Curable liquid resin composition and method for producing multilayer body using same

A curable resin and manufacturing method technology, applied in the direction of chemical instruments and methods, synthetic resin layered products, layered products, etc., can solve problems such as difficulty in reducing costs, achieve high scratch resistance and improve scratch resistance , The effect of simplifying the manufacturing process

Active Publication Date: 2007-02-28
ARAKAWA CHEM IND LTD
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the case of using the vapor deposition method, it is difficult to efficiently form a uniform anti-reflection film on a large-area substrate, and it is difficult to reduce the cost because a vacuum device is required.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Curable liquid resin composition and method for producing multilayer body using same
  • Curable liquid resin composition and method for producing multilayer body using same
  • Curable liquid resin composition and method for producing multilayer body using same

Examples

Experimental program
Comparison scheme
Effect test

manufacture example 1

[0267] (1) Synthesis of organic compounds having polymerizable unsaturated groups

[0268] Into a mixed solution of 221 parts of mercaptopropyltrimethoxysilane and 1 part of dibutyltin dilaurate in a container equipped with a stirrer, isophorone diacetate was dropped at 50° C. for 1 hour in dry air. After 222 parts of isocyanate, it stirred at 70 degreeC for 3 hours.

[0269] Next, NK ester A-TMM-3LM-N (consisting of 60% by mass of pentaerythritol triacrylate and 40% by mass of pentaerythritol tetraacrylate. Only the pentaerythritol triacrylate which has a hydroxyl group participated in the reaction.) After 549 parts, it stirred at 60 degreeC for 10 hours, and obtained the reaction liquid.

[0270] When the amount of residual isocyanate of the organic compound having a polymerizable unsaturated group, which is a product in the reaction liquid, was measured by FT-IR, it was 0.1% by mass or less, and it was confirmed that each reaction proceeded substantially quantitatively. U...

manufacture example 2

[0272] (2) Synthesis of urethane acrylate

[0273] In a container with a stirrer, NK Ester A- After 93 parts of TMM-3LM-N (only the pentaerythritol triacrylate having a hydroxyl group participated in the reaction), it was stirred at 60° C. for 6 hours to form a reaction liquid.

[0274] When the product in the reaction liquid, ie, the amount of remaining isocyanate was measured by FT-IR in the same manner as in Production Example 1, it was found to be 0.1% by mass or less, and it was confirmed that the reaction proceeded substantially quantitatively. In addition, it was confirmed that a urethane bond and an acryloyl group (polymerizable unsaturated group) were contained in the molecule.

[0275] By the above operations, in addition to obtaining 75 parts of urethane hexaacrylate compounds, a composition (A-2) in which 37 parts of pentaerythritol tetraacrylates that did not participate in the reaction were mixed was obtained.

manufacture example 3

[0277] [Preparation of a composition for a hard coat layer containing silica particles]

[0278] 2.32 parts of the polymerizable unsaturated group-containing composition (A-1) produced in Production Example 1, silica particle sol (methyl ethyl ketone silica sol, manufactured by Nissan Chemical Industry Co., Ltd. MEK- ST, number average particle diameter 0.022μm, silica concentration 30%) 91.3 parts (27 parts as silica particles), ion-exchanged water 0.12 parts and 0.01 parts of p-hydroxyphenyl monomethyl ether, at 60 After stirring at °C for 4 hours, 1.36 parts of methyl orthoformate was added, followed by heating and stirring at the same temperature for 1 hour to obtain reactive particles (dispersion liquid (A-3)). After weighing 2 g of this dispersion liquid (A-3) in an aluminum dish, it was dried on a hot plate at 175° C. for 1 hour, and the solid content was determined by weighing, and it was 30.7%. In addition, after weighing 2g of the dispersion liquid (A-3) in a magnetic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
refractive indexaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

Disclosed is a method for producing a multilayer body having a base, and a conductive layer (antistatic layer) and multilayer structure arranged on the base. The method for producing a multilayer body is characterized in that the conductive layer (antistatic layer) is formed by vapor-phase polymerization of at least one monomer selected from the group consisting of pyrrole, thiophene, furan, selenophene, 3,4-ethylenedioxythiophene and derivatives of those, then a liquid curable resin composition containing a fluorine-containing polymer (A), a thermosetting compound (B), a curing catalyst (C), metal oxide particles (D), a highly volatile solvent (E-1) and a less volatile solvent (E-2) is applied thereto for forming a coating and the solvent is evaporated from the coating, so that this single coating is formed into two or more layers. Also disclosed is a multilayer body produced by such a method.

Description

technical field [0001] The present invention relates to a liquid curable resin composition and a method for producing a laminate using the same, and more particularly to a liquid curable resin composition capable of forming two or more layers from one coating film and a laminate using the same manufacturing method. Background technique [0002] Now, along with the development of multimedia, various advances are manifested in various display devices. In addition, in various display devices, especially display devices that can be used outdoors mainly for portable use, the improvement of the visibility is becoming more and more important, and demanders demand that even in large-scale display devices and the matter remains a technical subject. [0003] Conventionally, as a method of improving the visibility of a display device, a method of covering a substrate of a display device with an antireflection film made of a low-refractive index material has been used. Plating is a m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/12B32B27/30C08K3/22C08K5/00
Inventor 下村宏臣土居本光伸铃木康伸山村哲也江利山祐一田边隆喜高濑英明
Owner ARAKAWA CHEM IND LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com