Sewage water body refuse type cement and method of preparing the same

A mud and sewage technology, applied in cement production, clay products, other household appliances, etc.

Inactive Publication Date: 2009-01-14
江苏金大地建材科学研究院有限公司
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In summary, so far, there have been no reports of other better environmentally friendly sludge treatment methods.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sewage water body refuse type cement and method of preparing the same
  • Sewage water body refuse type cement and method of preparing the same
  • Sewage water body refuse type cement and method of preparing the same

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038]Its preferred and practical preparation method is: add appropriate amount of water to the raw materials of the above-mentioned components by weight, process them into balls in a mixer molding machine (or other mixer), and dry them naturally to form raw balls; then put the raw balls in In the drying and roasting kiln (such as tunnel kiln, etc.), it is first dried in a low-temperature drying belt at 100-200°C for 20-40 minutes, then roasted in a high-temperature baking belt at 500-1000°C for 50-100 minutes, and then cooled naturally after leaving the kiln. The mature material ball is the sewage cement slag product; finally, the sewage cement slag product and cement clinker are mixed together at a ratio of 30% to 5%: 70% to 95% and ground into powder, which is the sewage cement slag cement. Sewage cement slag products can be ground into powder and then mixed with cement at a ratio of 30% to 5%: 70% to 95% to form sewage cement slag cement. The above-mentioned roasting tempe...

Embodiment 2

[0044] The sewage cement slag cement mixed with the slag powder of the existing commercial cementing material and the sewage cement slag product in a certain proportion is used as the cementitious material. For performance comparison, the results are shown in Table 2:

[0045] Table 2: Performance comparison between sewage cement slag cement and several commonly used cements

[0046]

[0047]

[0048] It can be seen from Table 2 that the sewage cement slag cement that is formed by mixing a certain proportion of sewage cement products into the existing commercial slag powder is used as a cementitious material, and its flexural strength, compressive strength and wear resistance, frost resistance, The drying shrinkage performance is higher than that of ordinary cement, road cement and composite cement not mixed with sewage cement slag products. It can be seen that it can be used in place of ordinary cement, road cement and composite cement.

Embodiment 3

[0050] Sewage cement slag cement (serial number 2-5 in the table) mixed by adding a certain proportion of sewage cement slag products into the commercial slag cement is used as the cementitious material and commercial slag cement (serial number 1 in the table) is used as the glue respectively. Concrete materials were tested and compared in terms of physical properties such as strength, wear resistance, frost resistance, and dry shrinkage according to the ISO relevant cement physical property test standards. The test results are shown in Table 3:

[0051] Table 3: Performance comparison between sewage cement slag cement and slag cement with different mixing ratios

[0052]

[0053] It can be seen from Table 3 that the flexural strength, compressive strength, abrasion resistance, frost resistance, dry shrinkage and other properties of the sewage cement slag cement mixed with a certain proportion of sewage cement products in the existing commercial slag cement are higher than ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to waste water sludge type cement, which is mainly mixed by cement and a product of waste water sludge. The product of waste water sludge is prepared by the method that waste water sludge, and acetylene gas slag or lime sludge, or waste water sludge, acetylene gas slag or lime sludge, bauxite slag, phosphogypsum or desulfurization gypsum, mineral slag and fly ash are in certain proportion with proper water to be added into a mixing and molding machine so as to be processed into nodules, after the nodules are naturally air dried into raw meal nodules, the raw meal nodules are dried and roasted, and the product of waste water sludge is prepared. Then the product of waste water sludge and cement clinker are mixed together in certain proportion to be ground into powder, that is, the waste water sludge type cement; or the product of waste water sludge is ground into powder, then the powder is mixed together with cement, and the waste water sludge type cement is formed. The product of waste water sludge can be mixed with pure clinker cement, and can be also mixed with other commercial cement. The method can process the waste water sludge, which is discharged from the waste water processing factories and is difficult to be processed, into high quality cement that has advantages of large demand, less investment, high wear-resisting strength, good frost resistance performance, small dry shrinkage performance, being favorable for environmental protection and reducing cost.

Description

technical field [0001] The invention relates to a new cement, in particular to a sewage cement slag cement produced by using sewage sludge discharged from a sewage treatment plant as a raw material, and provides a practical preparation method for it, belonging to the field of environmental protection or cement. Background technique [0002] Sewage cement slag in sewage treatment plants is the waste residue discharged from domestic sewage mainly by gravity concentration and mechanized dehydration. The organic matter that improves the soil structure also contains pathogenic microorganisms, parasites (eggs), heavy metals and some refractory organic poisons. The moisture content is 70-80%, so it is very difficult to develop and utilize. [0003] In order to deal with these sludges, many people at home and abroad have thought of many ways. The methods are mainly landfilling, stacking, throwing the sludge into the ocean, incineration, composting and so on. In the coming years of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B7/24C04B7/36
CPCC04B28/02C04B33/1324C04B33/135C04B7/24C04B18/023C04B33/1321Y02P40/10Y02P40/60Y02W30/91C04B7/40C04B18/103C04B18/0418
Inventor 谭纪林
Owner 江苏金大地建材科学研究院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com