Wood plastic composite plate capable of adsorbing toxic gas, and preparation method thereof

A wood-plastic composite material and toxic gas technology, applied in the field of wood-plastic composite materials, can solve the problems of high density and high price, and achieve the effects of low density, low cost and low production cost

Active Publication Date: 2011-11-02
扬州润友复合材料有限公司
View PDF6 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But there are also some obvious deficiencies, such as high density, high price, etc., so its scope of use has been greatly limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Polyvinyl chloride plastic particles 100, modified wood powder (100 mesh 35,

[0040] Nano magnesium oxide (30nm) 4, activated carbon (0.4mm) 1.5,

[0041] Azodicarbonamide 0.6, complex blowing aid 2.5,

[0042] Acrylic 7, heat stabilizer 6,

[0043] Chlorinated polyethylene 3, UV absorber (UV531) 0.15,

[0044] (1) Mix the silane coupling agent and water uniformly in a weight ratio of 1:3, wherein water is the solvent;

[0045] (2) Mix the wood flour and the diluted silane coupling agent uniformly in a weight ratio of 100:4, and dry in vacuum for 4.5 hours at 60° C. to make modified wood flour;

[0046] (3) take each raw material by formula quantity;

[0047] (4) Put polyvinyl chloride plastic particles, nano-magnesia, activated carbon, and heat stabilizer in a mechanical stirring tank and stir for 5 minutes, then extrude and granulate, and the granulation extrusion temperature is 160°C-180°C to obtain a modified Plastic particles;

[0048] (5) Place the above-me...

Embodiment 2

[0051] Polyvinyl chloride plastic particles 100, modified wood flour (80 mesh) 30,

[0052] Nano magnesium oxide (20nm) 3, activated carbon (0.2mm) 1,

[0053] Azodicarbonamide 0.4, complex blowing aid 1.5,

[0054] Acrylic 6, Heat Stabilizer 4,

[0055] Chlorinated polyethylene 2, UV absorber (L770) 0.1,

[0056] (1) Mix the silane coupling agent and water uniformly in a weight ratio of 1:1, wherein water is the solvent;

[0057] (2) Mix the wood flour and the diluted silane coupling agent uniformly in a weight ratio of 100:2, and dry in vacuum for 3 hours at 40° C. to make modified wood flour;

[0058] (3) take each raw material by formula quantity;

[0059] (4) Put polyvinyl chloride plastic particles, nano-magnesia, activated carbon, and heat stabilizer in a mechanical stirring tank and stir for 4 minutes, then extrude and granulate, and the granulation extrusion temperature is 160°C-175°C to obtain a modified Plastic particles;

[0060] (5) Place the above-mentioned m...

Embodiment 3

[0063] Polyvinyl chloride plastic particles 100, modified wood powder (120 mesh) 40,

[0064] Nano magnesium oxide (40nm) 5, activated carbon (0.6mm) 2,

[0065] Azodicarbonamide 0.8, complex blowing aid 3.5,

[0066] Acrylic 8, heat stabilizer 8,

[0067] Chlorinated polyethylene 4, UV absorber (UV531) 0.2,

[0068] (1) Mix the silane coupling agent and water uniformly in a weight ratio of 1:5, wherein water is the solvent;

[0069] (2) Mix the wood flour and the diluted silane coupling agent uniformly in a weight ratio of 100:6, and dry in vacuum for 6 hours at 80° C. to make modified wood flour;

[0070] (3) take each raw material by formula quantity;

[0071] (4) Put polyvinyl chloride plastic particles, nano-magnesia, activated carbon, and heat stabilizer in a mechanical stirring tank and stir for 6 minutes, then extrude and granulate. The granulation extrusion temperature is 165°C-180°C to obtain a modified Plastic particles;

[0072] (5) Place the above-mentioned ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a wood plastic composite material, in particular to a wood plastic composite plate capable of adsorbing toxic gas, and a preparation method thereof. The wood plastic composite plate is characterized by: adopting silane coupling agent modified wood flour as a raw material, mixing polyvinyl chloride, nano-magnesium oxide, active carbon and a heat stabilizer through stirringto obtain modified plastic particles; uniformly stirring the modified plastic particles, the modified wood flour, azobisformamide, a composite foaming agent, acrylic acid, chlorinated polyethylene and a ultraviolet absorber, followed by extruding, foaming and forming to obtain the wood plastic composite plate. The preparation method for the wood plastic composite plate is convenient. Compared to a common plastic plate, a gypsum board, a aluminum buckle plate and other wood plastic materials, the wood plastic composite plate provided by the present invention has characteristics of low density,light weight, high impact strength, low cost and toxic gas adsorbing, and can be made into a plurality of products such as photo frame, picture frame, ground pin line and the like, and can be widely applicable for a plurality of situations such as auditoriums and hotels, homes, office buildings, and the like.

Description

technical field [0001] The invention relates to a wood-plastic composite material, in particular to a wood-plastic composite material plate capable of absorbing toxic gas and a preparation method thereof. Background technique [0002] In recent years, with the enhancement of people's awareness of environmental protection, wood-plastic composite materials with a wide range of raw materials, environmental friendliness, renewable and recyclable use have attracted more and more attention, and their application fields have continued to expand, such as automotive interiors, composite pipes , Railway sleepers, car box boards, cable protection pipes, manhole covers, car parts, pallets, packing boxes, planks, beams, open-air tables and chairs, benches, etc. Wood-plastic profiles can be handled with general woodworking techniques, can be cut with a circular saw, and fixed with nails or screws, and the nail-holding force is significantly better than other synthetic materials, and the m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L97/02C08L23/28C08K13/02C08K3/22C08K3/04C08K5/09C08J9/10B29C47/92B29C48/92
CPCB29C48/04B29C48/92B29C2948/92704B29C2948/92895B29C2948/92904
Inventor 徐致伟徐电友李浩宇雷文
Owner 扬州润友复合材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com