A desulfurized gypsum, gypsum-based technology, applied in the field of gypsum-based self-leveling materials and their preparation, can solve the problems of high cost, poor strength, etc., and achieve the effects of low cost, excellent performance, and cheap and easily available raw materials

Inactive Publication Date: 2010-02-17
江苏仁和建材科技有限公司
View PDF0 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These two mold powders have their own advantages and disadvantages. The former has

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing gypsum-based self-leveling material by using desulfurization gypsum
  • Method for preparing gypsum-based self-leveling material by using desulfurization gypsum

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0025] Example 1:

[0026] By weight, take 60 parts of gypsum powder prepared from desulfurized gypsum, 0.1 part of citric acid, 0.5 part of methyl cellulose ether, 3 parts of Portland cement, 0.3 part of polycarboxylate water reducer, 0.1 part of defoamer, 1 part of redispersible latex powder was put into the mixer, mixed for 20 minutes, the speed of the mixer was 60 rpm, and then mixed with 35 parts of sand, the mixing time was 10 minutes, and the stirring speed was 60 rpm to obtain the finished gypsum-based self-leveling 100 materials.

Example Embodiment

[0027] Embodiment 2:

[0028] By weight, take 60 parts of gypsum powder prepared from desulfurized gypsum, 0.1 part of sodium citrate, 0.5 part of hydroxypropyl methyl cellulose ether, 3 parts of Portland cement, 0.3 part of sulfonated melamine water reducer, 0.1 part of foaming agent and 1 part of redispersible latex powder were put into a mixer, mixed for 20 minutes, the speed of the mixer was 60 rpm, and then mixed with 35 parts of sand, the mixing time was 10 minutes, and the stirring speed was 60 rpm to obtain 100 parts of finished gypsum-based self-leveling material.

Example Embodiment

[0029] Embodiment three:

[0030] By weight, take 62.9 parts of gypsum powder prepared from desulfurized gypsum, 0.3 part of sodium polyphosphate, 0.5 part of hydroxypropyl methyl cellulose ether, 0.2 part of sulfonated melamine water reducer, 0.1 part of defoamer, and recyclable 1 part of disperse latex powder and 5 parts of talc powder were put into a mixer, mixed for 20 minutes, the speed of the mixer was 60 rpm, and then mixed with 30 parts of sand, the mixing time was 10 minutes, and the stirring speed was 60 rpm to obtain the finished gypsum. Based on 100 parts of self-leveling materials.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing gypsum-based self-leveling material for use in building material industry. The main material of the gypsum-based self-leveling material is desulfurized gypsum which is a desulfurization product from power plants. The method comprises: firstly, calcining the desulfurized gypsum in a calcining kiln; and secondly, mixing calcined gypsum powder accountingfor 50 to 78 percent of the total weight of the material, a water reducer accounting for 0.1 to 1 percent of the total weight of the material, a retarder accounting for 0.01 to 0.5 percent of the total weight of the material, a water-retaining agent accounting for 0.02 to 5 percent of the total weight of the material, a reinforcing agent accounting for 0 to 10 percent of the total weight of the material, re-dispersible emulsion powder accounting for 0.2 to 1.5 percent of the total weight of the material, a defoamer accounting for 0.05 to 0.2 percent of the total weight of the material, riversand accounting for 25 to 45 percent of total weight of the material and a filler accounting for 0 to 20 percent of the total weight of the material to obtain a the high-performance gypsum-based product. The invention provides a new method for producing high-quality gypsum-based self-leveling material characterized by high strength, high flowability, small contraction deformation and low cost by using the desulfurized gypsum, which provides a new way of comprehensively using desulfurized gypsum that is a solid waste and fills the blank that the preparation of gypsum-based self-leveling materials from desulfurized gypsum lacks in China.

Description

Technical field: [0001] The invention relates to a gypsum-based self-leveling material and a preparation method thereof, in particular to a method for preparing a gypsum-based self-leveling material by using desulfurized gypsum. Background technique: [0002] With the construction of a large number of desulfurization projects in thermal power plants in my country, the emission of desulfurized gypsum has increased sharply. At present, the utilization rate of desulfurized gypsum in my country is still very low, and most of them are still stored in storage. It has become the second largest after thermal power plant fly ash. Large solid waste. If the desulfurization gypsum is discarded and stockpiled, a special storage site needs to be built, which not only requires a huge investment, occupies a lot of valuable land resources, but also has an adverse impact on the surrounding living environment. Therefore, the use of desulfurized gypsum has an important impact on national enviro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B11/26C04B28/14C04B111/62
Inventor 李东旭韩永圣权刘权
Owner 江苏仁和建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap