Molded fiber reinforced polymer artificial marble and its production method

A technology of artificial marble and its production method, which is applied in the field of building decoration materials, can solve problems such as low production efficiency, poor bending resistance, and lack of productivity, and achieve the effects of high production efficiency, reduced production cost, and easy promotion

Inactive Publication Date: 2007-07-11
WUHAN UNIV OF TECH
View PDF0 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this artificial marble product also has disadvantages such as low strength, poor bending resistance, and easy deformation. Due to the use of casting method, it still lacks mass productivity and low production efficiency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0014] The preparation method of molded fiber-reinforced polymer artificial marble comprises the following steps:

[0015] (1) Molding compound preparation: Weigh unsaturated polyester resin, curing agent, thickener, internal release agent and filler according to the above ratio, mix them evenly, and then add glass fiber and artificial color particles to make it Mix well, then knead into molding compound. Among them, the artificial color particles are cast from unsaturated polyester resin, methyl ethyl ketone peroxide, cobalt isooctanoate, calcium carbonate and pigments, and are crushed into particles with a diameter of 1 to 5 mm after solidification.

[0016] (2) Thickening: place the prepared molding compound to thicken, give full play to the thickening effect, and obtain a thickened molding compound.

[0017] (3) Heat the mold to 110-150°C and apply an external mold release agent, then put the thickened molding compound into the mold,

[0018] (4) Close the mold, molding ...

Embodiment 1

[0028] 1. Molded fiber reinforced polymer artificial marble formula:

[0029] Its components and ratio are: 40 parts by weight of unsaturated polyester resin; 0.8 parts by weight of curing agent; 0.8 parts by weight of thickener; 1.2 parts by weight of internal release agent; 44 parts by weight of filler; 8.1 parts by weight of glass fiber; 5.1 parts by weight of colored particles.

[0030] In the above formula, the curing agent adopts tert-butyl peroxybenzoate, the thickener adopts magnesium oxide, the internal release agent adopts zinc stearate, the filler adopts light calcium carbonate, the length of glass fiber is 10 mm, and the diameter of artificial color particles is 1 ~2mm.

[0031] 2. Manufacture of molded fiber-reinforced polymer artificial marble:

[0032] Put 40 parts by weight of unsaturated polyester resin, 0.81 parts by weight of curing agent tert-butyl peroxybenzoate, 0.81 parts by weight of thickener magnesium oxide, and 1.21 parts by weight of internal rele...

Embodiment 2

[0034] 1. Molded fiber reinforced polymer artificial marble formula:

[0035] Its components and ratio are: 38 parts by weight of unsaturated polyester resin; 0.8 parts by weight of curing agent; 1.1 parts by weight of thickener; 0.8 parts by weight of internal release agent; 45 parts by weight of filler; 9.4 parts by weight of glass fiber; 4.9 parts by weight of colored particles.

[0036] In the above formula, tert-butyl peroxybenzoate is used as curing agent, magnesium oxide is used as thickener, calcium stearate is used as internal mold release agent, aluminum hydroxide is used as filler, the length of glass fiber is 12mm, and the diameter of artificial color particles is 2-2mm. 3mm.

[0037] 2. Manufacture of molded fiber-reinforced polymer artificial marble:

[0038] 38 parts by weight of unsaturated polyester resin, 0.76 parts by weight of curing agent tert-butyl peroxybenzoate, 1.14 parts by weight of thickener magnesium oxide, and 0.76 parts by weight of internal re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses an artificial marble of moulded shaped fiber reinforced polymer and making method, which comprises the following parts: 32-46% insaturated polyester resin, 0.2-0.9% hardener, 0.2-1. 4% thickener, 0.6-1. 5% inner stripper, 41-46% fill, 7. 2-11. 9% glass fiber and 4. 8-6. 3% artificial colorful grain, wherein the artificial colorful grain is composed of 32-49% insaturated polyester resin, 0.5-2% methyl-ethyl ketone peroxide, 0.5-2% cobalt isooctanoic acid, 49-60% calcium carbonate and 1-4% dye. The making method of marble comprises the following steps: allocating mould plastic with those raw materials; thickening; moulding; shaping.

Description

technical field [0001] The invention relates to the field of building decoration materials, in particular to a molded fiber-reinforced polymer artificial marble and a manufacturing method thereof. Background technique [0002] As a substitute for natural marble, artificial marble has been widely used in the manufacture of sanitary ware and The field of architectural decoration. At present, most of the artificial marble products sold on the market are molded by casting method with unsaturated polyester resin and acrylic resin. Artificial marble products formed by casting method are processed by imitating the surface texture of natural marble. They have the mechanism characteristics similar to marble, and are better than natural marble in terms of hardness, gloss and wear resistance. However, this artificial marble product also has disadvantages such as low strength, poor bending resistance, and easy deformation. Due to the use of casting methods, it lacks mass productivity ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/18C04B14/42C04B22/06C04B24/08C04B14/04C04B14/26
CPCC04B26/18C04B18/022
Inventor 秦岩黄正群黄志雄梅启林王雁冰付承菊赵颖罗林
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap