Fine inorganic ceramic powder aggregate and preparing method thereof

A technology of inorganic ceramics and ceramic powders, applied in the direction of inorganic pigment treatment, chemical instruments and methods, fibrous fillers, etc., can solve the problems of difficult control of production costs and high energy consumption, and achieve superior physical and chemical indicators and stable chemical properties , Increase the effect of hardness and steel strength

Inactive Publication Date: 2009-12-30
章建利 +1
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But in the end, because of the high energy consumption in the process of waste porcelain conversion, it is difficult to control the production cost, and the good original intention was abandoned under the obstruction of corporate interests.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A fine inorganic ceramic powder aggregate consists of the following components in parts by weight:

[0027] Ceramic powder material 40

[0028] Aluminate coupling 0.6

[0029] Polyethylene wax 0.45

[0030] Zinc stearate 0.15

[0031] Atactic polypropylene 0.5

[0032] Antioxidant 168 0.15

[0033] Antioxidant 1010 0.08

[0034] Anti-ultraviolet agent UV-531 0.15

[0035] Decabromane 2

[0036] Antimony silicon trioxide 1

[0037] ACR processing aid 0.7

[0038] Appropriate amount of pigment

[0039] A kind of preparation method of fine inorganic ceramic powder aggregate, its specific steps are:

[0040] 1. Prepare the raw materials according to the above weight ratio;

[0041] 2. Grinding and sieving the ceramic fragments to obtain a powder material with a fineness of 800 mesh;

[0042] 3. Put the ceramic powder material into the high mixer for dehydration and drying treatment, so that the water content is 3‰;

[0043] 4. Put the aluminate coupling, polyet...

Embodiment 2

[0047] Ceramic powder material 50

[0048] Aluminate coupling 0.8

[0049] Polyethylene wax 0.75

[0050] Zinc stearate 0.35

[0051] Atactic polypropylene 0.8

[0052] Antioxidant 168 0.14

[0053] Antioxidant 1010 0.07

[0054] Anti-ultraviolet agent UV-531 0.13

[0055] Decabromane 1.8

[0056]Antimony silicon trioxide 0.8

[0057] ACR processing aid 0.6

[0058] Appropriate amount of pigment

[0059] A kind of preparation method of fine inorganic ceramic powder aggregate is the same as embodiment 1.

Embodiment 3

[0061] Ceramic powder material 60

[0062] Aluminate Coupling 1

[0063] Polyethylene wax 0.9

[0064] Calcium stearate 0.45

[0065] Atactic polypropylene 0.9

[0066] Antioxidant 168 0.12

[0067] Antioxidant 1010 0.06

[0068] Anti-ultraviolet agent UV-531 0.12

[0069] Decabromane 1.6

[0070] Antimony silicon trioxide 0.7

[0071] ACR processing aid 0.5

[0072] Appropriate amount of pigment

[0073] A kind of preparation method of fine inorganic ceramic powder aggregate is the same as embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of inorganic materials, in particular to fine inorganic ceramic powder aggregate and a preparing method thereof. The fine inorganic ceramic powder aggregate comprises the components of a plasticizer, an internal lubricant and an external lubricant, a crosslinking modifying agent, a filling agent, a flame retardant, paint and ceramic powder aggregate. In the technical scheme, the highly filled powder aggregate is prepared by adopting the mechanism of copolymerization and cladding of inorganic ceramic powder and other media, and the treatment problem of solid waste-ceramic scrap is effectively solved.

Description

technical field [0001] The invention belongs to the field of inorganic materials, in particular to a fine inorganic ceramic powder aggregate and a preparation method thereof. Background technique [0002] Ceramic manufacturers will produce a large amount of waste porcelain during the production process. These manufacturers generally hope to make full use of these waste porcelain to reduce production costs and solid waste pollution. However, since the waste porcelain has no plasticity after being ground into powder, the plasticity of the ceramic material added with the waste porcelain powder will become poor, it is not easy to shape, and the firing temperature is also high, so it can only be used as a ceramic filler in a small amount, and the dosage is generally 15 %the following. Therefore, there are still a large number of waste ceramics being dumped and landfilled, seriously polluting the environment, not only occupying land, blocking rivers, polluting farmland, affecting...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08K13/06C09C3/00C09C3/04C09C3/10C09C3/08C08L23/06
Inventor 章建利徐月明
Owner 章建利
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com