Process to separate the vanadium contained in inorganic acid solutions

a vanadium and inorganic acid technology, applied in the field of method to separate dissolved vanadium in acid solutions, can solve the problems of not desirable, requiring the dumping of neutralized solutions,

Inactive Publication Date: 2003-02-13
UNIVE SIMON BOLIVAR
View PDF25 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The latter implies partial neutralization of the original acid content, meaning that the neutralized solution must be thrown away, which is not desirable.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example no.1

EXAMPLE NO. 1

[0022] The vanadium dissolved in 150 ml of a solution containing 0.01 M vanadium pentoxide (0.1% dissolved vanadium), 0.013 M potassium ferricyanide (0.43% potassium ferricyanide) and 3.6 M sulfuric acid (35% sulfuric acid), was recovered passing electric charge through two platinum mesh electrodes of 86 cm.sup.2 each.

[0023] A mixing rod was used to improve mass transport to the platinum mesh surfaces, in order to increase the electrodeposition efficiency. An electric current of 10 mA was applied for 3.1 hours, for a charge density of 3.8 C / cm.sup.2.

[0024] When the electrochemical experiment was completed, the solution was filtered in order to collect the suspended solid, which was subsequently dried and weighted. The weight gain of the platinum mesh cathode, where electrodeposition of a green compound occurred, was also determined. The sum of both quantities, the filtered solid and the deposited compound, which corresponds to the total quantity of compound formed, was ...

example no.2

EXAMPLE NO. 2

[0027] Vanadyl and potassium ferrocyanide was synthesized mixing equal volumes of an aqueous solution of 0.02 M vanadium pentoxide (0.20% of dissolved vanadium) and 3.6 M sulfuric acid (35% of sulfuric acid), with another solution containing 0.026 M potassium ferrocyanide (0.96% ferricyanide) and 3.6 M sulfuric acid. Precipitation of the vanadyl and potassium ferrocyanide compound occurred instantaneously when both solutions came in contact.

[0028] The solid formed was filtered, dried and weighted, and its composition was determined dissolving a known quantity of the solid in a concentrated inorganic acid, analyzing the elemental composition of this solution using Inductively Coupled Plasma (ICP) spectroscopy. The results indicated that the compound corresponds to the molecular formula K.sub.2(VO).sub.3[Fe(CN).sub.6].sub.215H.sub.2O. The resulting yield of this reaction was of 98%; thus, 98% of the vanadium initially dissolved in solution was successfully recovered.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
cathodic current densityaaaaaaaaaa
temperatureaaaaaaaaaa
electric currentaaaaaaaaaa
Login to View More

Abstract

A process for recovering vanadium contained in inorganic acid solutions by precipitating the vanadium as a solid compound of vanadium and alkali metal or monovalent cation ferricyanide. Separation is carried out electrochemically by depositing the compound on to a metal immersed in the acid solution that contains vanadium, to which a ferricyanide salt of an alkali metal or a monovalent cation has been added. If the inorganic acid present in solution is different from nitric acid, the vanadium can be also separated by direct addition of a ferricyanide salt of an alkali metal or a monovalent cation to the acid solution containing vanadium. The method described allows recovery of vanadium without modifying the initial composition of the solution, except for the concentration of the vanadium dissolved.

Description

[0001] The invention refers to a chemical process that recovers the vanadium contained in inorganic acid solutions, precipitating it as a solid compound of vanadium and alkaline metal or monovalent cation ferrocyanide. Separation is carried out electrochemically, depositing the compound on to a metal immersed in the acid solution that contains vanadium as well as other dissolved metals, to which a ferrocyanide salt of an alkaline metal or a monovalent cation has been previously added. If the inorganic acid present in solution is different from nitric acid, the vanadium can be also separated by direct addition of a ferrocyanide salt of an alkaline metal or a monovalent cation to the acid solution containing vanadium. The method described allows recovery of vanadium without modifying the initial composition of the solution, except for the concentration of the vanadium dissolved.TECHNICAL BACKGROUND[0002] A method to separate dissolved vanadium in acid solutions is presented here. Thes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(United States)
IPC IPC(8): C01G49/00C22B34/22
CPCC01G49/009C22B34/225Y02P10/20
Inventor SCHARIFKER, BENJAMINARENARE, ROSSANA
Owner UNIVE SIMON BOLIVAR
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com