Ultraviolet curing coating for preventing static on plastic surface and method for preparing the same

A technology of curing coatings and ultraviolet light, applied in conductive coatings, coatings, etc., can solve the problems of poor anti-static durability, high environmental damage, and high energy consumption, and achieve the effect of saving space, good electrical conductivity, and meeting environmental friendliness.

Inactive Publication Date: 2009-05-06
SICHUAN UNIV
View PDF3 Cites 52 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Adopting ultraviolet light curing technology solves the problems of high environmental hazards, high energy consumption and poor antistat

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0041] Aromatic polyurethane acrylate (CN970A60, Sartomer Company)…………… 75g

[0042] High-purity trimethylolpropane triacrylate (SR351HP, Sartomer Company)... 25g

[0043] 2-Hydroxy-2-methyl-1-phenylacetone (Darocur1173, Swiss Ciba Specialty Chemicals)... 5g

[0044] Nano-ATO powder (National Superfine Powder Engineering Research Center)…………………… 25g

[0045] Leveling agent (Levelol835, Deqian company) …………………………… 0.5g

[0046] Defoamer (Defom5300, Deqian Company) …………………………………… 0.3g

[0047] Wetting and dispersing agent (Disponer9250, Deqian Company)…………………… 1.5g

[0048] (1) Mix reactive diluent high-purity trimethylolpropane triacrylate and nano-ATO powder according to the ratio, add wetting and dispersing agent, and ultrasonically disperse for 20 minutes; (2) After mixing aromatic polyurethane acrylate and Darocur1173, Stir evenly at 50°C; (3) After mixing the components obtained in steps (1) and (2), add a leveling agent and an antifoaming agent, and stir and mix thoro...

example 2

[0051] Epoxy acrylate (CNUVE150 / 80, Sartomer Company)………………… 20g

[0052] Aliphatic urethane acrylate (CN965, Sartomer Company)……………… 30g

[0053] 1,6-Hexanediol diacrylate (SR238, Sartomer Company)………… 20g

[0054] High-purity trimethylolpropane triacrylate (SR351HP, Sartomer Company)... 30g

[0055] 2-Hydroxy-2-methyl-1-phenylacetone (Darocur1173, Swiss Ciba Specialty Chemicals)...3g

[0056] 1-Hydroxycyclohexylbenzophenone (Irgacure184, Swiss Ciba Specialty Chemicals)... 3g

[0057] Composite conductive mica powder (Chengdu Institute of Organic Chemistry, Chinese Academy of Sciences)…………… 15g

[0058] Leveling agent (Levelol837, Deqian company) ……………………… 0.5g

[0059] Defoamer (Defom2700, Deqian Company)……………………… 0.3g

[0060] Wetting and dispersing agent (Disponer912, Deqian company) ………………… 2g

[0061] (1) Mix reactive diluent 1,6-hexanediol diacrylate, high-purity trimethylolpropane triacrylate, Darocur1173 and Irgacur184 according to the proportioning ratio, and s...

example 3

[0064] Fatty acid modified epoxy diacrylate (6109A, Jiangsu Sanmu Group) 50g

[0065] 1,6-Hexanediol diacrylate (SR238, Sartomer Company)……………… 25g

[0066] High-purity trimethylolpropane triacrylate (SR351HP, Sartomer Company)... 25g

[0067] 1-Hydroxycyclohexylbenzophenone (Irgacure184, Swiss Ciba Specialty Chemicals)………… 3g

[0068] Benzophenone (Runtecure1020, Changzhou Huatai Chemical Company) ... 2g

[0069] Active amine (P115, Belgian Eubicil Company) ……………………………… 4g

[0070] Composite conductive mica powder (Chengdu Institute of Organic Chemistry, Chinese Academy of Sciences)……………… 10g

[0071] Nano-ATO powder (National Superfine Powder Engineering Research Center)………………… 10g

[0072] Leveling agent (Levelol495, Deqian company) ……………………………… 0.5g

[0073] Defoamer (Defom3100, Deqian Company)…………………………… 0.3g

[0074] Wetting and dispersing agent (Disponer9220, Deqian Company) …………………… 3g

[0075] Ethyl acetate (analytically pure, Chengdu Kelong Chemical Reagent Fa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an ultraviolet photo-cured coating for the electrostatic prevention of the surface of plastic and a preparation method thereof, in particular to a photo-cured coating containing conductive powder of a metal oxide system or composite conductive powder. The coating comprises the following compositions in weight percent: 30 to 70 percent of oligomer, 25 to 65 percent of active thinner, 0.5 to 10 percent of light evocating agent, 5 to 40 percent of conductive powder, 0.2 to 8 percent of additive and 0 to 50 percent of solvent. As the added conductive powder of the metal oxide system and the composite conductive powder is white or light color, the prepared photo-cured has the characteristic of easy color modulation, has lasting antistatic property, high rigidity and wearing resistance, can be used for electrostatic prevention of the surface of electronic equipment, plastic vessel, shell of an electric appliance, office supplies, sports equipment and other plastic products.

Description

technical field [0001] The invention relates to an ultraviolet curable coating for antistatic plastic surface and a preparation method thereof, which is characterized in that the photocurable coating is prepared by using metal oxide conductive powder or composite conductive powder, which has antistatic durability, adjustable color, and is very durable. High hardness and wear resistance and other characteristics. Background technique [0002] Plastic has the characteristics of light weight, good design flexibility, low price and durability. It is increasingly used in industrial production and daily life instead of metal or wood materials. However, it is a good choice due to its high surface resistance and low dielectric constant. Insulators are prone to static electricity due to friction or impact, resulting in the accumulation of a large amount of static electricity on the plastic surface, which can easily cause surface dust collection, affect the appearance quality of the p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D4/02C09D5/24C08J7/04
Inventor 黄婉霞智茂永刘兴豪何鹏刘小杰
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka