Silk fibroin fiber bundles for matrices in tissue engineering

a technology tissue engineering, applied in the field of silk fiber bundles, can solve the problems of severe limitations in mobility, pain and discomfort, loss of the ability to participate in sports and exercise, etc., and achieve the effect of enhancing the differentiation and tissue development process

Inactive Publication Date: 2005-04-28
ALLERGAN INC
View PDF24 Cites 70 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0009] The present invention provides a novel silk-fiber-based matrix for producing ligaments and tendons ex vivo. More specifically, the present invention is directed to engineering mechanically and biologically functional anterior cruciate ligament using a novel silk-fiber-based matrix that may be seeded with pluripotent cells, such as bone marrow stromal cells (BMSCs). The mechanically and biologically autologous or allogenic anterior cruciate ligament comprised of the novel matrix a

Problems solved by technology

The ACL serves as a primary stabilizer of anterior tibial translation and as a secondary stabilizer of valgus-varus knee angulation, and is often susceptible to rupture or tear resulting from a flexion-rotation-valgus force associated with sports injuries and traffic accidents.
Ruptures or tears often result in severe limitations in mobility, pain and discomfort, and the loss of an ability to participate in sports and exercise.
It is widely known throughout the medical community that the ACL has poor healing capabilities.
To date, no surgical repair procedure has been shown to restore knee function completely, and novel treatment options would likely benefit a large number of patients.
The problems associated with the use of synthetic ACL replacem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Silk fibroin fiber bundles for matrices in tissue engineering
  • Silk fibroin fiber bundles for matrices in tissue engineering
  • Silk fibroin fiber bundles for matrices in tissue engineering

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0086] a. Preparation of Silk Films

[0087] Raw Bombyx mori silkworm fibers, shown in FIG. 1A, were extracted to remove sericin, the glue-like protein coating the native silk fibroin (see FIG. 1A-C). The appropriate number of fibers per group were arranged in parallel and extracted in an aqueous solution of 0.02M Na2CO3 and 0.3% (w / v) Ivory soap solution for 60 min at 90° C., then rinsed thoroughly with water to extract the glue-like sericin proteins.

[0088] b. Preparation of and Properties of the Silk-Fiber Based Matrix Construct

[0089] Costello's equation for a three-strand wire rope was derived to predict mechanical properties of the silk-fiber-based matrix. The derived model is a series of equations that when combined, take into account extracted silk fiber material properties and desired matrix geometrical hierarchy to compute the overall strength and stiffness of the matrix as a function of pitch angle for a given level of geometrical hierarchy

[0090] The material properties of...

example 2

Cell Isolation and Culture

[0097] Bone Marrow Stromal Cells (BMSC), pluripotent cells capable of differentiating into osteogenic, chondrogenic, tendonogenic, adipogenic and myogenic lineages, were chosen since the formation of the appropriate conditions can direct their differentiation into the desired ligament fibroblast cell line (Markolf et al., J. Bone Joint Surg. 71A: 887-893 (1989); Caplan et al., Mesenchymal stem cells and tissue repair. In The Anterior Cruciate Ligament: Current and Future Concepts, Ed. D. W. Jackson et al., Raven Press, Ltd, New York (1993); Young et al., J. Orthopaedic Res. 16: 406-413 (1998)).

[0098] Human BMSCs were isolated from bone marrow from the iliac crest of consenting donors ≦25 years of age by a commercial vendor (Cambrex, Walkersville, Md.). Twenty-two milliliters of human marrow was aseptically aspirated into a 25 ml syringe containing three milliliters of heparinized (1000 units per milliliter) saline solution. The heparinized marrow solution...

example 3

[0105] Studies are conducted to provide insight into the influence of directed multi-dimensional mechanical stimulation on ligament formation from bone marrow stromal cells in the bioreactor system. The bioreactor is capable of applying independent but concurrent cyclic multi-dimensional strains (e.g., translation, rotation) to the developing ligaments. After a 7 to 14 day static rest period (time post seeding), the rotational and translation strain rates and linear and rotational deformation are kept constant for 1 to 4 weeks. Translational strain (3.3%-10%, 1-3 mm) and rotational strain (25%, 90°) are concurrently applied at a frequency of 0.0167 Hz (one full cycle of stress and relaxation per minute) to the silk-based matrices seeded with BMSCs; an otherwise identical set of bioreactors with seeded matrices without mechanical loading serve as controls. The ligaments are exposed to the constant cyclic strains for the duration of the experiment days.

[0106] Following the culture pe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Temperatureaaaaaaaaaa
Forceaaaaaaaaaa
Forceaaaaaaaaaa
Login to view more

Abstract

The present invention provides a novel silk-fiber-based matrix having a wire-rope geometry for use in producing a ligament or tendon, particularly an anterior cruciate ligament, ex vivo for implantation into a recipient in need thereof. The invention further provides the novel silk-fiber-based matrix which is seeded with pluripotent cells that proliferate and differentiate on the matrix to form a ligament or tendon ex vivo. Also disclosed is a bioengineered ligament comprising the silk-fiber-based matrix seeded with pluripotent cells that proliferate and differentiate on the matrix to form the ligament or tendon. A method for producing a ligament or tendon ex vivo comprising the novel silk-fiber-based matrix is also disclosed.

Description

FIELD OF THE INVENTION [0001] The present invention is directed to a matrix or scaffold used in the production of bioengineered tissue, particularly ligaments and tendons. More particularly, the invention relates to a novel silk-fiber-based matrix upon which pluripotent cells may be seeded ex vivo and which proliferate and differentiate thereon into an anterior cruciate ligament for implantation into a recipient in need thereof. BACKGROUND OF THE INVENTION [0002] Every year, hundreds of thousands of Americans sprain, tear, or rupture ligaments and tendons of the knee, elbow, hand, shoulder, wrist and jaw (Langer et al., Science 260: 920-926 (1993)). Of particular importance is the anterior cruciate ligament of the knee. More than 200,000 people in the U.S. alone, will tear or rupture their anterior cruciate ligament (ACL) each year (Albright et al., 1999. Chapter 42-Knee and Leg:Soft-Tissue Trauma. In Orthopaedic Knowledge Update 6. American Academy of Orthopaedic Surgeons). ). The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61F2/08A61K35/12A61K38/17C12M1/00A61L27/00A61L27/22A61L27/38B32B27/04C12M3/00C12N5/00C12N5/02C12N5/071C12N5/10
CPCA61F2/08Y10T428/298A61K38/17A61L27/227A61L27/3608A61L27/3662A61L27/3804A61L27/3821A61L27/386A61L27/3895A61L27/48A61L2430/10C12N5/066C12N2533/50A61K35/12A61F2/00C07K14/43518A61K9/70C08L89/00Y10T428/249921Y10T442/2566A61P19/00A61P19/04A61P21/00A61P9/00A61K35/28A61L27/3834C12N5/0663
Inventor ALTMAN, GREGORY H.KAPLAN, DAVID L.HORAN, REBECCA L.HORAN, DAVID J.
Owner ALLERGAN INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap