High activity biological super-strong water absorption resin and preparation method thereof
A technology of water-absorbing resin and high activity, applied in the field of polymers, can solve the problems of porosity, poor salt resistance, high production cost, poor water absorption performance, etc., and achieve the effect of low price, low cost and strong liquid absorption capacity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0011] Example 1: Add 100 parts of acrylic acid to the reactor according to parts by mass, adjust the pH of the system to 5-7 with 40% sodium hydroxide aqueous solution, and then add 5 parts of corn starch, 5 parts of attapulgite to the system, 0.01 1% NN methylene bisacrylamide solution with a concentration of 1%, 0.01 part of 1% potassium persulfate aqueous solution, stir uniformly; heat up to 40°C, polymerize for about 2 hours, and stop stirring when the system is translucent; Continue to heat up to 60°C and polymerize for about 1 hour, the system becomes gel, the gel is taken out and granulated, dried; crushed into semi-finished products, and then sequentially added with NN methylene bisacrylamide with a mass of 0.1% of the semi-finished product and a concentration of 1% The solution, and the EM solution with 0.05% of the mass of the semi-finished product and the concentration of 5%, are stirred evenly, placed in an airflow drying box, and heated to 100°C for secondary surface...
Example Embodiment
[0013] Example 2: Add 100 parts of acrylic acid to the reactor by mass parts, adjust the pH of the system to 5-7 with 40% sodium hydroxide aqueous solution, and then sequentially add 10 parts of corn starch and 20 parts of white sericite to the system. 0.05 parts of glycerol solution with a concentration of 5%, 0.05 parts of hydrogen persulfate aqueous solution with a concentration of 1%, stir evenly; heat up to 35°C, polymerize for about 1.5 hours, stop stirring when the system is translucent gel; continue to heat up After polymerization at 70°C for about 2 hours, the system becomes a gel. The gel is taken out and granulated, dried; crushed into semi-finished products, and then sequentially added the NN methylene bisacrylamide solution with 0.5% of the mass of the semi-finished products and 5% concentration. The semi-finished EM liquid with 0.01% mass and 5% concentration is stirred evenly, placed in an airflow drying box, and heated to 90°C for secondary surface cross-linking tr...
Example Embodiment
[0015] Example 3: Add 100 parts of acrylic acid to the reactor by mass parts, adjust the pH of the system to 5-7 with 40% sodium hydroxide aqueous solution, and then add 20 parts of corn starch, 40 parts of kaolin, 1 part of kaolin to the system in sequence A polyvinyl alcohol solution with a concentration of 1%, a 1% cerium ammonium nitrate solution with a concentration of 1%, stir evenly; heat up to 45°C, polymerize for about 2 hours, stop stirring when the system is translucent gel; continue to heat up to 55 After polymerization at ℃ for about 2 hours, the system becomes gel, the gel is taken out and granulated, dried; pulverized into semi-finished products, and then sequentially added the NN methylene bisacrylamide solution with 0.5% of the semi-finished product mass and the concentration of 10% and the semi-finished product mass 0.5%, 10% concentration of EM solution, stir evenly, put it in the airflow drying box, heat up to 70 ℃ for secondary surface cross-linking treatment,...
PUM
Property | Measurement | Unit |
---|---|---|
Water absorption | aaaaa | aaaaa |
Water absorption | aaaaa | aaaaa |
Water absorption | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap