Phthalaznone-containing poly(aryl ether nitrile) end-capped with maleimide and preparation method thereof

A technology of xinthone biphenyl and maleimide, which is applied in polyether coatings, polyether adhesives, adhesive types, etc., and can solve unseen problems

Active Publication Date: 2012-01-04
DALIAN UNIV OF TECH
View PDF4 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The maleimide-terminated polyarylether nitrile containing phthalazinone biphenyl structure and its preparation method have not been found in relevant patent technical reports, nor have they appeared in domestic and foreign publications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phthalaznone-containing poly(aryl ether nitrile) end-capped with maleimide and preparation method thereof
  • Phthalaznone-containing poly(aryl ether nitrile) end-capped with maleimide and preparation method thereof
  • Phthalaznone-containing poly(aryl ether nitrile) end-capped with maleimide and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Example 1 Maleimide-terminated polyarylether nitrile resin containing phthalazinone biphenyl structure

[0035] Add 1 part of 4-(4-hydroxy-phenyl)-2H-phthalazin-1-one, 1.25 parts of Anhydrous potassium carbonate, 1.02 parts of 2,6-dichlorobenzonitrile, toluene and dimethyl sulfoxide, under a nitrogen atmosphere, react at 140°C for 4 hours, carry out toluene with water, and distill the toluene, heat up to 160°C to continue React for 6 hours. Then, the dimethyl sulfoxide solution of aminophenol is added dropwise into the reaction system through a constant-pressure feeding funnel, and a certain amount of toluene is added at the same time to bring water. The toluene was refluxed with water for 3 hours and the toluene was distilled off, and the temperature was raised to 160° C. to continue the reaction for 2 hours. After the reaction is finished, the reaction solution is poured into boiling water, washed with water, filtered and dried to obtain an amino-terminated polyaryl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a phthalaznone-containing poly(aryl ether nitrile) end-capped with maleimide and a preparation method thereof. Self-made 4-[4-(4-carboxyl phenoxyl) phenyl) -2-(4-carboxyl phenyl) naphthyridine-1-ketone or derivative thereof and 2, 6-dichlorobenzonitrile are used as polycondensation monomers. Meanwhile, other bisphenol and aromatic bi-halogen monomers can be added, p-aminophenol is used as an end-capping agent, and a solvent, a co-boiling dewatering agent and a catalyst are added for carrying out progressive polymerization reaction and synthesizing a phthalaznone-containing poly(aryl ether nitrile) resin end-capped with amino. On the basis, a phthalaznone-containing poly(aryl ether nitrile) polymer end-capped with amino, maleic anhydride, p-toluenesulfonic acid, a polymerization inhibitor, the solvent and the co-boiling dewatering agent are used as raw materials to prepare a phthalaznone-containing poly(aryl ether nitrile) resin end-capped with maleimide. The poly(aryl ether nitrile) resin can be co-cured with bis-maleimide or an epoxy resin, can be used in the fields of thermostable paint, coatings, adhesives, composite materials and the like and has broad application prospects.

Description

technical field [0001] The invention belongs to the field of polymer material synthesis, and in particular relates to a maleimide-terminated polyarylether nitrile containing a phthalazinone biphenyl structure and a preparation method thereof. Background technique [0002] Bismaleimide resin (Bismaleimide, referred to as BMI) is a bifunctional compound with maleimide (MI) as the active terminal group. BMI has the characteristics of excellent heat resistance, electrical insulation, radiation resistance, flame retardancy, good mechanical properties and dimensional stability, and is widely used in aviation, aerospace, machinery, electronics, resin matrix of advanced composite materials, resistance High temperature insulation materials and adhesives, etc. The bismaleimide resin monomer can be self-polymerized under thermal catalysis, and undergoes cross-linking reaction to form a highly cross-linked network. However, after the bismaleimide resin is cured, the crosslinking densi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G65/48C08G65/40C09D171/10C09J171/10C08L71/10
Inventor 蹇锡高刘程张守海王锦艳
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap