Method for heat resistant rare earth-magnesium alloy engine pistons through squeezing and casting

A technology of squeeze casting and rare earth magnesium, which is used in engine components, machines/engines, pistons, etc., to achieve the effects of excellent piston performance, increased comfort, and improved life.

Active Publication Date: 2010-04-14
SHANGHAI JIAO TONG UNIV
View PDF2 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, the magnesium alloy squeeze casting method is used to prepare

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for heat resistant rare earth-magnesium alloy engine pistons through squeezing and casting
  • Method for heat resistant rare earth-magnesium alloy engine pistons through squeezing and casting
  • Method for heat resistant rare earth-magnesium alloy engine pistons through squeezing and casting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The alloy composition (percentage by weight) of the magnesium alloy engine piston: 10% Gd, 3% Y, 2% Zn, 0.3% Zr, the impurity element is less than 0.02%, and the rest is Mg.

[0027] The concrete steps of the melting process of the alloy are as follows:

[0028] (1) Configure the alloy according to the above ingredients, preheat the pure magnesium and the master alloy used to 200°C in an oven, and keep it warm for 2 hours;

[0029] (2) Mg smelting: Add industrial pure magnesium into the smelting furnace, heat and smelt, and protect it with a covering agent at the same time;

[0030] (3) Add Y and Gd: Add the dried Mg-Y and Mg-Gd master alloys to the magnesium liquid at a temperature of 730°C;

[0031] (4) Adding Zn: After the master alloy is completely melted, add industrial pure zinc at a temperature of 700°C;

[0032] (5) Adding Zr: Raise the temperature of the magnesium liquid to 760°C, then add the Mg-Zr master alloy, stir for 2 minutes to promote its full melting...

Embodiment 2

[0038] The alloy composition (percentage by weight) of the magnesium alloy engine piston: 12% Gd, 2% Y, 1% Zn, 0.4% Zr, the impurity element is less than 0.02%, and the rest is Mg.

[0039] The concrete steps of the melting process of the alloy are as follows:

[0040] (1) Configure the alloy according to the above ingredients, preheat the pure magnesium and the master alloy used to 200°C in an oven, and keep it warm for 2 hours;

[0041] (2) Mg smelting: Add industrial pure magnesium into the smelting furnace, heat and smelt, and protect it with a covering agent at the same time;

[0042] (3) Add Y and Gd: Add the dried Mg-Y and Mg-Gd master alloys to the magnesium liquid at a temperature of 725°C;

[0043] (4) Adding Zn: After the master alloy is completely melted, add industrial pure zinc at a temperature of 700°C;

[0044] (5) Adding Zr: Raise the temperature of the magnesium liquid to 760°C, then add the Mg-Zr master alloy, stir for 2 minutes to promote its full melting...

Embodiment 3

[0050] The alloy composition (percentage by weight) of the magnesium alloy engine piston: 10% Gd, 3% Y, 1% Zn, 0.4% Zr, the impurity element is less than 0.02%, and the rest is Mg.

[0051] The concrete steps of the melting process of the alloy are as follows:

[0052] (1) Configure the alloy according to the above ingredients, preheat the pure magnesium and the master alloy used to 200°C in an oven, and keep it warm for 2 hours;

[0053] (2) Mg smelting: Add industrial pure magnesium into the smelting furnace, heat and smelt, and protect it with a covering agent at the same time;

[0054] (3) Add Y and Gd: Add the dried Mg-Y and Mg-Gd master alloys to the magnesium liquid at a temperature of 730°C;

[0055] (4) Adding Zn: After the master alloy is completely melted, add industrial pure zinc at a temperature of 700°C;

[0056] (5) Adding Zr: Raise the temperature of the magnesium liquid to 760°C, then add the Mg-Zr master alloy, stir for 2 minutes to promote its full melting...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Fatigue strengthaaaaaaaaaa
Fatigue strengthaaaaaaaaaa
Fatigue strengthaaaaaaaaaa
Login to view more

Abstract

A method for heat resistant rare earth-magnesium alloy engine pistons through squeezing and casting comprises preparing master alloy Mg-Y, Mg-Gd, Mg-Zr, industrial pure magnesium and industrial pure zinc, smelting alloy, obtaining magnesium alloy fused mass, squeezing and casting the magnesium alloy fused mass, obtaining the primary blank of a magnesium alloy piston, and obtaining a heat resistant tare earth-magnesium alloy engine piston through orderly carrying out the solid solution treatment, the cold treatment and the aging treatment. The heat resistant rare earth-magnesium alloy engine pistons prepared by the invention have light weight, simple technology and receivable cost, and further have very excellent high-temperature intensity and creep resistance performance and good fatigue intensity, and can better satisfy the service requirements of engine pistons.

Description

technical field [0001] The invention relates to a method in the technical field of automobile manufacturing, in particular to a method for preparing a heat-resistant rare earth magnesium alloy engine piston by squeeze casting. Background technique [0002] The piston is one of the most important parts in the engine, because it works under the conditions of high temperature, high pressure, corrosion, friction, and high-speed movement, the performance requirements of the material are very high. According to the working environment of the piston, the piston material should meet the following conditions: it should have high mechanical strength, especially high temperature strength and thermal stability; Appropriate clearance to reduce noise during mechanical operation and reduce fuel consumption; poor heat absorption and good thermal conductivity, which can transfer heat generated during work in time; large specific strength to reduce piston weight and improve work efficiency; ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C23/00C22C1/03B22D18/02C22F1/06F02F3/00
Inventor 王渠东尹冬弟陈长江
Owner SHANGHAI JIAO TONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap