Artists' canvas with-ethylene copolymer coating and without filler and its producing process

An ethylene copolymer and vinyl acetate technology, which is applied in the field of painting by painters, can solve problems such as affecting product performance and shelf life, unsatisfactory coating film compactness, and easy yellowing of white coatings, achieving improved compactness, Excellent surface performance and improved mechanical strength

Inactive Publication Date: 2006-11-08
宋健 +2
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The defect of this white-coated art canvas is that the compactness of the coating film is not ideal, and back seepage and oil absorption are often prone to occur during painting; because it contains more solid powder without fillers, it is prone to cracking and cracking of the coating and flaking; white coating tends to yellow
These defects affect the performance and shelf life of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Embodiment 1: The production process steps of the non-filler vinyl acetate-ethylene copolymer compound coated art oil canvas of the present invention are as follows:

[0032] 1. Preparation of coating materials for bottom, middle and overcoat coatings:

[0033] (1), undercoat material: get styrene-acrylic ester copolymer emulsion: 44%, vinyl acetate homopolymer emulsion: 15%, vinyl acetate-ethylene copolymer emulsion: 28%, sodium benzoate: 0.15%, glycerin: 0.10%, emulsifying wax: 0.20%, water: 12.55%; first heat the water to 75°C, add emulsifying wax and mix well, then add styrene-acrylate copolymer emulsion or pure acrylate copolymer Polymer emulsion, vinyl acetate homopolymer emulsion, vinyl acetate-ethylene copolymer emulsion were mixed evenly, then sodium benzoate and glycerin were added, stirred and mixed evenly at room temperature, and set aside.

[0034] (2) Coating material for intermediate coating: take styrene-acrylate copolymer emulsion or pure acrylate copo...

Embodiment 2

[0040] The production process steps of the non-filler vinyl acetate-ethylene copolymer compound coated art oil canvas of the present invention are as follows:

[0041] 1. Preparation of coating materials for bottom, middle and overcoat coatings:

[0042] (1), base coating material: get styrene-acrylic ester copolymer emulsion: 40%, vinyl acetate homopolymer emulsion: 20%, vinyl acetate-ethylene copolymer emulsion: 25%, sodium benzoate: 0.1%, glycerin: 0.2%, emulsifying wax: 0.15%, water: 14.55%; first heat the water to 75°C, add emulsifying wax and mix well, then add styrene-acrylate copolymer emulsion or pure acrylate copolymer Polymer emulsion, vinyl acetate homopolymer emulsion, vinyl acetate-ethylene copolymer emulsion were mixed evenly, then sodium benzoate and glycerin were added, stirred and mixed evenly at room temperature, and set aside.

[0043] (2) Coating material for intermediate coating: Take styrene-acrylate copolymer emulsion or pure acrylate copolymer emulsio...

Embodiment 3

[0047] The production process steps of the non-filler vinyl acetate-ethylene copolymer compound coated art oil canvas in the embodiment of the present invention are as follows:

[0048] 1. Preparation of coating materials for bottom, middle and overcoat coatings:

[0049] (1), base coating material: get styrene-acrylic ester copolymer emulsion: 32%, vinyl acetate homopolymer emulsion: 18%, vinyl acetate-ethylene copolymer emulsion: 34%, sodium benzoate: 0.20%, glycerin: 0.15%, emulsifying wax: 0.25%, water: 15.4%; first heat the water to 75°C, add emulsifying wax and mix well, then add styrene-acrylate copolymer emulsion or pure acrylate copolymer Polymer emulsion, vinyl acetate homopolymer emulsion, vinyl acetate-ethylene copolymer emulsion were mixed evenly, then sodium benzoate and glycerin were added, stirred and mixed evenly at room temperature, and set aside.

[0050] (2) Coating material for intermediate coating: take styrene-acrylate copolymer emulsion or pure acrylat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The present invention belongs to the field of drawing article technology, and is especially one kind of artists' canvas with coating of vinyl acetate-ethylene copolymer and no filler suitable for oil painting, propylene drawing, gouache and decoration and its production process. The artists' canvas producing process includes compounding the coating materials for the bottom layer, the middle layer and facing layer; painting the bottom coating and stoving; painting 1-3 middle coating and stoving; and painting 1 or 2 facing coating and stoving to obtain the product. The artists' canvas has fine smooth and homogeneous coating, improved use performance, no oil permeation, high water resistance, and other advantages.

Description

technical field [0001] The invention relates to a non-filler vinyl acetate-ethylene copolymer compound coated art oil painting cloth and its production process, specifically for painting artists, suitable for oil painting, acrylic painting and gouache painting, and can also be used for decoration, The decoration belongs to the technical field of painting supplies. Background technique: [0002] Before the present invention was made, in prior art, artist's painting usually adopts traditional white coated canvas. It is mainly to apply white coating material directly on the base fabric. The white coating material adopts polymer emulsion such as polyvinyl alcohol, ethylene acetic acid homopolymer emulsion, styrene-acrylic ester copolymer emulsion and pure acrylate copolymer emulsion as one-component or two-component emulsion as coating base A large number of fillers such as titanium dioxide, lithopone, talcum powder, calcium carbonate, zinc oxide, etc. are mixed. Then apply t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/04B44D2/00
Inventor 宋健宋奇宋磊
Owner 宋健
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap