique [0002] Aluminum silver paste coating is a kind of coating with metallic glitter effect, such as Chinese patent with application number 92106365.3 discloses a kind of quick-drying silver powder paint, which is composed of silver powder, film former, tackifier, anti-aging agent and solvent, It has fast drying speed, stable performance, long-term storage without deterioration, good low temperature resistance, wear resistance and simple production process. The Chinese Patent Application No. 93111243.5 discloses a silver-aluminum powder paint, which is composed of silver-aluminum powder, polystyrene foam, modifier and solvent. The product has stable performance, good water and wear resistance, good low temperature resistance, high brightness of the paint layer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/04
Inventor 方君利刘瀛梁笑丛
Owner CHINA LUCKY FILM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com