Method for spray-welding anisotropic material on sealing surface of cast iron valve plate

A technology of heterogeneous materials and sealing surfaces, applied in welding equipment, arc welding equipment, manufacturing tools, etc., can solve problems such as cracks easily, achieve the effects of increasing adhesion, reducing production costs, and simple spray welding process

Active Publication Date: 2011-11-16
TIANJIN FSK FLOW CONTROL EQUIP
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention aims to overcome the deficiencies in the prior art and provide a method for spray-welding heterogeneous materials on the sealing surface of cast iron valve plate, adopting supersonic plasma spray-welding process, spray-welding corrosion-resistant on the sealing surface of nodular cast iron valve plate , wear-resistant stainless steel, which solves the problem of easy cracks, and also reduces energy consumption and production costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for spray-welding anisotropic material on sealing surface of cast iron valve plate
  • Method for spray-welding anisotropic material on sealing surface of cast iron valve plate
  • Method for spray-welding anisotropic material on sealing surface of cast iron valve plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0008] Below in conjunction with the preferred embodiments, the specific embodiments provided by the present invention are described in detail as follows: Refer to the accompanying drawings for details, a method for spray welding heterosexual materials on the sealing surface of a cast iron valve plate, the specific process steps are as follows: 1. The valve plate Sort and check the spray welding position and the valve plate within 20mm of the adjacent two sides for oil pollution, and place the valve plate with oil pollution and the valve plate without oil pollution respectively; 2. The sealing surface of the valve plate is polished 1. The angle of the valve plate without oil pollution The mill grinds off the sharp edges on both sides of the sealing surface of the valve plate and the sharp edges at the orifice of the shaft hole, so as to make the arc transition of the sealing plate surface; 2. Soak the valve plate with synthetic water-based anti-rust cleaning agent for the valve ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for spray-welding anisotropic material on a cast iron valve plate. The specific technique includes the steps of: valve plate selecting, valve plate sealing surface polishing, sanding and coursing, adopting special valve plate sealing surface spray-welding device to spray weld the valve plate sealing surface, adjusting the current of a wire feeder to 200A-400A and the voltage to 10V-40V to maintain the wire-feeding speed at 3-8m / min, obtaining the supersonic speed particle radiation under the working conditions that the gas flow is adjusted to be 3-6 square meters per hour and the power is adjusted to be 50-80kW, opening the spray gun opening for spray-welding, ensuring the welding wire from the spray gun to form beam-shaped flame, sending two electriferous welding wires to the spray gun, generating electric arc at the contact tips of the two welding wires to form molten drops, spraying the melt molten drops through compressed air onto the surface of working piece to form a coating layer, and detecting. The invention has the beneficial effects that the spray-welding process is simple; the heating before welding and the heat processing after welding are not needed for the valve plate; the stainless steel spray-welding layer is firmly combined with the valve plate main body, the valve plate is prevented from crackles; thereby the purposes of increasing the wearing resistance and the corrosion resistance of the valve plate are achieved.

Description

technical field [0001] The invention belongs to a valve processing technology, and in particular relates to a method for spray-welding heterosexual materials on the sealing surface of a cast iron valve plate. Background technique [0002] The valve plate of the valve is usually made of ductile iron. During the use of the valve, due to the poor wear resistance and corrosion resistance of the valve plate, the valve will run out and drip after a short time of use. Valve manufacturers have been trying to improve the wear resistance and corrosion resistance of the valve plate for a long time, especially for valves used in the water treatment industry, and all parts in contact with the medium must not pollute the medium. The methods currently used are: The first method: using electric welding, this method cannot be implemented by spray welding stainless steel coating on the ductile iron valve plate. Not only the base metal is cracked, but the welding layer is also cracked; due t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K9/04
Inventor 范全军王先文
Owner TIANJIN FSK FLOW CONTROL EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com