Paper-making environmentally-friendly mineral deinking agent
A kind of green environmental protection, deinking agent technology, applied in the field of papermaking auxiliaries, to achieve the effect that the mitigation ratio cannot be greatly increased, the removal effect is good, and the deinking production efficiency and economic benefits are improved
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0034] Mix and heat 0.8 tons of tallow fatty acid and 1.4 tons of stearic acid at 70°C-75°C to a molten fluid state, stir at a speed of 120r / min for 20-30min, and slowly spray 2.2 tons of talcum powder on the molten mixed sample , increase the rotation speed to 150r / min, mix the talc powder and the mixed sample at 70°C-75°C for 30min, add 0.8 tons of polyoxyethylene 12-methyl stearyl ether, and react for 1h. The temperature of the above mixed liquid was raised to 85°C, and then 0.2 tons of polyoxyethylene oleate, 0.05 tons of polyether L61 and 0.2 tons of sodium chloride were added to the mixed sample, stirred and reacted for 30 minutes to obtain a green and environment-friendly mineral deinking agent.
Embodiment 2
[0036] Mix and heat 0.8 tons of tallow fatty acid and 1.2 tons of stearic acid at 70°C-75°C to a molten fluid state, stir at a speed of 120r / min for 20-30min, and slowly spray 2.0 tons of saponite powder on the molten mixed sample , increase the rotation speed to 150r / min, mix the soapstone powder and the mixed sample at 70°C-75°C for 30min, add 1.2 tons of polyoxyethylene 12-methyl stearyl ether, and react for 1h. The temperature of the above mixed liquid was raised to 85°C, and then 0.2 tons of polyoxyethylene oleate, 0.05 tons of polyether L62 and 0.2 tons of sodium sulfate were added to the mixed sample, stirred and fully reacted for 30 minutes to obtain a green and environment-friendly mineral deinking agent.
Embodiment 3
[0038]Mix 0.8 tons of palm oil fatty acid and 1.0 tons of stearic acid at 70°C-75°C and heat it to a molten fluid state, stir at a speed of 120r / min for 20-30min, and slowly spray 1.8 tons of kaolin on the molten mixed sample, lift Rotate to 150r / min, mix the kaolin and the mixed sample at 70°C-75°C for 30min, add 1.6 tons of polyoxyethylene 12-ethyl stearyl ether, and react for 1h. The temperature of the above mixed solution was raised to 85°C, and then 0.2 tons of polyoxyethylene ether oleate, 0.05 tons of polyether L61 and 0.2 tons of sodium chloride were added to the mixed sample, stirred and fully reacted for 30 minutes to obtain a green and environmentally friendly mineral deinking agent.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com