Catalyst for dehydrogenation of C16-C19 long chain normal alkanes and preparation method and application thereof

A C16-C19, dehydrogenation catalyst technology, applied in the direction of metal/metal oxide/metal hydroxide catalysts, chemical instruments and methods, physical/chemical process catalysts, etc., can solve the dehydrogenation of long-chain alkanes, there is no literature Reporting, low stability, unable to meet the requirements of industrial use, etc.

Active Publication Date: 2010-02-10
PETROCHINA CO LTD +1
View PDF42 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But specifically for C 16 -C 19 Catalysts for the dehydrogenation of long-chain alkanes have not been reported in the literature so far in the world
And the catalyzer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Catalyst for dehydrogenation of C16-C19 long chain normal alkanes and preparation method and application thereof
  • Catalyst for dehydrogenation of C16-C19 long chain normal alkanes and preparation method and application thereof
  • Catalyst for dehydrogenation of C16-C19 long chain normal alkanes and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] γ-Al 2 o 3 Preparation of vector

[0027] Mix aluminum hydroxide, pseudo-boehmite and kale powder with a weight ratio of 8:1:1 evenly, add 15% nitric acid, stir and extrude into strips with an extruder, and then dry at 120°C for 4 hours , roasted at 650°C for 8 hours, crushed into 18-20 mesh particles, and finally treated with steam at 650°C for 8 hours. The physical and chemical properties of the obtained carrier are: bulk specific gravity 0.68 g / ml, specific surface area 198 m 2 / g, average particle crushing strength 112 N / cm, pore volume 0.61 cm 3 / g, the average pore diameter is 135nm, of which 0~10nm pores account for 38%, and 100~2000nm pores account for 40%.

Embodiment 2

[0029] Catalyst preparation

[0030] Get the Al prepared in Example 1 2 o 3 50ml of the carrier is placed in an incubator, and at the same time, take 4.4ml of chloroplatinic acid aqueous solution containing 0.02g / ml of platinum, 2.4ml of concentrated hydrochloric acid, 4.5ml of stannous chloride aqueous solution containing 0.06g / ml of tin, and 0.06g / ml of iron 0.9 milliliters of ferric chloride aqueous solution, 2.0 milliliters of potassium chloride aqueous solution containing potassium 0.1 g / ml, add deionized water so that the volume of soaking solution is 42 ml. Add the above impregnating solution into an impregnator equipped with a carrier, impregnate evenly and dry, then roast in a muffle furnace at 500°C for 4 hours, then in the roasting furnace with an air flow rate of 200 ml / min and a water flow rate of 40 g / hour, 500 Treat with 30% steam for 4 hours at ℃, stop the water and continue air cooling, and reduce with pure hydrogen (purity>99.9%) with water content less tha...

Embodiment 3

[0035] long chain n-alkanes C 18 Dehydrogenation to Monoolefins

[0036] On the fixed-bed reactor, the catalyst prepared in Example 2 is evaluated for the long-chain alkane dehydrogenation reaction. 18 Alkanes are raw materials, at a pressure of 0.14 MPa (gauge pressure) and a liquid space velocity of 20 -1 , the ratio of hydrogen to hydrocarbon is 600:1 (volume ratio), and the reaction is carried out under the condition of controlling the initial outlet temperature of the catalyst bed at 455° C., and the conversion rate of normal alkanes is calculated by analyzing the dehydrogenation product components. Orthomorphic C 18 For the alkane conversion rate-time curve, see figure 1 (A).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a catalyst for dehydrogenation of C16-C19 long chain normal alkanes and a preparation method and application thereof. The catalyst comprises the following components in percentage by weight: 0.2 to 0.5 percent of platinum, 0.4 to 2.0 percent of tin, 0.1 to 2.0 percent of iron, 0.4 to 2.0 percent of potassium and the balance of large-pore strip alumina with dual-pore distribution; and the catalyst is used in a reaction for the dehydrogenation of C16-C19 long chain normal alkanes to prepare monoolefine, the conversion rate is 11.4 percent, and the selectivity is 91.9 percent; the catalyst can undergo C16-C19 catalytic dehydrogenation reaction for a long time; and alkylbenzene sulfonate synthesized by dehydrogenized products can have ultra interfacial tension in a wide alkali concentration range for oil-water in actual oil field, and compared with the oil displacement performance of a byproduct of C10-C13 alkylbenzene, namely heavy alkylbenzene sulfonate, the alkali concentration is shifted to the low-concentration direction, and the interface activity of a sample is better.

Description

Technical field: [0001] The present invention relates to a method for C 16 -C 19 A dehydrogenation catalyst for long-chain normal alkanes, a preparation method and application thereof. This catalyst is mainly used for heavy liquid wax (C 16 -C 19 ) dehydrogenation to produce monoolefins and then synthesize heavy alkylbenzene sulfonates and use them in the tertiary oil recovery process of oilfields. Background technique: [0002] Some old oilfields in our country have reached the high water cut period after a long period of exploitation, and the crude oil recovery has shown a downward trend. In order to maintain a stable and high yield, tertiary oil recovery technology must be adopted. The research and application of ASP ASP flooding (alkali, surfactant, polymer) technology has become a leading technology for enhancing oil recovery in my country. The core of ASP ASP flooding technology is surfactant. In recent years, petroleum sulfonate, lignin sulfonate, petroleum carb...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J23/89C07C5/333C09K8/584
Inventor 孙承林戴锡海何松波王斌杜鸿章白子武杨旭段霞赵玲张力郭奇
Owner PETROCHINA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap