Self-crosslinking polyacrylate rubber latex, preparation method thereof and water-based paper printing ink

A polyacrylate and acrylate technology, used in papermaking, paper coatings, textiles and papermaking, etc., can solve problems such as different price differences, achieve fast drying, prevent sticking, and speed up drying.

Inactive Publication Date: 2010-10-27
SUN YAT SEN UNIV +1
View PDF2 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The reason is that domestic water-based resins cannot be diluted with ethanol, and the price of inks prepared from imported resins is about 30% to 50% higher than that of solvent-based inks. The price difference varies with different colors.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] 1. Synthetic self-crosslinking polyacrylate latex

[0050] Weigh 7.6 grams of acrylic acid, 1.0 grams of adipic acid dihydrazide, and 43.5 grams of methyl methacrylate and add them to the high tank A and mix them evenly; weigh 52.5 grams of deionized water, 0.6 grams of sodium lauryl sulfate, and 6.0 grams of acrylic acid Ethyl ester, 36.1 grams of butyl acrylate and 2.2 grams of diacetone acrylamide were added to the high tank of B and mixed evenly; weighed 0.1 grams of ammonium persulfate and dissolved it in 10 grams of deionized water to obtain an aqueous solution of C initiator; weighed 0.4 grams of persulfuric acid Dissolve ammonium in 25 grams of deionized water to obtain an aqueous solution of D initiator; in a normal-pressure reactor with temperature control and stirring, add 44 grams of deionized water and 2.5 grams of allyloxy hydroxypropanesulfonate, and stir well Then start to heat up. When the temperature reaches 75°C, add the mixture in the high position t...

Embodiment 2

[0054] 1. Synthetic self-crosslinking polyacrylate latex

[0055] Weigh 6.0 grams of methacrylic acid, 3.0 grams of methylene succinic acid, 1.8 grams of adipic acid dihydrazide, 41 grams of ethyl methacrylate, and 3 grams of isobornyl acrylate, and add them to the A high tank and mix evenly; weigh Add 60.0 grams of deionized water, 1.6 grams of DOWFAX 2A1, 0.5 grams of isotridecanyl polyoxyethylene ether of BASF company, 38 grams of 2-ethylhexyl acrylate and 3.0 grams of diacetone acrylamide into the B high tank and mix well; Take by weighing 0.2 gram of potassium persulfate and be dissolved in 12 gram of deionized water, obtain C initiator aqueous solution; Take by weighing 0.35 gram of potassium persulfate and dissolve in 28 gram of deionized water, obtain D initiator aqueous solution; Add 48 grams of deionized water and 1.55 grams of allyloxy hydroxypropyl sulfonate to the normal pressure reactor, stir well and start to heat up, when the temperature reaches 75°C, add the m...

Embodiment 3

[0059] 1. Synthetic self-crosslinking polyacrylate latex

[0060] Weigh 9.5 grams of acrylic acid, 1.4 grams of adipic acid dihydrazide, and 30 grams of butyl methacrylate and add them to the high tank A and mix them evenly; weigh 54.0 grams of deionized water, 1.0 grams of sodium dodecylbenzenesulfonate, 0.3 Add 1 gram of nonylphenol polyoxyethylene ether, 49.3 grams of butyl methacrylate and 3.5 grams of diacetone acrylamide into the high tank of B and mix evenly; weigh 0.2 grams of ammonium persulfate and dissolve it in 10 grams of deionized water to obtain C trigger Aqueous solution of D initiator; Weigh 0.3 gram of potassium persulfate and dissolve in 25 gram of deionized water to obtain aqueous solution of D initiator; In a normal pressure reactor with temperature control and stirring, add 51.5 gram of deionized water, 4.5 gram of vinyl sulfonate Sodium acid, stir well and start to heat up. When the temperature reaches 75°C, add the mixture in the high-level tank of A an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses self-crosslinking polyacrylate rubber latex, a preparation method thereof and water-based paper printing ink. The self-crosslinking polyacrylate rubber latex is prepared by the following steps: mixing an acrylic ester monomer, a hydrophilic monomer and ADH in a head tank A; mixing water, an emulsifier, the acrylic ester monomer and DAAM in a head tank B; adding water, the emulsifier and polymerizable self-emulsifying functional monomer, stirring the mixture, heating the mixture to 75 DEG C, and dripping a mixture in the head tank A and an initiator to prepare a protective colloid first; dripping the mixture in the head tank B and the initiator at 85 DEG C; and performing a constant-temperature reaction. The water-based paper printing ink is prepared by the following steps: dissolving a phenylethylene-acrylic acid polymer and a pH value regulator in water at 60 DEG C with stirring; adding a pigment and necessary assistant and mixing the mixture to prepare color paste; and uniformly mixing the color paste with the self-crosslinking polyacrylate rubber latex, a surface tension regulator and water. The water-based paper printing ink can be diluted by one or a mixture of two of water and ethanol, can be dried quickly and has high printing adaptability.

Description

technical field [0001] The invention relates to a method for making water-based paper printing ink, in particular to a method for making self-crosslinking water-based paper printing ink that can be diluted with one or two mixtures of water and ethanol. Background technique [0002] Gravure printing (referred to as gravure printing) is one of the main printing methods for high-grade paper (such as cigarette packs). With the improvement of printing substrates, equipment and processes, paper gravure printing inks are also constantly improving. Toluene solvents were used in the early 1990s, ester solvents were used in the late period, and alcohol ester solvent inks were used in this century. At present, high-end paper gravure printing inks such as cigarette labels, wine labels, and pictorials used in the market are based on alcohol ester solvents. [0003] The biggest feature of water-based inks that use water as the main solvent is that the main solvent that volatilizes when t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L33/12C08L33/10C08L33/08C08K5/25C08K5/092C08F220/14C08F220/06C08F220/18C08F220/58C08F2/24C08J3/24D21H19/58
Inventor 王小妹颜锋马军刘长来
Owner SUN YAT SEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com