High specific gravity tungsten alloy material and preparation method for nano crystal block thereof

A tungsten alloy, high specific gravity technology, applied in the field of high specific gravity tungsten alloy material and its nanocrystalline bulk preparation, can solve the problems of not obtaining nanocrystalline bulk material, increase production cost, harsh sintering equipment, etc., and achieve the material preparation process The effect of route simplification, efficiency improvement, and short sintering time

Inactive Publication Date: 2008-03-26
SOUTH CHINA UNIV OF TECH
View PDF0 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the composition formula of tungsten alloy and the selection of sintering process, nanocrystalline bulk materials have not been obtained.
In addition, because the spark plasma sintering method mainly uses a single pulse current to sinter the powder, in order to realize the full sintering and densification of the powder body, a higher requirement is put forward for the peak intensity of the pulse current, which brings more stringent requirements on the sintering equipment. Requirements directly increase equipment investment, resulting in increased production costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Step 1: Formula of high specific gravity tungsten alloy

[0029] The components and their contents in terms of mass percentage are: tungsten W: 93.0%, nickel Ni: 4.5%, iron Fe: 1.5%, cobalt Co: 1.0%, containing unavoidable trace impurities;

[0030] Tungsten, nickel, iron and cobalt are all added in the form of simple substances. Among them, the diameter of tungsten powder is about 2.3-2.7μm, and the purity is ≥99.0%; the diameter of nickel powder is about 1-3μm, and the purity is ≥99.8%; iron powder Flat particle diameter is about 1-3μm, purity ≥99.5%; cobalt powder flat particle diameter is about 1-3μm, purity ≥99.0%;

[0031] Step 2: Mix the powder

[0032] Dry mix in V-0.002 type powder mixer for 24 hours according to the mass percentage of the above powder raw materials;

[0033] Step 3: High energy ball milling

[0034] The ball milling process was completed in a QM-2SP20 planetary ball mill, the material of the balls and the inner wall of the ball mill cylinde...

Embodiment 2

[0038] Step 1: Formula of high specific gravity tungsten alloy

[0039] The components and their contents in terms of mass percentage are: W: 93.0%, Ni: 3.5%, Fe: 2.0%, Co: 1.5%, containing unavoidable trace impurities.

[0040] Tungsten, nickel, iron and cobalt are all added in the form of simple substances. Among them, the diameter of tungsten powder is about 2.3-2.7μm, and the purity is ≥99.0%; the diameter of nickel powder is about 1-3μm, and the purity is ≥99.8%; iron powder Flat particle diameter is about 1-3μm, purity ≥99.5%; Co powder flat particle diameter is about 1-3μm, purity ≥99.0%;

[0041] Step 2: Mix the powder

[0042] Dry mix in V-0.002 type powder mixer for 24 hours according to the mass percentage of the above powder raw materials;

[0043] Step 3: High energy ball milling

[0044] The ball milling process was completed in a QM-2SP20 planetary ball mill, the material of the balls and the inner wall of the ball mill cylinder was YG8 hard alloy, the mass r...

Embodiment 3

[0048] Step 1: Formula of high specific gravity tungsten alloy

[0049] The components and their contents in terms of mass percentage are: W: 93.0%, Ni: 4.0%, Fe: 1.8%, Co: 1.2%, containing unavoidable trace impurities.

[0050]Tungsten, nickel, iron and cobalt are all added in the form of simple substances, among which, the diameter of tungsten powder is about 2.3-2.7μm, and the purity is ≥99.0%; the diameter of nickel powder is about 1-3μm, and the purity is ≥99.8%; Co powder Flat particle diameter is about 1-3μm, purity ≥99.0%; iron powder flat particle diameter is about 1-3μm, purity ≥99.5%;

[0051] Step 2: Mix the powder

[0052] Dry mix in a V-0.002 type powder mixer for 24 hours according to the mass percentage of the above powder raw materials;

[0053] Step 3: High energy ball milling

[0054] The ball milling process was completed in a QM-2SP20 planetary ball mill, the material of the balls and the inner wall of the ball mill cylinder was YG8 hard alloy, the mass...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Densityaaaaaaaaaa
Densityaaaaaaaaaa
Login to View More

Abstract

The present invention relates to high tungsten alloy material and the preparation process of its nanometer crystal lump. The materials including W 93.0 wt%, Ni 3.5-4.5 %, Fe 1.5-2.0 %, Co 1.0-1.5 % and small amount of inevitably impurity are mixed, high energy ball milled until the W phase crystal grains are refined to nanometer level, and DC pulse-constant current sintered quickly at the pressure of 40-50 MPa for 3-8 min to obtain the high tungsten alloy material with nanometer crystal lumps. The high tungsten alloy material has high mechanical performance.

Description

technical field [0001] The invention relates to plastic forming technology and powder metallurgy technology, in particular to a high-specific-gravity tungsten alloy material and a method for preparing nanocrystal blocks thereof. Background technique [0002] Due to its high density, excellent mechanical properties and good corrosion resistance, tungsten-based alloys have broad application prospects in the defense industry and civilian industry. The existing tungsten-based high-density alloys are mainly composed of matrix tungsten and binder phases such as nickel, cobalt, and iron, and are mainly prepared by methods such as hot isostatic pressing, radiation heating sintering, and induction sintering. Among them, due to the long sintering time and high sintering temperature of the hot isostatic pressing and radiation heating sintering methods, the structure of the sintered material obtained is relatively coarse, which is not conducive to improving the performance of the sinter...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C27/04C22C1/04B22F9/04B22F3/105
Inventor 李小强李元元郑峰屈胜官夏伟
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com