Macromer compound with porous cross-linking structure and preparation method thereof
A technology of cross-linked structure and macromonomer, which is applied in the field of processing and preparation of macromonomer compounds to achieve the effect of stabilizing the structure
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0032] The poly(2-methyl-1,3-adipate propyl ester) and 2.7g diisocyanate that take by weighing 10g dihydroxyl-terminated are dissolved in 40ml acetone respectively, and diisocyanate acetone solution is transferred in the there-necked flask, polyadipate Transfer the isobutylene adipate acetone solution into a separatory funnel, add 0.1g of dibutyltin dilaurate, slowly drop the polyisobutylene adipate acetone solution into a three-necked flask, stir, and react in a water bath at 35°C for 5 hours , the temperature of the water bath was raised to 50°C, 1.6g of hydroxyethyl methacrylate and 0.05g of dibutyltin dilaurate were added, the stirring was continued, the reaction was carried out for 5 hours, and the material was discharged to obtain a macromonomer acetone solution with a macromonomer weight concentration of 26 %. Structural formula such as (1), wherein: n=10;
[0033] The molecular weight of dihydroxy-terminated poly(2-methyl-1,3-propyl adipate) was 2,000.
[0034] The i...
Embodiment 2
[0045] Add 0.1 g of benzoyl peroxide and 6 g of polyhydroxybutyrate valeric acid copolyester into 45 g of the above-mentioned macromonomer acetone solution, stir, pour the solution into a petri dish, put it in an oven, and evaporate at 50 ° C Solvent, and then place the material on a flat bed (model XLB-D350) produced by Shanghai Dehong Rubber and Plastic Machinery Co., Ltd. to press the film.
[0046] The macro monomer thermally initiates cross-linking polymerization under the action of an initiator, the curing temperature is strictly controlled at 70°C, the cross-linking time is 30 minutes, and the material is discharged to obtain a cured cross-linked polymer film.
[0047]Then soak the cured cross-linked polymer film in acetone for 24 hours to wash away the polyhydroxybutyrate copolyester to obtain the product. The measured porosity is 55% (chemical fiber irregularity test method FZ / T 50002-1991).
[0048] The test results are as follows:
[0049] Using dichloromethane as...
Embodiment 3
[0054] Add 0.12g of potassium persulfate and 4g of polyhydroxybutyrate valeric acid copolyester into 45g of the above-mentioned macromonomer acetone solution, stir, pour the solution into a petri dish, put it into an oven, and evaporate the solvent at 50°C. Then the material is placed on a flat vulcanized bed (model XLB-D350) produced by Shanghai Dehong Rubber and Plastic Machinery Co., Ltd. to press the film.
[0055] The macro monomer thermally initiates cross-linking polymerization under the action of an initiator, the curing temperature is strictly controlled at 60°C, the cross-linking time is 45 minutes, and the material is discharged to obtain a cured cross-linked polymer film.
[0056] Then soak the cured cross-linked polymer film in acetone for 24 hours to wash away the polyhydroxybutyrate copolyester to obtain the product. The measured porosity is 65% (chemical fiber irregularity test method FZ / T 50002-1991).
[0057] The test results are as follows:
[0058] Using ...
PUM
Property | Measurement | Unit |
---|---|---|
porosity | aaaaa | aaaaa |
voidage | aaaaa | aaaaa |
voidage | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com