Method for preparing cold-bonded pellets from iron containing sludge by compound adhesive

A technology of composite adhesive and cold-set pellets, which is applied in the field of adhesives for metallurgical ironmaking, can solve the problems of lowering the iron grade of cold-set pellets, lowering the iron-containing grade of pellets, affecting smelting energy consumption and output, etc. The effect of energy consumption, improving iron content and reducing secondary pollution

Inactive Publication Date: 2010-07-14
TONGJI UNIV
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

my country's pellets are added with an average of 4% bentonite, the most of which reaches 7-8%, and the least is no less than 2.5%, so that the iron-containing grade of the pellets decreases, which affects the energy consumption and output of smelting. Blast furnace ironmaking causes huge economic losses, and SiO2 in bentonite can also inhibit the reduction of iron, so it is urgent to develop new binders
[0005] In the process of producing cold-set pellets, if only inorganic adhesive is added, it will not only increase the cost of pelletizing, but also reduce the iron grade of cold-set pellets, which greatly restricts the use of cold-set agglomeration technology; if Only adding organic adhesives will not only reduce the bonding strength at high temperature, but also cause the thermal strength of the pellets to decrease, and even cause the pellets to burst at high temperatures

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing cold-bonded pellets from iron containing sludge by compound adhesive
  • Method for preparing cold-bonded pellets from iron containing sludge by compound adhesive
  • Method for preparing cold-bonded pellets from iron containing sludge by compound adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Composite adhesive formula is as follows: (calculated by weight fraction)

[0024]

[0025] Add vinyl acetate, acrylic acid, and sodium carboxymethyl cellulose into the four-neck bottle according to the proportion, then add water according to the proportion, stir at 90°C and 1500 rpm until the glue is evenly mixed, and then mix the glue Pour out the solution and cool it to room temperature, and finally mix the cooled glue solution with molasses evenly according to the proportion to obtain the organic adhesive A. Take bentonite, calcium oxide, high-temperature cement, and alkaline sodium hydroxide according to the proportion, and mix them evenly to obtain inorganic adhesive B.

[0026] According to the proportion, the organic adhesive A and the inorganic adhesive B are compounded and stirred evenly (the compounding ratio is 1: 1), and then added in the mixture of iron concentrate powder and iron-containing sludge according to the proportioning (the mixing ratio is: co...

Embodiment 2

[0028] Composite adhesive formula is as follows: (calculated by weight fraction)

[0029]

[0030] Add vinyl acetate, acrylic acid, and sodium carboxymethyl cellulose into the four-neck bottle according to the proportion, then add water according to the proportion, stir at 90°C and 1500 rpm until the glue is evenly mixed, and then mix the glue Pour out the solution and cool it to room temperature, and finally mix the cooled glue solution with molasses evenly according to the proportion to obtain the organic adhesive A. Take bentonite, calcium oxide, high-temperature cement, and alkaline sodium hydroxide according to the proportion, and mix them evenly to obtain inorganic adhesive B.

[0031] According to the proportion, the organic adhesive A and the inorganic adhesive B are compounded and stirred evenly (the compounding ratio is 1: 1), and then added in the mixture of iron concentrate powder and iron-containing sludge according to the proportioning (the mixing ratio is: co...

Embodiment 3

[0033] Composite adhesive formula is as follows: (calculated by weight fraction)

[0034]

[0035] Add vinyl acetate, acrylic acid, and sodium carboxymethyl cellulose into the four-neck bottle according to the proportion, then add water according to the proportion, stir at 90°C and 1500 rpm until the glue is evenly mixed, and then mix the glue Pour out the solution and cool it to room temperature, and finally mix the cooled glue solution with molasses evenly according to the proportion to obtain the organic adhesive A. Take bentonite, calcium oxide, high-temperature cement, and alkaline sodium hydroxide according to the proportion, and mix them evenly to obtain inorganic adhesive B.

[0036] According to the proportion, the organic adhesive A and the inorganic adhesive B are compounded and stirred evenly (the compounding ratio is 1: 1), and then added in the mixture of iron concentrate powder and iron-containing sludge according to the proportioning (the mixing ratio is: co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing cold-bonded pellets from sludge containing iron by an compound adhesive, belonging to the technical field of adhesives for metallurgical ironmaking. The method of the invention comprises the following concrete steps: adopting the compound adhesive of an inorganic adhesive and an organic adhesive, wherein the organic adhesive in the compound adhesive comprises the following raw materials: vinyl acetate, acroleic acid, sodium cellulose glycolate, polyvinyl alcohol, polyisobutylene, molasses and coal tar; and the inorganic adhesive comprises the following raw materials: bentonite, calcium oxide, basic sodium silicate, sodium chloride, talcum powder and light calcium carbonate. When the organic adhesive and the inorganic adhesive in the adhesive are prepared, the components are proportioned and controlled strictly in a proper order, so that the defects of one adhesive singly used can be avoided, and the compound adhesive has good caking property on the iron containing sludge. The method of the invention recycles iron from iron containing sludge and changes waste into resources, thereby reducing pollution of storage and transport on the environment, and saving the energy consumption in the sintering and high furnace production.

Description

technical field [0001] The invention belongs to the technical field of adhesives for metallurgical ironmaking, and in particular relates to a method suitable for preparing cold-set pellets by using composite adhesives in iron-containing sludge. Background technique [0002] In the production of iron-making blast furnaces and steel-making converters in iron and steel enterprises, a large amount of smoke and dust are produced, which are processed and recycled to obtain iron-containing sludge (mainly containing Fe, C, CaO and other substances) through environmental protection and dust removal. This iron-containing sludge mainly includes converter sludge and blast furnace sludge. The sludge has a large water content, and it cannot be mixed evenly when directly mixed with raw materials, and it is easy to cause the belt to stick and the feed port to be blocked during the belt conveying process. The dried sludge slabs can't be used as raw materials even if they become agglomerated....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22B1/242
Inventor 任天斌黄超韩宇朱金鑫钟震
Owner TONGJI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com