Method for removing aluminum trichloride and purifying products in C5 petroleum resin production process

A technology of petroleum resin and aluminum trichloride, which is applied in the field of petrochemical industry, can solve the problems of difficult separation, emulsion formation, and difficulty in obtaining light-colored resins, and achieve the effects of reducing production costs, easy separation, and increasing softening point

Active Publication Date: 2007-04-11
SINOPEC LANZHOU GASOLINEEUM CHEM IND CORP
View PDF2 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

but if C 5 When the viscosity of the polymerization liquid is very high, it is easy to cause C 5 Petroleu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for removing aluminum trichloride and purifying products in C5 petroleum resin production process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Embodiment 1, with 100 parts (weight parts) by C 5 C 5 Petroleum resin, after being heated to fusing, add 60 parts (parts by weight) of concentration and be 3% sodium hydroxide solution to neutralize the aluminum chloride in the petroleum resin polymerization liquid; The mixed solution is heated to 100 ℃, and the control stirrer rotating speed is at 150 rpm to ensure that the resin liquid and the sodium hydroxide solution are mixed evenly and fully reacted, stop heating, continue stirring for about 10 minutes, then cool at room temperature, the oil phase and the water phase are separated, and the resin solidifies. Rinse with water to remove residual sodium hydroxide on the surface of the resin, and then put C 5 Petroleum resin is crushed into 10-100 μm powder with crushing equipment, soaked in 100 parts of distilled water containing 0.2% non-ionic surfactant OP-10 for 24 hours, then washed with clean water until neutral, and drained, then The petroleum resin powder wa...

Embodiment 2

[0026] Embodiment 2, with 100 parts (weight parts) by C 5 C 5 Petroleum resin, after being heated to fusing, add 20 parts (weight parts) concentration and be 12% sodium hydroxide solution to neutralize the aluminum chloride in the petroleum resin polymerization liquid; Mix solution is heated to 90 ℃, control the stirring speed of agitator at 150 rpm to ensure that the resin liquid and the sodium hydroxide solution are mixed evenly and fully reacted, stop heating, continue stirring for about 10 minutes, then cool at room temperature, the oil phase and the water phase are separated, and the resin solidifies. Rinse with water to remove residual sodium hydroxide on the surface of the resin, and then put C 5 Petroleum resin is crushed into 10-100μm powder with crushing equipment, soaked in 100 parts of distilled water containing 0.3% non-ionic surfactant fatty acid polyoxyethylene ester for 20 hours, then washed with clean water until neutral, and drained , and then the petroleum...

Embodiment 3

[0027] Embodiment 3, with 100 parts (weight parts) by C 5 C 5Petroleum resin, after being heated to fusing, add 40 parts (weight parts) concentration and be 8% sodium hydroxide solution to neutralize the aluminum chloride in the petroleum resin polymerization liquid; Mixed solution is heated to 120 ℃, control the stirrer rotating speed at 150 rpm to ensure that the resin liquid and the sodium hydroxide solution are mixed evenly and fully reacted, stop heating, continue stirring for about 10 minutes, then cool at room temperature, the oil phase and the water phase are separated, and the resin solidifies. Rinse with water to remove residual sodium hydroxide on the surface of the resin, and then put C 5 Petroleum resin is crushed into 10-100μm powder with crushing equipment, soaked in distilled water containing 0.5% non-ionic surfactant Tween for 12 hours, then washed with clean water until neutral, and drained, and then the petroleum resin The powder was vacuum dried at 80 °C ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Softening pointaaaaaaaaaa
Softening pointaaaaaaaaaa
Softening pointaaaaaaaaaa
Login to view more

Abstract

The present invention is method of eliminating aluminum trichloride and purifying product in C5 petroleum resin producing process with C5 fraction as material and aluminum trichloride as catalyst. The method includes adding 3-12 % concentration sodium hydroxide solution in 20-60 vol% of the resin liquid into the molten C5 petroleum resin liquid, heating the mixture to 90-120 deg.c and stirring for the resin liquid and the sodium hydroxide solution to react, cooling to room temperature for separating oil phase and water phase and solidifying petroleum resin, washing the solidified petroleum resin with water, crushing solidified petroleum resin into 10-100 micron powder, soaking in distilled water containing non-ionic surfactant for 20-24 hr, washing with water to neutrality, eliminating water, and vacuum drying to obtain purified C5 petroleum resin.

Description

technical field [0001] The invention belongs to the field of petrochemical industry, and relates to a method for removing catalysts in the production process of petroleum resin to purify products, in particular to a by-product C in the production of ethylene 5 The distillate is used as raw material, and aluminum chloride is used as a catalyst to prepare C 5 A method for removing aluminum trichloride and purifying products in the production process of petroleum resin. Background technique [0002] C 5 Petroleum resin is cracked C by-product of ethylene plant 5 The distillate was separated as raw material and used anhydrous AlCl 3 or BF 3 The ether complex is the resin obtained after cationic polymerization of the catalyst. cationic polymerized C 5 Petroleum resins contain catalysts, unpolymerized monomers and oligomers with very small molecular weights, which need to be removed by suitable methods to obtain good quality products. Catalyst removal is the synthesis of C ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F240/00C08F6/16
Inventor 王凌潘广勤卢灿辉张耀亨夏和生李亮张军华肖军刘鹏波毛兵崔树勋齐永新刘秀兰曹耀强张英杰张霖黄英
Owner SINOPEC LANZHOU GASOLINEEUM CHEM IND CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap