Method for preparing ZrB2-Al2O3 composite powder

A zrb2—al2o3, composite powder technology, applied in the field of ceramics and refractory materials, can solve the problems of high production cost, need for special atmosphere, complex self-propagating synthesis equipment, etc., and achieve the effect of low synthesis cost, easy to obtain, and small particle size

Inactive Publication Date: 2009-05-06
SINOSTEEL LUOYANG INST OF REFRACTORIES RES
View PDF2 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Yang Zhenguo et al. adopted the self-propagating method. The disadvantages of this method are: the self-propagating synthesis equipment is complex, requires a special atmosphere, and the production cost is high.
Chen Haigong et al. adopted high-energy ball milling method, but its disadvantage is that high-energy ball milling equipment and special atmosphere are needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Will Fe 2 o 3 Powder (purity 90%, particle size 100 μm) and metal Al powder (purity 90%, particle size 100 μm) were weighed at a molar ratio of 1:2 and put into a ball mill tank for ball milling and dry mixing. 3 hours.

[0020] Metal Al powder (purity 99%, particle size 50μm), ZrO 2 Powder (purity 99%, particle size 45 μm), and B 2 o 3 The powder (purity 99%, particle size 45μm) is weighed at a molar ratio of 10:3:3, put into a ball mill tank and dry-mixed evenly. The volume ratio of the ball to the material is 3:1. Ball mill for 3 hours. Pressed into a green body under pressure.

[0021] The green body is surrounded by carbon felt and placed in the middle of a ceramic container, buried with thermite, and ignited with magnesium strips. After the reaction is over, the reactants are crushed and sieved to obtain ZrB with a purity of 96% and a particle size of 6-9 μm. 2 —Al 2 o 3 Composite powder.

Embodiment 2

[0023] Will Fe 2 o 3 Al powder (purity 90%, particle size 100 μm) and metal Al powder (purity 92%, particle size 74 μm) were weighed in a molar ratio of 1:2, put into a ball mill jar and dry-mixed evenly, the volume ratio of ball to material was 2:1, and ball mill 4 hours.

[0024] Metal Al powder (purity 99.3%, particle size 38μm), ZrO 2 (purity 99%, particle size 38 μm), and B 2 o 3 The powder (purity 99%, particle size 45μm) is weighed according to the molar ratio of 10:3:3.5, put into the ball mill and dry-mixed evenly. Pressed into a green body under pressure.

[0025] The pressed green body is surrounded by carbon felt and placed in the middle of a ceramic container, buried with thermite and ignited with magnesium strips. After the reaction is finished, the reactant is crushed and sieved to obtain a product with a purity of 97% and a particle size of 5-8 μm.

Embodiment 3

[0027] Will Fe 2 o 3 Al powder (purity 92%, particle size 80 μm) and metal Al powder (purity 94%, particle size 74 μm) were weighed at a molar ratio of 1:2.1 and put into a ball mill tank for ball milling and dry mixing. The volume ratio of ball to material was 2:1. 5 hours.

[0028] Metal Al powder (purity 99.5%, particle size 25μm), ZrO 2 Powder (purity 99.3%, particle size 20 μm), and B 2 o 3 The powder (purity 99%, particle size 38 μm) is weighed according to the molar ratio of 10:3:4, put into the ball mill tank and dry-mixed evenly. The volume ratio of ball to material is 3:1. Ball mill for 5 hours. Pressed into a green body under pressure.

[0029] The pressed green body is surrounded by carbon felt and placed in the middle of a ceramic container, buried with thermite and ignited with magnesium strips. After the reaction is finished, the reactant is crushed and sieved to obtain a product with a purity of 98% and a particle size of 5-7 μm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of ceramics and refractory materials, and particularly relates to a method for preparing ZrB2-Al2O3 composite powder. Fe2O3 powder and metal Al powder are taken as raw materials of a thermit, the metal Al powder, ZrO2 powder and B2O3 powder are taken as raw materials for synthesizing the ZrB2-Al2O3 composite powder, and the heat emitted by a thermit reaction is utilized to ignite a reaction for synthesizing the ZrB2-Al2O3 composite powder. The method has a simple preparation technology, does not need special equipment and atmosphere, has cheap needed raw materials and small energy consumption and using time, and is environment-friendly; and the synthesized powder has high purity, fine granularity, and low manufacturing cost.

Description

technical field [0001] The invention belongs to the technical field of ceramics and refractory materials, and in particular relates to a method for preparing ZrB 2 —Al 2 o 3 Method of composite powder. Background technique [0002] ZrB 2 It is a metalloid structure compound of C32 type in the hexagonal system. The Zr-B ionic bond between the boron atomic face and the zirconium atomic face and the strong bond of the B-B covalent bond determine the ZrB 2 Ceramic has the characteristics of high melting point, high hardness, high stability, good electrical conductivity, thermal conductivity and good corrosion resistance, and is a high-temperature ceramic material with excellent performance. ZrB 2 Ceramics have been widely used in the fields of high-temperature structural ceramic materials, composite materials, refractory materials, electrode materials, and nuclear control materials. But due to ZrB 2 Ceramics have a high melting point, are not easy to sinter, and their own...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/66
Inventor 王刚王来稳周继伟王龙庆周军李代兵
Owner SINOSTEEL LUOYANG INST OF REFRACTORIES RES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap