High-performance polyurethane elastomer and making method thereof
A polyurethane elastomer, high-performance technology, applied in the field of high-performance polyurethane elastomer and its manufacturing, can solve the problems of not being able to provide high hardness and high wear resistance, not being able to guarantee the dynamic performance of the material, and poor material strength, so as to improve the preservation Performance, high hardness, performance-enhancing effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0012] Example 1:
[0013] Combine polyethylene adipate polyol (number average molecular weight 2000, place of production: Shandong Huada Chemical Co., Ltd.) and 1,5-naphthalene diisocyanate (place of production: Bayer Chemical Co., Ltd.) in a weight ratio of 1:0.25 , Under the action of the catalyst triethylenediamine (DABCO331: American Gas Chemicals Co., Ltd.) to generate isocyanate group-terminated low molecular prepolymer, and then the reaction generated isocyanate group-terminated prepolymer The polymer and 1,4-butanediol (BASF Chemical Co., Ltd.) are reacted at a weight ratio of 1:0.05 to obtain a polyurethane elastomer. The manufacturing method of the polyurethane elastomer is carried out according to the following process steps: 1) Polyethylene adipate polyol and 1,5-naphthalene diisocyanate are added to the reactor according to the above-determined weight ratio to mix and stir, and the catalyst is added Triethylenediamine reacts to form isocyanate group-terminated prepol...
Example Embodiment
[0014] Example 2:
[0015] The polycaprolactone polyol (number average molecular weight 2000, production place: Japan Daicel Chemical Co., Ltd.) and dimethyl biphenyl diisocyanate (production place: Japan Soda Co., Ltd.), in a weight ratio of 1:0.23, in the catalyst Under the action of triethylenediamine (DABCO331: American Gas Chemicals Co., Ltd.), it reacts to generate isocyanate group-terminated low-molecular prepolymer, and then the isocyanate group-terminated prepolymer and 1,4-Butanediol (BASF Chemical Co., Ltd.) was reacted at a weight ratio of 1:0.045 to obtain a polyurethane elastomer. The manufacturing method of the polyurethane elastomer is carried out according to the following process steps: 1) The polycaprolactone polyol and dimethyl biphenyl diisocyanate are added to the reactor according to the above-determined weight ratio, mixed and stirred, and the catalyst triethylenedi The amine reacts to form an isocyanate group-terminated prepolymer, and the temperature is c...
Example Embodiment
[0016] Example 3:
[0017] The polycarbonate polyol (number-average molecular weight 2000, place of production: Asahi Kasei Chemical Co., Ltd.) and dimethyl biphenyl diisocyanate (place of production: Soda Co., Ltd.), in a weight ratio of 1:0.23, on the catalyst two laurel Under the action of dibutyl tin acid (origin: Shanghai Chemical Reagent Company), the low-molecular-weight prepolymer blocked by isocyanate groups is formed by reaction, and then the isocyanate group blocked prepolymer and 1,6- Hexanediol (origin: BASF Chemical Co., Ltd.) was reacted at a weight ratio of 1:0.05 to obtain a polyurethane elastomer. The manufacturing method of the polyurethane elastomer is carried out according to the following process steps: 1) The polycarbonate polyol and dimethyl biphenyl diisocyanate are added to the reactor according to the above-determined weight ratio, mixed and stirred, and the catalyst dibutyl tin dilaurate is added at the same time The reaction is carried out to generate ...
PUM
Property | Measurement | Unit |
---|---|---|
Hardness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap