Xylon polymerized composite material and its preparation method

A composite material and wood technology, which is applied in the field of wood-polymer composite materials and its preparation, can solve the problems of high production cost, low product quality, and no price advantage of wood-plastic products, increase the possibility of polymerization and complexation, and improve The effect of product quality and reduction ratio

Inactive Publication Date: 2006-08-30
陈根长
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The wood-plastic composite materials (such as Japan's Ain wood) that started from the chemical industry have taken a step forward in technology, but there are many important defects, which have caused the wood-plastic industry to fail to achieve great development. The defects mainly include: 1. Wood-plastic materials The main technology is plastic modification. Wooden materials are only used as fillers, while unmodified woody materials have poor compatibility with plastics. Compared with low-molecular mineral fillers such as calcium carbonate, the use value of woody materials is much lower. Many; 2. It is difficult to extrude the material with wood material as the filler, the product quality is not high, and the scrap rate is high; 3. The variety of plastics used is very narrow, and the requirement is a single type of pure plastic, and it is difficult to process when mixed with other types; 4. Due to the fact that it is mainly made of plastic and difficult to process, the production cost of wood-plastic products is very high. Compared with other materials, it has no price advantage and it is difficult to enter the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Xylon polymerized composite material and its preparation method
  • Xylon polymerized composite material and its preparation method
  • Xylon polymerized composite material and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Embodiment 1, take wood powder, polyethylene (PE), stearic acid as raw material to prepare polymeric wood material

[0030] The first step, material preparation

[0031] Stearic acid can be purchased in chemical raw material stores for industrial use.

[0032] Polyethylene (PE) Buy new PE pellets at plastic stores, or use recycled flakes. Generally, you can buy oil barrels, soy sauce barrels, baby bottles, plastic wine bottles, etc. from the plastic recycling department, and then use a plastic crusher to grind them into flakes and wash them with clean water or alkaline water. While cleaning, materials can be selected. Compared with PE and other engineering plastics, the specific gravity is lighter and can float on the water. After cleaning, it can be directly bagged and waited for use.

[0033] The second step, wood flour modification: wood flour should be plant material with cellulose, hemicellulose and lignin as the main components. Sawdust, shavings, peanut shells...

Embodiment 2

[0041] Embodiment 2, modified wood flour performance test

[0042] The formula of the present invention: 200 kilograms of modified wood flour, 20 kilograms of PE-based sheet plastics, 17 kilograms of particles granulated from recycled agricultural film, 5 kilograms of stearic acid and paraffin wax.

[0043] Comparative formula: 300 kg of ordinary wood flour, 60 kg of PE-based sheet plastic, 51 kg of agricultural film pellets, 7.5 kg each of stearic acid and paraffin.

[0044] The ZC-75 co-rotating twin-screw granulator assembled by Jiangsu Wuxi Shinan Wood Plastic Processing Co., Ltd. was selected for granulation. The first to sixth zones and the head temperature were set to 110°C, 140°C, 148°C, and 150°C, respectively. , 155° C., 160° C., 162° C., and other operating procedures are the same as in Example 1.

[0045] result:

[0046] 1, granulation property: more than 95% of the particles produced by the formula of the present invention are granules, while more than 70% of t...

Embodiment 3

[0056] Embodiment 3, single-screw granulation test

[0057] Invented formula: 60 kg of modified wood powder, 20 kg of agricultural film material, 20 kg of PE sheet material, 2.5 kg of stearic acid, 2.5 kg of paraffin, and 0.5 kg of iron oxide red;

[0058] Comparative formula: 60 kg of ordinary wood flour, 20 kg of agricultural film material, 20 kg of PE sheet material, 2.5 kg of stearic acid, 2.5 kg of paraffin wax, and 0.5 kg of iron oxide red;

[0059] The YH-TD single-screw granulator produced by Beijing Yuquan Tuochuang Environmental Protection Technology Development Center was selected for granulation. The results showed that the granules obtained from the invented formula were soft and sticky, and the smoke was small during the granulation process; angry.

[0060] Use the single-screw granulator produced by Jiangsu Wuxi Shinan Wood Plastic Processing Co., Ltd. to produce 16mm thick hollow floor with the obtained particles:

[0061] When the particles obtained by the f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention discloses a xylon polymerized composite material and its preparation method. The xylon polymerized composite material provided by said invention contains 65-85 wt% of modified xylon raw material, 10-30 wt% of thermoplastic material and 5-10 wt% of additive. The modified xylon raw material is obtained by spraying reactive initiator into the broken xylon raw material, sealing and stacking the above-mentioned material. Said xylon polymerized composite material can be made into various products instead of various plastics and wood material.

Description

technical field [0001] The invention relates to a wood polymer composite material (referred to as polymer wood) and a preparation method thereof. Background technique [0002] Wooden raw materials, like cement, steel, and plastics, are one of the indispensable basic raw materials for modern social and economic development. In 2003, my country produced 45.53 million tons of wood-based panel materials, making it the world's largest producer. With the development of the national economy, the demand and production will increase. At present, the basic raw materials of artificial wood have problems such as insufficient supply of wood, backward production technology, large amount of waste discharge in the production process, release of toxic substances during use, and serious pollution. On the other hand, there are plant raw materials that are equivalent to five to seven times the wood production in my country and can produce woody basic raw materials, which are wasted year after ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L97/02C08K5/54C08J3/12B29B9/12
Inventor 陈根长
Owner 陈根长
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com