Semi-crisp corundum fine grinding abrasive band

A semi-brittle corundum and fine grinding technology, which is applied in the field of semi-brittle corundum fine grinding belts, can solve the problems of low work efficiency, poor heat resistance and flexibility, and poor self-sharpening of abrasive grains, so as to improve the smoothness and precision, The effect of overcoming poor heat resistance and excellent heat resistance

Active Publication Date: 2008-03-19
JIANGSU FENGMANG COMPOUND MATERIAL SCI&TECH GRP CO LTD
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the adhesives for fine grinding belts in the domestic market are composed of phenolic resin, dispersant, thinner, etc., and phenolic resin has its own insurmountable shortcomings: high brittleness and poor flexibility, so that the existing fine grinding belts The adhesives in the grinding process The medium strength is not high, the heat resistance and flexibility are not good, and the heat dissipation is not fast, so that the abrasive debris is not easy to separate from the abrasive grains, resulting in poor self-sharpening of the abrasive grains
Therefore, the existing fine grinding abrasive belts have short service life, low work efficiency, low frequency of grit renewal and grinding during operation, and are easy to scratch the surface of the workpiece.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Semi-crisp corundum fine grinding abrasive band

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] This embodiment is a semi-brittle corundum fine grinding belt, which is composed of a cloth base, an adhesive, and a grinding material. The grinding material is semi-brittle corundum. The grinding material is bonded to the cloth base through an adhesive. The adhesive is composed of the following weight percentage: grouped into:

[0035] First-stage thermosetting phenolic resin 36%

[0036] Diphenolic propane type epoxy resin 4%

[0037] Melamine resin 1.8%

[0038] Boron 0.1%

[0039] SPAN-60 0.3%

[0040] Silane coupling agent 0.3%

[0041] Ethylene glycol ether 5%

[0042] Calcium Carbonate 26%

[0043] Sodium fluoroaluminate 26%

[0044] XeF2 0.5%.

[0045] When specifically preparing the adhesive of the present invention, first the first-order thermosetting phenolic resin of 36kg, the diphenolic propane type epoxy resin of 4kg, the melamine resin of 1.8kg are mixed into the modified synthetic resin of 41.8kg, after stirring and mixing evenly, then Add 0.1kg...

Embodiment 2

[0047] This embodiment is a semi-brittle corundum fine grinding belt, which is composed of a cloth base, an adhesive, and a grinding material. The grinding material is semi-brittle corundum. The grinding material is bonded to the cloth base through an adhesive. The adhesive is composed of the following weight percentage: grouped into:

[0048] First-stage thermosetting phenolic resin 39%

[0049] Diphenol propane type epoxy resin 5%

[0050] Melamine resin 2%

[0051] Boron 0.3%

[0052] Tween-60 0.2%

[0053] Titanate coupling agent 0.1%

[0054] Methanol 4%

[0055] Calcium Carbonate 24%

[0056] Sodium fluoborate 25%

[0057] XeF4 0.4%.

[0058]When specifically preparing the adhesive of the present invention, first mix 39kg of first-order thermosetting phenolic resin, 5kg of diphenolic propane type epoxy resin, and 2kg of melamine resin into 46kg of modified synthetic resin. After stirring and mixing evenly, add 0.3 The boron of kg, the Tween-60 of 0.2kg, the tita...

Embodiment 3

[0060] This embodiment is a semi-brittle corundum fine grinding belt, which is composed of a cloth base, an adhesive, and a grinding material. The grinding material is semi-brittle corundum. The grinding material is bonded to the cloth base through an adhesive. The adhesive is composed of the following weight percentage: grouped into:

[0061] First-stage thermosetting phenolic resin 40%

[0062] Diphenol propane type epoxy resin 4.5%

[0063] Melamine resin 2.6%

[0064] Boron 0.5%

[0065] Polyglyceride 0.1%

[0066] Aluminate coupling agent 0.2%

[0067] Ethanol 6%

[0068] Calcium Carbonate 23%

[0069] Calcium Fluoride 23%

[0070] XeF6 0.1%.

[0071] When specifically preparing the adhesive of the present invention, first the first-order thermosetting phenolic resin of 40kg, the diphenolic propane type epoxy resin of 4.5kg, the melamine resin of 2.6kg are mixed into the modified synthetic resin of 47.1kg, after stirring and mixing, Then add 0.5kg of boron, 0.1kg...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an abrasive belt, a semi-friable alumina finishing abrasive belt in detail. The abrasive belt consists of a fabric base, an adhesive and grinding material, wherein the grinding material is the semi-friable alumina and usually is adhered to the fabric base by the adhesive. The abrasive belt is characterized in that the adhesive consists of the following components of the specific weight percentage: 36percentage-40percentage A-stage thermosetting phenolic resin; 4 percentage-5.5 percentage diphenol-propane epoxy resin; 1.8 percentage-2.8 percentage melamine resin; 0.1 percentage-0.6 percentage boron; 0.1 percentage-0.3 percentage dispersant; 0.1 percentage-0.3 percentage resin acceptor; 2 percentage-6 percentage thinner;18 percentage-26 percentage calcium carbonate; 18 percentage-26 percentage fluoride salt; and 0.1 percentage-0.5 percentage inert gas fluoride. The adhesive of the invention equips with sufficient strength, excellent heat resistance and necessary flexibility in the grinding process. The finishing abrasive belt combined with the semi-friable alumina has the advantages of good sharpness and high hardness, thus improving the degree of finish and precision of the work-pieces requiring processing.

Description

technical field [0001] The invention relates to an abrasive belt, in particular to a semi-brittle corundum fine abrasive belt. Background technique [0002] With the rapid development of the machinery industry, the requirements for coated abrasive products are getting higher and higher, and the consumption is also increasing. In the grinding process of the surface treatment of metal structural parts, various requirements are also put forward for the grinding of the workpiece to be ground. [0003] Economically developed countries such as Japan and South Korea have produced fine grinding abrasive belt products that can prevent scratches on the surface of the ground workpiece and have high processing accuracy. Precisely process the surface of metal products. At present, the fine grinding belts produced by domestic manufacturers have the defects that the surface of the base material is relatively moist, the heat dissipation of the resin is not fast, the abrasive particles are ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B24D11/00B24D3/32C09J161/06C09J163/00C09J161/28
Inventor 王荣生
Owner JIANGSU FENGMANG COMPOUND MATERIAL SCI&TECH GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap