Method for recovering nickel and cobalt from nickel oxide ore and nickel silicide ore

A technology of nickel oxide ore and nickel silicate, which is applied in the field of mineral processing engineering, can solve the problems of high metal recovery rate and failure to achieve, and achieve the effects of good economic benefit, quick effect and simple process.

Inactive Publication Date: 2006-09-06
KUNMING UNIV OF SCI & TECH +1
View PDF0 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The metal recovery rate of pressure acid leaching is high, but the plants that have been put into operation in recent years using the pressure acid leaching process have not achieved the expected ideal results

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for recovering nickel and cobalt from nickel oxide ore and nickel silicide ore

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Example 1: Yuanjiang nickel silicate ore, the raw ore contains 1.2% nickel and 0.08-0.1% cobalt. Crush the raw ore to -3mm-0mm, and then grind it to -200 mesh with a Raymond mill, accounting for 80-90wt%, add 12.5wt% coke powder with a particle size of -3mm-0mm, chlorinating agent CaCl 2 25wt%, additive MOP 0.5wt%, mixed pellets, made into pellets with a particle size of 8-15mm, and dried in the air until the moisture content was less than 8%. Segregation and roasting in a segregation rotary kiln at 400-500 ° C, the rotary kiln speed is 1.2 rpm, the roasting time is 1-1.2 hours, the roasting fuel is pulverized coal, the roasting method is counter-current roasting, the roasted products are unloaded into the pool and quenched with water. The quenched product is taken out and crushed and then ground. The grinding fineness is -200 mesh, accounting for 75~78wt%. The nickel grade of the mixed concentrate is 11.5%, the recovery rate is 84.5%, the cobalt grade is 0.56%, and t...

Embodiment 2

[0023] Example 2: Laterite nickel ore in the Philippines. The ore sample is taken from the Philippines. The grade of nickel in the raw ore is 1.28%, and the grade of cobalt is 0.041%. Crushing the raw ore to -3mm-0mm, and then grinding it to -200 mesh with a Raymond mill, accounting for 80-90wt%, adding 10wt% coke powder with a particle size of -3mm-0mm, 30wt% chlorinating agent (NaCl), and additives ( Copper dimethyl thiocarbamate) 0.6wt% mixed pellets, particle size 5-10mm, air-dried in the air until the moisture content is <3-5%, added to the high-temperature zone with a temperature of 1000-1200°C and a kiln tail temperature of 400 Segregation roasting in a segregation rotary kiln at ~500°C, the rotary kiln speed is 1 rpm, the roasting time is 1.5-2 hours, the roasting fuel is pulverized coal, the roasting method is countercurrent roasting, and the roasted products are discharged into the water pool for water quenching, water quenching The product is taken out and crushed a...

Embodiment 3

[0024] Example 3: Hanyuan cobalt-nickel ore, the raw ore contains 0.14% nickel grade and 0.25% cobalt grade. Crush the raw ore to -3mm-0mm, and then grind it to -200 mesh with Raymond Mill to account for 80-90wt%, add 5wt% of coke powder with a particle size of -3mm-0mm, chlorinating agent (CaCl 2 ) 23wt%, additives (CuCl: NH 4Cl=1:1) 1wt% mixed pellets, particle size 8-15mm, air-dried to moisture <3-5%, add high-temperature zone temperature of 1000-1300°C kiln tail temperature of 500-600°C Isolation roasting in the segregation rotary kiln, the rotational speed of the rotary kiln is 2 rpm, the roasting time is 1-1.5 hours, the roasting fuel is pulverized coal, the roasting method is countercurrent roasting, the roasted products are unloaded into the water pool for water quenching, and the water quenched products are taken out after Grinding after crushing, the grinding fineness is -200 mesh, accounting for 95wt%, separated by a magnetic separator with a magnetic field strengt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates the reclaiming nickel-to-cobalt method from nickel oxide ore and silicic acid nickel ore, comprising the following steps: milling the nickel oxide ore and silicic acid nickel ore to -200 mesh, adding 5-15% coke breeze, 10-30% chloration agent, and 0.1-1.0% adjuvant to make 5-15mm pellet, adopting chloridising separating and roasting, controlling the high temperature of rotary kiln at 1000-1300Deg.C and back kiln at 400-600Deg.C, the rotation rate of rotary kiln being 0.75-2 revolution per minute, time being 1-2 hours, then putting the product into magnet separator whose magnetic density is 1500-3000G, finally getting the cobalt-nickel ore, whose nickel grade is 5-15%, and recovery ratio is 80-85%, and whose cobalt grade is 0.3-1.7%, and recovery ratio is 70-80%.

Description

[0001] One, technical field: the present invention relates to a kind of method that reclaims nickel, cobalt from nickel oxide, nickel silicate ore. It belongs to the field of mineral processing engineering. 2. Background technology [0002] Due to the excellent properties of nickel metal, nickel has become an indispensable raw material for national defense industry and civil industry, and has an extremely important position and role in the national economy. There are three types of nickel deposits known in the world: copper-nickel sulfide deposits, nickel oxide deposits and weathered crust nickel silicate deposits. Nickel oxide deposits are nickel-bearing peridotites that have undergone large-scale long-term weathering and leaching metamorphism in tropical or subtropical regions. They are loose clay-like ores composed of iron, aluminum, silicon and other hydrous oxides. Due to the oxidation of iron, the ore is red, so it is called laterite ore. Laterite ore and nickel silica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22B1/00C22B1/02B03C1/02C22B23/00
CPCC22B1/245C22B1/2406C22B23/021C22B23/005B03C1/30Y02P10/20
Inventor 张昱陈晓鸣
Owner KUNMING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com