A kind of polyethylene stone composite wallpaper and its manufacturing process

A production process and technology of polyethylene stone powder, applied in special paper, synthetic resin layered products, paper and other directions, can solve the problems of low efficiency, not suitable for large-scale industrial production, no flame retardant performance, complex preparation process, etc. To achieve the effect of excellent decorative effect, enhanced physical and mechanical properties and dimensional stability, and simple production process

Inactive Publication Date: 2011-12-21
夏丽蓉
View PDF2 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In recent years, synthetic wallpapers that combine polymer materials with inorganic stone materials have also appeared, but there are still many problems in this kind of wallpapers, such as low strength, variability, unstable size, poor adhesion, and no flame retardancy, etc.
In addition, the preparation process of this type of wallpaper is complicated, difficult to operate, high in production cost, low in efficiency and not suitable for large-scale industrial production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] Weigh the following masterbatch components in mass percentage and components in the auxiliary agent: polyethylene: 25%, CaCO3: 51%, talcum powder: 20%; the auxiliary agent is composed of the following components in mass percentage: titanium Ester coupling agent: 1%, polyethylene glycol: 1%, magnesium hydroxide: 0.7%, azodicarbonamide: 0.3%, polypropylene-maleic anhydride graft copolymer: 1%, dry in vacuum Dry in the box for 24 hours, and the drying temperature is set to 100°C. According to the manufacturing process steps of the present invention, the temperature of the heat mixing is set to 100°C. During calendering, the temperature of the calender is set to 200°C, and the speed of the calender roller is 90m / min, the thickness of the polyethylene stone paper layer obtained after calendering is 2mm, and the temperature of the laminating machine is set at 150°C during the laminating process to obtain a synthetic wallpaper with a total thickness of 2.2mm.

Embodiment 2

[0053] Weigh the following masterbatch components and additives in mass percentage: polyethylene: 20%, CaCO3: 70%, talcum powder: 7%; additives are composed of the following components in mass percentage: titanium Ester coupling agent: 0.8%, polyethylene glycol: 1%, magnesium hydroxide: 0.5%, azodicarbonamide: 0.1%, polypropylene-maleic anhydride graft copolymer: 0.6%, dry in vacuum Dried in the box for 24 hours, and the drying temperature was set to 100°C. According to the manufacturing process steps of the present invention, the temperature of the heat mixing was set to 110°C. During calendering, the temperature of the calender was set to 210°C, and the speed of the calender rollers was 50m / min, the thickness of the polyethylene stone paper layer obtained after calendering is 3mm, the temperature of the laminating machine is set at 160°C during the lamination process, and a synthetic wallpaper with a total thickness of 3.1mm is obtained.

Embodiment 3

[0055] Weigh the following masterbatch components in mass percentage and components in the auxiliary agent: polyethylene: 20%, CaCO3: 50%, talcum powder: 25%; the auxiliary agent is composed of the following components in mass percentage: titanium Ester coupling agent: 1%, polyethylene glycol: 1%, magnesium hydroxide: 1%, azodicarbonamide: 1%, polypropylene-maleic anhydride graft copolymer: 1%, dry in vacuum Dry in the box for 24 hours, and the drying temperature is set to 100°C. According to the manufacturing process steps of the present invention, the temperature of the heat mixing is set to 100°C. During calendering, the temperature of the calender is set to 200°C, and the speed of the calender roller is 90m / min, the thickness of the polyethylene stone paper layer obtained after calendering is 1mm, and the temperature of the laminating machine is set at 150°C during the lamination process to obtain a synthetic wallpaper with a total thickness of 1.2mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a wallpaper and its technology, in particular to a polyethylene stone composite composite wallpaper and its manufacturing technology. Polyethylene stone synthetic wallpaper, which includes a mesh roving layer and a polyethylene stone powder polymer material layer; the polyethylene stone powder polymer material layer is composed of a masterbatch and an auxiliary agent, wherein the masterbatch is composed of the following components in mass percent: Polyethylene: 20-25%, CaCO3: 50-70%, talcum powder: 7-25%; additives are composed of the following components in mass percentage: composite coupling agent: 0.5-1%, dispersant: 0.5-1%, flame retardant: 0.5-1%, micro foaming agent: 0.1-1%, compatibilizer: 0.5-1%. The polyethylene stone composite wallpaper of the present invention has high strength, strong adhesion and flame retardant function. The manufacturing process adopted by the present invention has the advantages of simple process, low cost and high efficiency, and is suitable for large-scale industrial production.

Description

[0001] technical field [0002] The invention relates to a wallpaper and its technology, in particular to a polyethylene stone composite composite wallpaper and its manufacturing technology. Background technique [0003] Paper is one of China's four great inventions. The raw materials of traditional paper are mainly plant fibers such as wood. With the introduction of the national forest protection policy and the implementation of the ban on logging, the raw materials for papermaking can only be maintained by imported wood pulp. The traditional paper production process produces a large amount of waste water and other three wastes, which seriously pollutes the environment and is extremely difficult to treat. Traditional paper is not resistant to moisture and corrosion. Various physical and mechanical properties and dimensional stability are poor, which can no longer meet the special requirements of many paper fields. Paper production and development require innovation. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D21H27/20D21H27/38C08L23/06C08K13/02C08K3/26C08K3/34E04F13/075B32B3/12B32B27/12B32B27/32B32B27/18
Inventor 夏丽蓉夏开邦
Owner 夏丽蓉
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap