Polyphenylether modified phenolic resin, and its preparing method

A technology of phenolic resin and polyphenylene ether, which is applied in the field of polyphenylene ether modified phenolic resin and its preparation, can solve problems such as high friction coefficient, phenolic resin does not have self-lubricating effect, and mechanical wear of materials, so as to achieve excellent mechanical properties, Effects of improving mildew resistance, insulation, and impact resistance

Inactive Publication Date: 2007-06-13
NORTHWESTERN POLYTECHNICAL UNIV
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, phenolic resin itself does not have self-lubricating effect. Compared with graphite, molybdenum disulfide and other so...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyphenylether modified phenolic resin, and its preparing method
  • Polyphenylether modified phenolic resin, and its preparing method
  • Polyphenylether modified phenolic resin, and its preparing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] a: Add 10 parts of modifier X to phenol under stirring condition, and make it dissolve in phenol;

[0028] b: After fully dissolving, add 10 parts of polyphenylene ether under stirring condition;

[0029] c: add 40 parts of solid paraformaldehyde again;

[0030] d: Add 10 polysulfone under stirring condition;

[0031] e: Add 94 parts of ethanol solvent in the reactor to dilute the resin, and add 2 parts of sodium pentachlorophenate;

[0032] f: Evenly impregnate 55 parts of glass fiber into the above resin after coupling treatment;

[0033] g: Dry the impregnating material so that the water and volatile matter content is 2-5%;

[0034] h: After-baking the toughened phenolic molding compound;

[0035] i: The impregnating material is cut into pellets on a pelletizer and molded.

Embodiment 2

[0037] a: Add 15 parts of modifier X to 100 parts of phenol under stirring condition, and make it dissolve in phenol;

[0038] b: After fully dissolving, 15 parts of polyphenylene ether under stirring conditions;

[0039] c: add 45 parts of solid paraformaldehyde again;

[0040] d: Add 20 parts of polysulfone under stirring condition;

[0041] e: Add 100 parts of acetone dissolving agent in the reactor to dilute the resin, and add 5 parts of sodium pentachlorophenate;

[0042] f: Evenly impregnate 60 parts of cotton cloth in the above resin after coupling treatment;

[0043] g: Dry the impregnating material so that the water and volatile matter content is 2-5%;

[0044] h: After-baking the toughened phenolic molding compound;

[0045] i: The impregnating material is cut into pellets on a pelletizer and molded.

Embodiment 3

[0047] a: Add 12 parts of modifier X to phenol under stirring condition, and make it dissolve in phenol;

[0048] b: After fully dissolving, add 12 parts of polyphenylene ether under stirring condition;

[0049] c: add 43 parts of solid paraformaldehyde again;

[0050] d: Add 15 parts of polysulfone under stirring condition;

[0051] e: Add 97 parts of solvent acetone in the reactor to dilute the resin, and add 3 parts of sodium pentachlorophenate;

[0052] f: Evenly impregnate 57 parts of cotton fibers in the above resin after coupling treatment;

[0053] g: Dry the impregnating material so that the water and volatile matter content is 2-5%;

[0054] h: After-baking the toughened phenolic molding compound;

[0055] i: The impregnating material is cut into pellets on a pelletizer and molded.

[0056] In the above embodiments, the size of the diced impregnation material is about 15-25mm or oriented at 1600-1800mm. The molding temperature is 160±5°C, the molding pressure i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

This invention involves a naphthol modified phenolic resin and its preparation. The ratio of the components : Phenol 100, solid paraform 40 - 45, polyphenylene oxide ether10- 15, modifier X 10-15, fiberglass 55 - 60, polysulfone 10 - 20, while sodium pentachlorophenate 2 -5, solvents 94 -100. Through the stir conditions adding modifier X into phenol, adding certain proportion of the solid paraform and polysulfone. In reactor adding solvents, resin diluted, and joined the sodium pentachlorophenate; fiberglass couple treated then uniform impregnation, after drying, postbaking, processing pelletizing and molding.

Description

Technical field: [0001] The invention relates to a polyphenylene ether modified phenolic resin and a preparation method thereof, which is mainly prepared by using phenol, polyphenylene ether, modifier X, solid paraformaldehyde, a catalyst and a toughening agent as raw materials. This kind of phenolic molding compound can be used to prepare wear-resistant, high-temperature-resistant and insulating structural parts. Background technique: [0002] At present, in many fields, it is necessary to use phenolic resin. It can be used in the manufacture of molding compounds, laminated plastics, foamed plastics, cellular plastics, various composite materials, adhesives, coatings, ion exchange resins, etc. Phenolic plastics are cheap, easy to obtain raw materials, and have good comprehensive performance. [0003] However, phenolic resin itself does not have self-lubricating effect. Compared with solid lubricants with self-lubricating effect such as graphite and molybdenum disulfide, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G8/36C08L61/14C08J5/08
Inventor 齐暑华张剑黄英
Owner NORTHWESTERN POLYTECHNICAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap