A kind of preparation method of porous foamed iron-nickel-chromium alloy material

An iron-nickel-chromium alloy and porous foam technology is applied in the field of preparation of porous foamed iron-nickel-chromium alloy materials, and can solve unreasonable process flow and process parameters, low thickness of porous foam alloy materials, high temperature resistance, poor corrosion resistance, etc. problems, to achieve the effect of easy quality control, excellent corrosion resistance, and high temperature resistance

Inactive Publication Date: 2011-12-14
JILIN ZHUOER TECH
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The disadvantage of the existing electrodeposition method related to the preparation method of the present invention is that the selected process flow and process parameters are unreasonable, the thickness of the prepared porous foam alloy material is low, usually below 5mm, and the porosity is low, usually at 80-90%, poor high temperature resistance and corrosion resistance, cannot meet the requirements of high temperature resistance, corrosion resistance and other harsh working conditions, and the preparation cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0020] A kind of preparation method of porous foamed iron-nickel-chromium alloy material of the present invention comprises the following steps:

[0021] 1) Choose one of polyurethane through-hole three-dimensional network foam sponge, polyether through-hole three-dimensional network foam sponge, fiber mesh or non-woven porous material, with a thickness of 5-100mm and the number of holes per inch PPi is 5-130 between

[0022] 2) The porous material described in step 1) is impregnated with a water-based polymer adhesive at room temperature, and the water-based polymer adhesive is isocyanate;

[0023] 3) Use powder spraying equipment to evenly spray 5-10 nanometer chromium powder on the surface of the porous material where the isocyanate is impregnated in step 2) under the wind pressure of 0.8MPa and the powder feeding rate of 3kg / h;

[0024] 4) Dry the porous material sprayed with chromium powder in step 3) with a mesh-belt electric furnace at a drying temperature of 80-100°C ...

Embodiment 1

[0032] Embodiment 1: a kind of preparation method of porous foamed iron-nickel-chromium alloy material comprises the following steps:

[0033] 1) Use fiber mesh with a thickness of 5mm and PPi of 5 holes per inch;

[0034] 2) impregnating the porous material described in step 1) with isocyanate at room temperature;

[0035] 3) Using powder spraying equipment, under the wind pressure of 0.8MPa and the powder feeding rate of 3kg / h, evenly spray 5nm chromium powder on the surface of the porous material impregnated with isocyanate in step 2);

[0036] 4) Dry the porous material sprayed with chromium powder in step 3) with a mesh-belt electric furnace at a drying temperature of 80°C and a mesh speed of 25m / h in the electric furnace;

[0037] 5) Put the porous material dried and sprayed with chromium powder in step 4) into a 230-mesh screen vibrator, vibrate the excess chromium powder, and separate the excess chromium powder from the porous material matrix;

[0038] 6) Dip the ch...

Embodiment 2

[0043] Embodiment 2: the preparation method of another kind of porous foamed iron-nickel-chromium alloy material comprises the following steps:

[0044] 1) Use polyurethane through-hole three-dimensional reticulated foam sponge with a thickness of 80mm and PPi of 100 holes per inch;

[0045] 2) impregnating the porous material described in step 1) with isocyanate at room temperature;

[0046] 3) Using powder spraying equipment, under the wind pressure of 0.8MPa and powder feeding rate of 3kg / h, evenly spray 8nm chromium powder on the surface of the porous material impregnated with isocyanate in step 2);

[0047] 4) Dry the porous material sprayed with chromium powder in step 3) with a mesh-belt electric furnace at a drying temperature of 90°C and a mesh speed of 25m / h in the electric furnace;

[0048] 5) Put the porous material dried and sprayed with chromium powder in step 4) into a 240-mesh screen vibrator, vibrate the excess chromium powder, and separate the excess chromium ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The present invention is a preparation method of a porous foamed iron-nickel-chromium alloy material, which is characterized in that: the steps include: selecting a porous material, immersing a water-based polymer adhesive at normal temperature; spraying nano-chromium powder evenly on the Immersion on the surface of porous material with water-based polymer adhesive; drying; separating excess chromium powder from porous material matrix; dip-coating conductive adhesive on chromium porous material; electrodepositing iron-nickel alloy after heating and curing treatment on chromium porous material ; Oxidation-reduction treatment; Carrying out secondary diffusion treatment of chromium to obtain porous foamed iron-nickel-chromium alloy material. Its preparation method is scientific, the selected process parameters are reasonable, the quality is easy to control, the cost is low, and it can be produced with light weight, large specific surface area, super thickness, thickness of 5-100mm, high porosity of 96-99.9%, high temperature resistance and corrosion resistance. Excellent, able to meet the requirements of high temperature resistance, corrosion resistance and other harsh working conditions. It is especially suitable as high-temperature filtration, chemical catalysis, carrier, burner gas distribution and high-temperature flame-retardant materials.

Description

technical field [0001] The invention relates to a preparation method of an alloy material, which is a preparation method of a porous foamed iron-nickel-chromium alloy material. Background technique [0002] Porous foam alloy material can be widely used in filtration, chemical industry, energy, vibration reduction, sound absorption, damping, heat insulation, heat dissipation and flame retardancy due to its small bulk density, large specific surface area, uniform structure, good mechanical properties and processing performance. field. Especially with the continuous development of science and technology, the dependence on porous foam alloy materials has been further used in harsh working conditions such as high temperature resistance and corrosion resistance. [0003] There are many kinds of preparation methods for existing porous foam alloy materials, which are classified according to the state of the metal to be processed: 1. The method based on metal melt; 2. The method bas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22B1/08
Inventor 辛长军边树华
Owner JILIN ZHUOER TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com