Room-temperature curing water-based mono-component metal-plate-covered hide glue

A room temperature curing, one-component technology, applied in the direction of monocarboxylate copolymer adhesive, adhesive type, etc., can solve problems such as poor adhesion of metal plates, and achieve improved adhesion, water resistance and moisture resistance. Strength-enhancing effect

Inactive Publication Date: 2010-08-18
刘少来
View PDF3 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a room temperature curing water-based single-component metal plate covering adhesive, which can solve the shortco

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0010] Specific embodiment one: this specific embodiment adopts the following technical scheme: it is made of polyvinyl alcohol as 3.0%, vinyl acetate 40%, acrylic acid 0.2%, butyl acrylate 1.5%, tertiary vinyl carbonate 5.8%, hydroxyethyl acrylate 1.5%, 1.0% hydroxypropyl acrylate, 2.8% dibutyl phthalate, 0.11% ammonium persulfate, 0.12% sodium bicarbonate, 44% water, and 0.8% emulsifier; its preparation method is: Measure vinyl acetate, acrylic acid, butyl acrylate, vinyl tert-carbonate, hydroxyethyl acrylate, and hydroxypropyl acrylate into the monomer tank for mixing. Then put water into the dissolution kettle, turn on the stirring, slowly put in polyvinyl alcohol, sodium bicarbonate, emulsifier, then heat up to 95°C, keep it warm for 1 hour, cool down to 78°C, add 10% of the total amount of monomers % mixed monomers and 20% ammonium persulfate aqueous solution. When the emulsion in the reactor is slightly blue and there is no reflux in the condenser, start to add one-fif...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to room-temperature curing water-based mono-component metal-plate-covered hide glue, and to modified polyvinyl acetate copolymerization emulsion, which solves the problems of the prior art that the polyvinyl acetate emulsion has poor adhesion on the metal plate and the adhesive has poor water resistance, and consists of water, polyvinyl alcohol, ammonium persulfate, sodium bicarbonate, crylic acid, butyl acrylate, hydroxy-ethyl acrylate, hydroxy-propyl acrylate, vinyl versatate, vinyl acetate, emulsifier and dibutyl phthalate. Compared with the similar products both at home and abroad, the indexes of the glue such as wood-metal adhesion strength, glue membrane water resistance, minimum membrane-formation temperature and the like are greatly improved.

Description

Technical field: [0001] The invention relates to a room-temperature-curable water-based single-component metal plate covering glue, in particular polyvinyl acetate copolymerized modified emulsion, which is used for compounding metal plates and solid wood veneers. Background technique: [0002] At present, there are many types of adhesives that can be used to bond metal and non-metallic materials, but most of them are two-component, which is troublesome to use, and has certain organic volatiles, which is not conducive to environmental protection. Most of the one-component adhesives are Solvent-based adhesives have poor heat resistance, and for a small number of water-based one-component adhesives, they cannot form a strong force on metal materials. Therefore, a single-component, water-based adhesive that can bond metal plates and wood is developed. It means a lot. [0003] Polyvinyl acetate emulsion has decades of production history. It has the advantages of high strength an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J131/04C08F218/08C08F220/06C08F220/18C08F218/04C08F220/28
Inventor 刘少来
Owner 刘少来
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap