Coated member

A covering component and surface covering technology, which is applied in the directions of drilling tool accessories, sputtering coating, tool holder accessories, etc., can solve the problems that the covering tools cannot meet the processing requirements, etc., and achieve excellent adhesion, excellent oxidation resistance, and tools The effect of life extension

Active Publication Date: 2011-06-15
TUNGALOY CORP
View PDF1 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As a result, previous covering tools became unsuitable for these demanding machining requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coated member
  • Coated member
  • Coated member

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] As a base material, a K20-equivalent cemented carbide insert having a shape of SDKN1203AETN was prepared. Regarding the invention, as a target of the AlP apparatus, a target having the composition ratios of metal elements and additive elements shown in Tables 1 and 2 was installed in the AlP apparatus. Load the substrate in the AlP device, heat the substrate temperature to 600°C through the heater, and introduce Ar and N into the AlP device after bombarding the substrate with Ar gas 2 The mixed gas, the pressure is adjusted to 4 ~ 5Pa, the DC bias voltage: -600 ~ -800V, arc discharge current: 100A on the substrate is pre-discharged for 2 ~ 3 minutes. After the pre-discharge is over, keep the arc discharge current, substrate temperature and pressure constant, and slowly adjust the DC bias voltage of the substrate from -600 to -800V to -80 to -120V after 2 minutes. Next, discharge for 100 to 140 minutes in the case of a single-layer film under the conditions of DC bias v...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a coated member for cutting tools which renders a long life possible under severe cutting conditions as in high-speed processing, high-feed-rate processing, cutting of works having enhanced hardness, and cutting of works difficult to cut. The coated member comprises a base having a surface coated with one or more coating films. At least one of the coating films is a hard film of a cubic metallic compound comprising at least one metallic element (M) selected from Al, Si, Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, and W and at least one element (X) selected from C, N, and O. In the pole figure for the (111) plane of the hard film, the X-ray intensity distribution in the alpha axis has a maximum intensity in the alpha-angle range of 75-90 DEG. In the pole figure for the (220) plane of the hard film, the X-ray intensity distribution in the alpha axis has a maximum intensity in the alpha-angle range of 75-90 DEG .

Description

technical field [0001] The present invention relates to a covering member for covering the surface of a substrate such as a sintered alloy, ceramics, cBN sintered body, or diamond sintered body with a film. In particular, it relates to a covering member suitable for cutting tools represented by inserts, drills, and end mills, various wear-resistant tools, and various wear-resistant parts. Background technique [0002] Covering members covered with coatings such as TiC, TiCN, TiN, (Ti, Al)N, CrN, etc. on the surface of substrates such as sintered alloys, ceramics, cBN sintered bodies, and diamond sintered bodies have the advantages of high strength, high toughness and The film has excellent wear resistance, oxidation resistance, lubricity, and welding resistance, so it is often used as a cutting tool, wear-resistant tool, and wear-resistant parts. [0003] As the prior art of coatings, there is a hard coating for cutting tools composed of (Ti, Al, Cr)(C, N) (for example, ref...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23B27/14B23B51/00B23C5/16C23C14/06
CPCC23C14/325C23C14/022C23C14/0641Y10T428/2495Y10T428/265B23B27/14B23B51/00B23C5/16C23C14/06
Inventor 陈路木幡护
Owner TUNGALOY CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com