Calcium sulfate whisker modified polyphenylene sulfide composite material and preparation method thereof

A technology of calcium sulfate whiskers and polyphenylene sulfide, which is applied in the field of polyphenylene sulfide composite materials and its preparation technology, can solve the problems of reducing the thermal physical properties of PPS, restricting the application of PPS, etc., and achieves excellent thermal physical properties and low cost. , good insulation and thermal conductivity

Active Publication Date: 2012-01-11
XIANGFU NEW BUILDING MATERIAL HUNAN
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The existing technology improves the thermal conductivity of PPS, but re

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Calcium sulfate whisker modified polyphenylene sulfide composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The calcium sulfate whisker modified polyphenylene sulfide composite material in this example is made of the following raw materials in parts by weight: 48.5 parts of polyphenylene sulfide (PPS), 10 parts of calcium sulfate whisker with a diameter of 10-20 μm, and a diameter of 10 μm. - 35 parts of 300 μm thermal conductive filler magnesium oxide, 5 parts of silane coupling agent, 0.5 part of antioxidant 1010, 1 part of lubricant calcium stearate.

[0024] Preparation:

[0025] (1) Pretreatment of thermally conductive filler magnesium oxide: Add 35 parts by weight of thermally conductive filler magnesium oxide with a diameter of 10-300 μm into the high-speed mixer, then add 3 parts by weight of silane coupling agent, and mix for 10 minutes;

[0026] (2) Pretreatment of calcium sulfate whiskers: add 10 parts by weight of calcium sulfate whiskers with a diameter of 10-20 μm and 2 parts by weight of silane coupling agent into a high-speed mixer and mix for 10 minutes to ob...

Embodiment 2

[0033] The calcium sulfate whisker modified polyphenylene sulfide composite material in this example is made of the following raw materials in parts by weight: 43.5 parts of polyphenylene sulfide (PPS), 15 parts of calcium sulfate whiskers with a diameter of 10-20 μm, and a diameter of 10 μm. - 35 parts of thermally conductive filler alumina of 300 μm, 5 parts of titanate coupling agent, 0.5 part of antioxidant 1010, and 1 part of lubricant zinc stearate.

[0034] Preparation:

[0035] (1) Pretreatment of thermally conductive filler alumina: add 35 parts by weight of thermally conductive filler alumina with a diameter of 10-300 μm into the high-speed mixer, then add 3 parts by weight of titanate coupling agent, and mix for 10 minutes;

[0036] (2) Pretreatment of calcium sulfate whiskers: Add 15 parts by weight of calcium sulfate whiskers with a diameter of 10-20 μm and 2 parts by weight of titanate coupling agent into a high-speed mixer and mix for 10 minutes to obtain modifi...

Embodiment 3

[0043] The calcium sulfate whisker modified polyphenylene sulfide composite material in this example is made of the following raw materials in parts by weight: 38.5 parts of polyphenylene sulfide (PPS), 20 parts of calcium sulfate whiskers with a diameter of 10-20 μm, and a diameter of 10 μm. - 35 parts of thermal conductive filler aluminum nitride of 300 μm, 5 parts of aluminate coupling agent, 0.5 part of antioxidant 1010, 1 part of lubricant calcium stearate.

[0044] Preparation:

[0045] (1) Pretreatment of thermally conductive filler aluminum nitride: add 35 parts by weight of thermally conductive filler aluminum nitride with a diameter of 10-300 μm into the high-speed mixer, then add 3 parts by weight of aluminate coupling agent, and mix for 10 minutes;

[0046] (2) Pretreatment of calcium sulfate whiskers: Add 20 parts by weight of calcium sulfate whiskers with a diameter of 10-20 μm and 2 parts by weight of aluminate coupling agent into a high-speed mixer and mix for ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a calcium sulfate whisker modified polyphenylene sulfide composite material and a preparation method thereof. The composite material comprising the following components in parts by weight: polyphenylene sulfide 35-50 parts, calcium sulfate whisker 10-20 parts, thermal conductive filler 30-40 parts, coupling agent 2-5 parts, antioxidant1010 0.2-0.5 part and lubricant 0.5-1.5 parts. The preparation method of the calcium sulfate whisker modified polyphenylene sulfide composite material comprises the steps of: pre-processing the thermal conductive filler and the calcium sulfate; adding the pre-processed thermal conductive filler, the polyphenylene sulfide, the antioxidant1010 and the lubricant into a high-speed mixer, and mixing for 5-15 min; and then adding the modified calcium sulfate whisker and mixing for 4-6 min; pelletizing the obtained mixture by extruding; and carrying out injection molding on the pellets to obtain the finished product. The calcium sulfate whisker modified polyphenylene sulfide composite material provided by the invention has the advantages of good insulation and thermal conductivity and excellent thermal physical property and is particularly applicable to electronic products and weaponry, electrical communication, electrical equipment and instruments.

Description

technical field [0001] The invention relates to a polyphenylene sulfide composite material and a preparation process thereof, in particular to a calcium sulfate whisker-modified polyphenylene sulfide composite material and a preparation process thereof. Background technique [0002] Industrial production and the development of science and technology have put forward higher requirements for thermally conductive materials. In addition to thermal conductivity, materials are also required to have excellent comprehensive properties, such as light weight, easy processing and molding, excellent thermal fatigue performance, electrical insulation and chemical stability. good etc. Traditional heat conduction materials such as metals and metal oxides and other non-metallic materials have been unable to meet the heat conduction requirements of power tubes, integrated blocks, heat pipes, integrated circuits, and copper-clad laminates that are widely used in the field of electromagnetic s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L81/02C08K13/06C08K9/06C08K9/04C08K3/22C08K3/28C08K3/34C08K7/08B29B9/06B29C47/92B29C45/76B29C48/92
CPCB29C48/04
Inventor 刘珍如刘立文付桃梅杨志强宁勇鲁纪鸣
Owner XIANGFU NEW BUILDING MATERIAL HUNAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap