Gas-shielded overlaying flux cored soldering wire for repairing hot-forging mould

A technology of gas shielding and hot forging, which is applied to welding media, manufacturing tools, welding equipment, etc., can solve the problems of low efficiency, achieve the effects of small spatter, good crack resistance of welding wire, and improve production efficiency

Active Publication Date: 2011-04-27
TIANJIN YONGCHANG WELDING WIRES
View PDF6 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the repair of hot forging dies in China mainly uses surfacing electrodes, and the efficiency is low.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0012] A gas-shielded surfacing flux-cored wire for repairing hot forging molds, using SPCC-SD cold-rolled low-carbon steel strip as the wire material, adopting conventional flux-cored transition alloys, general powder specifications and flux-cored wire production process Manufacturing, the formula of welding wire flux core is composed of fluoride, calcium carbonate, feldspar, magnesia and alloy powder, the alloy powder includes iron powder, high carbon ferrochrome, electrolytic manganese, ferrosilicon, ferromolybdenum, ferrovanadium, nickel powder, tungsten powder and cobalt powder, wherein the fluoride includes calcium fluoride, sodium fluoride and barium fluoride in a mass ratio of (6:2:1), and the formula weight percentage of the welding wire flux core is fluoride 9 %, calcium carbonate 8%, feldspar 3%, magnesia 2%, high carbon ferrochrome 18%, electrolytic manganese 12%, molybdenum iron 6%, vanadium iron 4%, nickel powder 6%, tungsten powder 9%, cobalt Powder 4%, the bala...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a gas-shielded overlaying flux cored soldering wire for repairing a hot-forging mould, which is manufactured by taking SPCC-SD cold-rolling low-carbon steel belts as raw materials of a soldering wire and utilizing a conventional flux cored transient alloy way, a universal flux cored standard and a flux cored soldering wire manufacturing technique. The soldering wire flux core contains fluoride, calcium carbonate, feldspar, magnesia and alloy powder according to a proportion, wherein the fluoride comprises calcium fluoride, sodium fluoride and barium fluoride, and the alloy powder contains iron powder, high-carbon ferrochrome, electrolytic manganese, ferrosilicon, ferromolybdenum, ferrovanadium, nickel powder, tungsten powder and cobalt powder. The invention has the following beneficial effects: because the gas-shielded overlaying flux cored soldering wire takes CO2 or a gas mixture with volume percentage ratio of 80% Ar and 20% CO2 as the protective gas, the gas-shielded overlaying flux cored soldering wire has the advantages of great soldering technique, stable electric arc, less splash, easy deslagging, good crack resistance, great high-temperature hardness and thermal fatigue resistance, continuous soldering and improvement on production efficiency.

Description

technical field [0001] The invention belongs to welding material preparation technology, in particular to a gas-shielded surfacing flux-cored welding wire for repairing hot forging dies. Background technique [0002] After the hot forging die is used thousands of times, the mold cavity must be repaired. The repaired mold can reach or even exceed the service life before the repair. At present, surfacing welding electrodes are mainly used for repairing hot forging dies in China, and the efficiency is low. The use of flux-cored wire repair can realize continuous welding and improve production efficiency. The welding slag of flux-cored wire is far less than that of welding rod, which improves the deposition rate and reduces the workload of slag removal. Contents of the invention [0003] The purpose of the present invention is to address the above existing problems, to provide a gas-shielded surfacing flux-cored welding wire for hot forging mold repair, using the gas-shield...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B23K35/30B23K9/04B23K9/16
Inventor 张健
Owner TIANJIN YONGCHANG WELDING WIRES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap