Solid-phase decarburization method of high-carbon Fe-Mn alloy

A technology of high-carbon ferromanganese and ferromanganese alloys, which is applied in the field of solid-phase decarburization of high-carbon ferromanganese alloys, can solve the problems of poor overall effect of decarburization, low decarbonization efficiency, and high energy consumption of decarbonization, so as to reduce energy consumption , fast decarburization speed and simple process

Inactive Publication Date: 2011-04-06
TAIYUAN UNIV OF TECH
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Ferromanganese alloy is the most important raw material in the iron and steel industry. With the rapid development of chromium-manganese stainless steel and low-carbon alloy steel, the decarburization of high-carbon ferromanganese alloy has become a key to iron and steel metallurgy technology. Due to the high vapor pressure of manganese, The binding energy of manganese and oxygen is relatively large, which seriously affects the decarburization of liquid-phase ferromanganese, such as low decarburization efficiency, high decarbonization energy consumption, serious environmental pollution, and poor overall decarburization effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solid-phase decarburization method of high-carbon Fe-Mn alloy
  • Solid-phase decarburization method of high-carbon Fe-Mn alloy
  • Solid-phase decarburization method of high-carbon Fe-Mn alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0067] The present invention will be further described below in conjunction with accompanying drawing:

[0068] figure 1 As shown, it is the state diagram of solid-phase decarburization by microwave heating, and the positions of each part must be correct and operated in sequence.

[0069]The preparation is carried out in a microwave heating solid-phase decarburization furnace. The lower part of the microwave decarburization furnace 1 is the furnace base 2, and the upper part is the sealing cover 4 and the furnace cover 3, and the opening and closing are controlled by the opening and closing frame 5. In the furnace cover 3. The sealing cover 4 is provided with a thermocouple 13 and an air hole 10. A microwave generator 6 is provided on the furnace wall of the microwave decarburization furnace 1. The microwave generator 6 is a furnace cavity 9 in the microwave decarburization furnace 1. In the middle lower part of the furnace chamber 9 is a crucible seat 7, on the top of the cr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a solid-phase decarburization method of high-carbon Fe-Mn alloy, and the method aims at the actual situation that the carbon content of Fe-Mn alloy powder is high and adopts the solid-phase decarburization technology. The method comprises the following steps: by using calcium carbonate powder as decarbonizer and nitrogen as protective gas for decarburization, decarburization is performed in a microwave decarbonization furnace, wherein the temperature of microwave heating is 1000 DEG C, the heating time is 60min, the specific power of microwave heating is 10KW / kg and the rate of decarburization is up to 85.78%; and the obtained low and medium carbon Fe-Mn alloy is briquetted by a briquetting machine to prepare a block material for use, wherein the calcium oxide in the material is a good desulfurization and dephosphorization agent, and the generated carbon monoxide gas can be recycled. The method does not discharge metallurgical residue and cause the pollutions caused by waste gas, wastewater and residue, is a clean decarburization technology and is an ideal solid-phase decarburization method of high-carbon Fe-Mn alloy.

Description

technical field [0001] The invention relates to a solid-phase decarburization method for a high-carbon ferromanganese alloy, which belongs to the technical field of removing carbon elements from black metal ferromanganese. Background technique [0002] Ferromanganese alloy is the most important raw material in the iron and steel industry. With the rapid development of chromium-manganese stainless steel and low-carbon alloy steel, the decarburization of high-carbon ferromanganese alloy has become a key to iron and steel metallurgy technology. Due to the high vapor pressure of manganese, The binding energy between manganese and oxygen is relatively large, which seriously affects the decarburization of liquid-phase ferromanganese, such as low decarburization efficiency, high decarbonization energy consumption, serious environmental pollution, and poor overall decarburization effect. [0003] Solid-phase decarburization has the advantages of low reaction temperature, good select...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C33/00
Inventor 陈津郭丽娜刘科刘金营赵晶张猛
Owner TAIYUAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com