Method of preparing oxidation methyl tin

A technology of methyl tin oxide and methyl tin chloride, which is applied in the direction of tin organic compounds, can solve problems such as difficult industrial production, alcohol safety, hidden danger conversion rate, etc., and achieve good product quality, stable quality, and no environmental pollution Effect

Active Publication Date: 2009-11-25
衢州建华南杭药业有限公司
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Chinese patent CN01813770.9 reports that organic tin oxides are formed by reacting powdered tin metal and alcohol at a high temperature of about 200-400°C. According to this method, monoalkyltin, dialkyltin and trialkyltin are produced in a certain yield. Alkyl tin oxide, this method introduces alcohol into tin powder to generate organic tin oxide at high temperature, and cools down to collect the product. The disadvantage is that alcohol has potential safety hazards at high temperature and the conversion rate is low, so it is not easy for industrial production
At present, there is no relevant technical report on other methods for preparing methyl tin oxide

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Add 120g of monomethyl tin trichloride and 240g of water into a stirred reactor, stir until all solids are dissolved, raise the temperature to 50°C, slowly and uniformly add 606g of 10% aqueous sodium hydroxide solution dropwise, and the reaction time is 3 hours , the reaction temperature is controlled at 70°C, and the reaction is completed when the measured pH value is 8.0, the reaction solution is filtered, the filtrate is an aqueous solution of sodium chloride, the sodium chloride is recovered by dehydration, and the solid matter obtained after the filter cake is washed twice with water is dehydrated at 80°C Dry to obtain monomethyl tin oxide 81.1g, yield is 98.1%.

Embodiment 2

[0022] The monomethyl tin trichloride in embodiment 1 is replaced by dimethyl tin dichloride, consumes 10% aqueous sodium hydroxide solution is 441g, other conditions are constant, obtains dimethyl tin oxide 88.5g, yield is 98.5%.

Embodiment 3

[0024] The monomethyl tin trichloride in embodiment 1 is changed into monomethyl tin trichloride and dimethyl tin dichloride mixture, and its molar ratio is 25: 75, and concentration is 40% aqueous solution 300g, consumes 10 The % sodium hydroxide aqueous solution was 441g, and 88.5g of a mixture of monomethyl tin oxide and dimethyl tin oxide was obtained, and the yield was 98.5%.

[0025] In Example 1, the impact of different raw material concentrations, reaction temperature, alkali species, alkali concentration, reaction times, and pH value control on product quality and yield is shown in Table 1:

[0026] Table 1: Example data sheet of monomethyltin oxide produced from monomethyltin trichloride

[0027]

serial number

Monomethyltin trichloride and water

Amount to weight ratio

temperature reflex

base name

Alkali concentration

Reaction time (h)

end of reaction

Point PH

yield ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A method of preparing oxidation methyl tin belongs to the technical field of preparing method of chemical products. The method comprises the steps as follows: adding chloride methyl tin into a reactor, adding with water to stir until totally solving, heating up to 50 to 60 DEG. C; slowing and uniformly dropping alkali metal hydroxide solution or ammonia, the reaction temperature being 30 to 110 DEG. C, the reaction time being 2 to 5 hours, the reaction terminal being controlled at PH value 7 to 9, finally filtering the reaction solution, washing and purifying, the obtained solid being the oxidation methyl tin. The method of preparing oxidation methyl tin is simple and the production is easily controlled; the prepared products have excellent and stable quality and high yield. The prepared oxidation methyl tin is easily stored and transported, and is conveniently applied, and can be the raw materials of preparing thiol methyl tin and organic acid methyl tin such that the cost of preparing thiol methyl tin and organic acid methyl tin is obviously reduced; the production process has no pollution to the environment, and the production is easily controlled, the prepared products have excellent and stable quality.

Description

technical field [0001] The invention belongs to the technical field of preparation methods of chemical products, in particular to a preparation method of methyl tin oxide. Background technique [0002] Chinese patent CN01813770.9 reports that organic tin oxides are formed by reacting powdered tin metal and alcohol at a high temperature of about 200-400°C. According to this method, monoalkyltin, dialkyltin and trialkyltin are produced in a certain yield. Alkyl tin oxide, this method introduces alcohol into tin powder to generate organic tin oxide at high temperature, and cools down to collect the product. The disadvantage is that alcohol has potential safety hazards at high temperature and the conversion rate is low, so it is not easy for industrial production. At present, no relevant technical reports on other methods for preparing methyltin oxide have been found. Contents of the invention [0003] For the above-mentioned problems existing in the prior art, the object of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C07F7/22
Inventor 唐吉元
Owner 衢州建华南杭药业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products