Method for preparing CNT/Fe3O4@ZnO one-dimensional nanocomposite by polyol one-pot method

A nanocomposite material and technology of composite materials, which are applied in the field of preparation of CNT/Fe3O4@ZnO one-dimensional nanocomposite materials, can solve the problem of no photocatalysis, and achieve the effects of being difficult to agglomerate, saving resources, and being easy to operate.

Inactive Publication Date: 2011-06-15
HARBIN INST OF TECH
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Existing CNT / Fe 3 o 4 There are only magnetic properties, no optical properties such as photocatalysis

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing CNT/Fe3O4@ZnO one-dimensional nanocomposite by polyol one-pot method
  • Method for preparing CNT/Fe3O4@ZnO one-dimensional nanocomposite by polyol one-pot method
  • Method for preparing CNT/Fe3O4@ZnO one-dimensional nanocomposite by polyol one-pot method

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0008] Specific implementation mode 1: In this implementation mode, polyalcohol one-pot method prepares CNT / Fe 3 o 4 The method of @ZnO one-dimensional nanocomposite material is carried out according to the following steps: 1. Weigh 100mg multi-walled carbon nanotubes (one-dimensional matrix), 100-400mg iron acetylacetonate (precursor) and 25ml triethylene glycol (solvent) ) after mixing, then ultrasonically disperse until uniform, then pass in argon gas, then heat to the boiling point of triethylene glycol and reflux for 30-60min; The boiling point of triethylene glycol, reflux for 30-60min, magnetically separate after cooling, wash with ethanol 4 times, and dry to obtain CNT / Fe 3 o 4 @ZnO composites.

specific Embodiment approach 2

[0009] Embodiment 2: This embodiment differs from Embodiment 1 in that the frequency of ultrasonic dispersion in Step 1 is 80 KHz.

specific Embodiment approach 3

[0010] Embodiment 3: This embodiment is different from Embodiment 1 in that: the heating rate in step 2 is 5° C. / min).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for preparing a CNT / Fe3O4@ZnO one-dimensional nanocomposite by a polyol one-pot method. The method comprises the following steps: 1, weighing and then mixing a multiwall nanotube, ferric acetylacetonate and triethylene glycol, then carrying out ultrasonic dispersion on the mixture until the mixture is uniform, then introducing argon, then heating the mixture to the boiling point of triethylene glycol and then carrying out reflux; and 2, then cooling the product to the room temperature, then throwing zinc acetate, then slowing heating the mixture to the boiling point of triethylene glycol, then carrying out reflux, carrying out magnetic separation after cooling, washing the product with ethanol and drying the product to obtain the CNT / Fe3O4@ZnO composite. The composite is applied in the fields of photoelectric device assembly and photocatalysis.

Description

technical field [0001] The present invention relates to a kind of CNT / Fe 3 o 4 Preparation methods of @ZnO one-dimensional nanocomposites. Background technique [0002] Carbon nanotubes (CNTs) have excellent mechanical, thermal, electrical properties and one-dimensional nanostructures, and have broad application prospects in nanoelectronic devices, reinforced composite materials, hydrogen storage materials, biomedicine, and catalysis. Ferroferric oxide nanoparticles have excellent magnetic properties and good biocompatibility, and can be used in fields such as magnetic fluids, targeted drug delivery, cancer hyperthermia, magnetic resonance imaging, and magnetic recovery carriers. At present, some researchers have assembled Fe on CNT 3 o 4 Nanoparticles endow CNTs with good magnetic responsiveness, and prepare them into magnetorheological fluids, electrode materials, targeted drug carriers, etc. [0003] Existing CNT / Fe 3 o 4 There are only magnetic properties and no o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/80H01F1/01
Inventor 隋解和李静蔡伟
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap