Completely degradable plant protein wood adhesive and preparation thereof

A wood adhesive and plant protein technology, which is applied in the field of fully degradable plant protein wood adhesive and its preparation, can solve the problems of less research on plant protein, and achieve the effects of simple process operation, high bonding strength, and short curing time

Active Publication Date: 2009-04-22
郑州佰沃科技发展有限公司
View PDF0 Cites 29 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the research on the use of vegetable protein to make wood adhesives is mainly focused on the modification of soybean protein, and there are relatively few studies on other vegetable proteins.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Embodiment 1: fully degradable vegetable protein wood adhesive formulation (parts by weight) is:

[0030] Gluten 9

[0031] water 100

[0032] Citric acid 0.77

[0033] Disodium hydrogen phosphate 2.21

[0034] Phosphorus oxychloride 0.5

[0035] Carbon tetrachloride 2.5

[0036] Glycerin 0.5

[0037] Potassium sorbate 0.1.

[0038] The preparation process is as follows: dissolving citric acid and disodium hydrogen phosphate in water at 20-30 DEG C to prepare a buffer solution with a pH of 6.0, adding gluten powder while stirring to disperse evenly to form an emulsion. Dissolve phosphorus oxychloride in carbon tetrachloride in advance to form a 20% (v / v) solution. While stirring, the phosphorus oxychloride solution was slowly added dropwise to the reaction system, and the dropwise addition was completed within 10 minutes. Keep the stirring speed constant, and keep the temperature for 60 minutes. 5 minutes before the end of the reaction, glycerol and potassium s...

Embodiment 2

[0039] Embodiment 2: the fully degradable vegetable protein wood adhesive formulation (parts by weight) is:

[0040] Defatted soybean meal 10

[0041] water 100

[0042] Acetic anhydride 1

[0043] Sodium polyacrylate 0.1

[0044] Dehydroacetic acid 0.25

[0045] Sodium bentonite 5

[0046] The preparation process is as follows: the weighed defatted soybean powder is slowly added into water preheated to 50° C., the feeding time is controlled at 5 to 10 minutes, and the stirring speed is 150 rpm during the adding process. After stirring to form a uniform emulsion, acetic anhydride was added to the reaction system in 5 times, and the addition was completed within 10 minutes. The stirring speed was reduced to 75r / min, and the reaction was incubated for 90 minutes. When the reaction was carried out to 80 minutes, sodium polyacrylate and dehydroacetic acid were added. After the reaction is over, lower the temperature to 20°C to 30°C, add sodium bentonite, and continue stirring...

Embodiment 3

[0047] Embodiment 3: fully degradable vegetable protein wood adhesive formulation (parts by weight) is:

[0048] Defatted Rapeseed Meal 10

[0049] water 100

[0050] Sodium carbonate 11.5

[0051] Sodium bicarbonate 0.5

[0052] Sodium Lauryl Sulfate 0.5

[0053] Mercaptoethanol 0.2

[0054] Butyl p-hydroxybenzoate 0.2

[0055] Octanol 0.2

[0056] Kaolin 5.

[0057] The preparation process is as follows: Sodium carbonate and sodium bicarbonate are prepared into aqueous solutions with a concentration of 0.1mol / L, and the two are mixed at a ratio of 4:6 to form a buffer solution. Preheat the buffer solution to 55°C, add defatted rapeseed powder while stirring, the stirring speed is 100r / min, and the addition is completed within 5 minutes. Keep the stirring speed constant, add sodium lauryl sulfate and mercaptoethanol in turn, and keep warm for 60 minutes. Octanol was added during the reaction to eliminate the foam generated by the reaction. Five minutes before the en...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
release amountaaaaaaaaaa
Login to View More

Abstract

The invention relates to a full biodegradable plant protein wood adhesive and a preparation method thereof, and belongs to the technical field of adhesive. The adhesive is prepared from the following components in weight portion: 100 portions of water, 5 to 20 portions of plant protein powder, 0 to 15 portions of acidity regulator, 0.05 to 20 portions of modifying agent, 0.05 to 10 portions of assistant, 0.1 to 10 portions of preservative, and 0 to 10 portions of stuffing. The preparation method comprises the following steps in turn: adding the water into a container, and dissolving the acidity regulator under a stirring state; adding the plant protein powder into the container under the stirring state; at the same time, complementing the acidity regulator according to change situations of pH values; heating a reaction system to a temperature needed by modification reaction, adding the modifying agent and the assistant into the container under the stirring state, and keeping the temperature to make the mixture reacted for 15 to 240 minutes at a temperature of between 5 and 60 DEG C; and in the last 2 to 5 minutes of the temperature keeping reaction, adding the preservative into the solution, and stirring the mixture evenly; and adding the stuffing into the reaction system, stirring evenly the mixture, and finally obtaining the wood adhesive. The adhesive has the advantages that the adhesive is easy to process, good in adhering property, and degradable.

Description

technical field [0001] The invention belongs to the technical field of adhesives, in particular to a fully degradable vegetable protein wood adhesive and a preparation method thereof. Background technique [0002] Wood adhesives are generally polymer compounds, which can be divided into natural polymer adhesives and synthetic polymer adhesives according to their different raw material sources. Natural polymer adhesives have a very long history in our country, and were also widely used in the United States and Europe in the first half of the last century. Because it mainly uses natural substances as raw materials, there are a large number of hydrophilic groups such as hydroxyl groups in the molecule, and its water resistance, heat resistance and bonding strength are not ideal, which limits its wide application in industry. Since the 1960s, with the expansion of the wood-based panel industry, the demand for adhesives has also increased, thus promoting the development of synth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J189/00
Inventor 杨立新陈锡建
Owner 郑州佰沃科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com