Process for producing novel material with high functional capability from waste diatomaceous earth, and novel material with high functional capability from waste diatomaceous earth, and diatomaceous e
A technology of waste diatomite and new materials, which can be used in waste disinfection or sterilization methods, fertilizer mixtures, soil conditioning materials, etc., can solve problems such as threatening manufacturing costs, complex activation processing, and difficult processing.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0089] Powdered slaked lime (manufactured by Yoshizawa Lime Industry Co., Ltd.) 9Kg, white cement 8Kg, burned white diatomaceous earth (manufactured by Kitaki Diatomite Co., Ltd.) 5Kg, and sepiolite (manufactured by Showa Steel Industry Co., Ltd.) : Product name Mirucon) 5Kg was mixed to prepare a composition for building materials. Further, in order to improve the adhesiveness with the substrate, 0.6 Kg of acrylic powder resin (manufactured by Hekisto Gosei Co., Ltd.: trade name Acryl Powder A1000), Metrolz (Metroroz) were mixed into the composition for building materials. (Shin-Etsu Chemical Co., Ltd.: brand name Shin-Etsu SH30000FD) 0.4 Kg, antifoaming agent (Sannobuko Co., Ltd.: brand name SN-14HB) 0.15 Kg. 36.595 liters of water were added to 28.15 kg of the composition for building materials, and kneaded. Then, brush coating was carried out on a plasterboard of 30×30 cm. The above-mentioned coating is performed once with a thickness of about 0.5 mm as a primer, and onc...
Embodiment 2
[0092] To the building material composition of Example 2 above, ±0.5 kg of Chinese loess was further added, and 37.245 liters of water was added to the total weight of 28.65 kg, followed by kneading. Then, a paint roller application was carried out on plasterboards of 30×330 cm. The above-mentioned coating is about 0.5 mm thick for the base coat and about 2 mm thick for the top coat. Leave it at room temperature for 1 day to make it harden and make a 30×30cm wallboard.
[0093] The appearance was slightly yellow, and similar to Example 2, there was almost no sagging phenomenon during operation, white powder was scattered, and it did not adhere to the work clothes. Moreover, it can ensure that the water absorption rate is more than 60% of its own weight, and it can be made into a wallboard with good humidity control effect.
Embodiment 3
[0095] To the composition for building materials of the above-mentioned Example 2, ± 1 Kg of naturally-dried diatomaceous earth was further added, and 29 liters of water was added to the total weight of 29.15 Kg, followed by kneading. Then, spray on a 30 x 30 cm plasterboard. The above spray coating is about 0.5mm thick for the base coat and about 2mm thick for the surface. Leave it at room temperature for 1 day to make it harden and make a 30×30cm wallboard.
[0096] The appearance was slightly gray, and similarly to Example 2, during handling, there was almost no sagging, white powder was scattered, and it did not adhere to work clothes. Moreover, it can ensure that the water absorption rate is more than 65% of its own weight, and it can be made into a wallboard with good humidity control effect.
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com