Halogen-free anti-flaming transparent unsaturated polyester insulated dope and preparation method thereof
An insulating coating, unsaturated technology, used in polyester coatings, coatings, etc., to achieve the effect of improving weather resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0020] Example 1
[0021] 60g of maleic anhydride, phthalic anhydride, and propylene glycol with a molar ratio of 1:1:2.2 were subjected to melt polycondensation reaction, and 40g of styrene and 0.05g of p-benzene were added during the cooling process of the obtained unsaturated polyester prepolymer Diphenol, if mixed evenly, is unsaturated polyester resin.
[0022] 80g of the above unsaturated polyester resin, 9g of resorcinol bis(diphenyl phosphate), 5g of butanol etherified amino resin, 5g of methyl phenyl silicone resin (molar of organic group and silicon atom) The ratio is 1.1, the phenyl group accounts for 80% by mole percent of the organic group), 1g of dicumyl peroxide is stirred and mixed at 40°C for 0.5 hours, which is a halogen-free flame-retardant transparent unsaturated polyester insulating coating.
Example Embodiment
[0023] Example 2
[0024] Melt polycondensation reaction of 60g of maleic anhydride, phthalic anhydride, terephthalic acid, propylene glycol, and diethylene glycol with a molar ratio of 2:1:1:2.2:2 to obtain unsaturated polyester During the cooling process of the prepolymer, 40g vinyl toluene and 0.1g hydroquinone are added, and the mixture is evenly mixed to form an unsaturated polyester resin.
[0025] 50g of the above unsaturated polyester resin, 5g of oligomeric bisphenol A bis(diphenyl phosphate), 13g of butanol etherified amino resin, 30g of methyl phenyl silicone resin (organic group and silicon atom The molar ratio is 1.6, and the phenyl group accounts for 30% by mole percentage of organic groups.), 2g of 1,1-bis(tert-butylperoxy)-3,3,5-trimethylcyclohexane are stirred and mixed at 10°C 3 hours, it is halogen-free flame-retardant transparent unsaturated polyester insulating coating.
Example Embodiment
[0026] Example 3
[0027] 60g of maleic anhydride, phthalic anhydride, propylene glycol, and dipropylene glycol with a molar ratio of 1:1:1.2:1 were subjected to melt polycondensation reaction, and 40g of the obtained unsaturated polyester prepolymer was added during cooling. Methyl methacrylate, 0.2g hydroquinone, mixed evenly, becomes unsaturated polyester resin.
[0028] 66g of the above-mentioned unsaturated polyester resin, 15g of triphenyl phosphate, 5g of methanol etherified amino resin, 13.5g of methyl phenyl silicone resin (the molar ratio of organic groups to silicon atoms is 1.3, phenyl accounts for organic The base mole percentage is 50%), 0.5g parts of ethyl-3,3-bis(tert-butylperoxy)butyrate are stirred and mixed for 1 hour at 20°C, which is a halogen-free flame-retardant transparent unsaturated polyester Insulating paint.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap