Nylon composite material for wire and cable sheaths

A nylon composite material, wire and cable technology, applied in the direction of insulated cables, cables, circuits, etc., can solve the problems of anti-termite, rodent-proof agent, high toxicity, unable to prevent rat teeth, human and environmental poisoning, etc., and achieve excellent anti-termite prevention. , low cost, good corrosion resistance

Inactive Publication Date: 2011-07-06
马艳荣
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above method has achieved a certain effect, but due to the high toxicity of the ant-proof and rodent-proof agents, it will cause poison and pollution to the human body and the environment, and cannot prevent the teeth of the mice from biting, and cannot fundamentally solve the problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of wire and cable sheath nylon composite material, its composition and the mass content of each component are as follows:

[0024] Nylon 90%,

[0025] Antioxidant 0.1%,

[0026] Release agent 5%,

[0027] Light stabilizer 0.1%,

[0028] Tackifier 4.8%;

[0029] The nylon is a long-chain nylon PA6; the antioxidant is an aromatic amine antioxidant diphenylamine; the release agent is selected from siloxane; the light stabilizer is a light-shielding light stabilizer carbon black, The tackifier is a PET tackifier.

[0030] The preparation method of the above-mentioned wire and cable sheath nylon composite material comprises the following steps:

[0031] Step A: Weigh each component according to the formula and mix evenly;

[0032] Step B: Add the mixture obtained in Step A into a high-speed mixer and mix for 5 minutes to obtain a blended material; the obtained blended material is added to a twin-screw extruder, and after mixing, melt extrusion at a temperature o...

Embodiment 2

[0035] A kind of wire and cable sheath nylon composite material, its composition and the mass content of each component are as follows:

[0036] Nylon 85%,

[0037] Antioxidant 2%,

[0038] Release agent 8%,

[0039] Light stabilizer 2.5%,

[0040] Tackifier 2.5%;

[0041] The nylon is a mixture of long-chain nylon PA11 and PA12; the antioxidant is a mixture of aromatic amine antioxidant diphenylamine and p-phenylenediamine and dihydroquinoline; the mold release agent is selected from metal stearin The mixture of salt and polyvinyl alcohol; the light stabilizer is a light-shielding light stabilizer zinc oxide, and the tackifier is a tackifier.

[0042] The preparation method of the above-mentioned wire and cable sheath nylon composite material comprises the following steps:

[0043] Step A: Weigh each component according to the formula and mix evenly;

[0044] Step B: Add the mixture obtained in Step A into a high-speed mixer and mix for 10 minutes to obtain a blended ma...

Embodiment 3

[0047] A kind of wire and cable sheath nylon composite material, its composition and the mass content of each component are as follows:

[0048] Nylon 80%,

[0049] Antioxidant 2%,

[0050] Release agent 8%,

[0051] Light stabilizer 5%,

[0052] Tackifier 5%;

[0053] The nylon is a mixture of long-chain nylon PA6 and PA12; the antioxidant is an aromatic amine antioxidant 4,4'-thiobis(6-tert-butyl-3-methylphenol; the mold release The agent is selected from a mixture of polyolefin and polyvinyl alcohol; the light stabilizer is a mixture of light-shielding light stabilizer titanium dioxide and barium zinc, and the tackifier is a PET tackifier.

[0054] The preparation method of the above-mentioned wire and cable sheath nylon composite material comprises the following steps:

[0055] Step A: Weigh each component according to the formula and mix evenly;

[0056] Step B: Add the mixture obtained in Step A into a high-speed mixer and mix for 8 minutes to obtain a blended mate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a nylon composite material for wire and cable sheaths. The nylon composite material for wire and cable sheaths is characterized in that the nylon composite material comprises the following components by mass percentage: 80-90 percent of nylon, 0-2 percent of antioxidant, 0-8 percent of mold release agent, 0-5 percent of light stabilizer and 0-5 percent of viscosity increaser; nylon is long-chain nylon; the antioxidant is aromatic amine type antioxidant; the mold release agent is selected from siloxane, metallic stearate, polyvinyl alcohol, fluorine-containing oligomer, polyolefine or a mixture thereof; the light stabilizer is light-shield type light stabilizer; and the viscosity increaser is polyethylene terephthalate (PET) viscosity increaser. The wire and cable sheaths manufactured by the nylon composite material are environment-friendly, non-toxic and durable, and not only have the excellent anti-rat and anti-termite properties, but also have good physical mechanical properties.

Description

technical field [0001] The invention relates to the technical field of electric wires and cables, in particular to a nylon composite material for electric wires and cables. Background technique [0002] For a long time, anti-termite, anti-mouse, wear-resistant and corrosion-resistant are the main problems faced by wire and cable sheaths. For this reason, people add special anti-termite and anti-rodent agents into the cable sheath material to repel or reduce their taste sensitivity, thereby reducing the degree of being bitten by teeth. Or take measures such as adding armored structure or using cables with large outer diameters to achieve the purpose of avoiding rats. The above method has achieved certain effects, but due to the high toxicity of the ant-proof and rodent-proof agents, it will cause poisoning and pollution to the human body and the environment, and cannot prevent the teeth of the mice from biting, and cannot fundamentally solve the problem. Contents of the in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08L77/06C08K13/02C08K5/18C08K3/04C08K5/3437C08K3/22H01B7/17
Inventor 马艳荣
Owner 马艳荣
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com