Water-based epoxy anti-corrosive coating and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of water-based epoxy and anti-corrosion coatings, applied in anti-corrosion coatings, epoxy resin coatings, fire-resistant coatings, etc., to achieve low flame spread, improve aging resistance, and limit the spread of flames
Active Publication Date: 2012-01-11
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF5 Cites 33 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] At present, there are few water-based paints used for the interior of the cabin. The primer is generally made of paint, while the top coat
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
example 1
[0033] Example one: A component (parts by weight):
[0034] Epoxy Emulsion 35
[0035] Fluorocarbon emulsion 10
[0036] distilled water 10
[0037] Wetting and dispersing agent 0.2
[0038] Defoamer I 0.3
[0039] Rutile titanium dioxide 7
[0040] Complex Zinc Phosphate 2
[0041] Iron titanium powder 2
[0042] Talc powder 2
[0043] Precipitated Barium Sulfate 8
[0044] Mica powder 6
[0045] Ultrafine Aluminum Hydroxide 10
[0046] Aluminum tripolyphosphate 10.5
[0047] Flash rust inhibitor 0.3
[0048] Thickener 0.5
[0049] Defoamer II 0.1
[0050] Substrate wetting agent 0.1
[0051] B component:
[0052] Waterborne epoxy curing agent 100
[0053] A: B = 100:12, the effective period of construction is 6 hours.
[0054] Process preparation method:
[0055] Add water, additive wetting and dispersing agent, defoamer I, defoamer II, and flash rust inhibitor into the stock pot in sequence, stir evenly at low speed, then add pigments and fillers, disperse...
example 2
[0057] Example two: A component (parts by weight):
[0058] Epoxy emulsion 40
[0059] Fluorocarbon emulsion 10
[0060] distilled water 5
[0061] Wetting and dispersing agent 0.2
[0062] Defoamer I 0.3
[0063] Rutile titanium dioxide 5
[0064] Complex Zinc Phosphate 5
[0065] Iron titanium powder 5
[0066] Talc powder 2
[0067] Precipitated Barium Sulfate 5
[0068] Mica powder 3
[0069] Superfine Aluminum Hydroxide 12
[0070] Aluminum tripolyphosphate 5.5
[0071] Flash rust inhibitor 0.3
[0072] Thickener 0.5
[0073] Defoamer II 0.1
[0074] Substrate wetting agent 0.1
[0075] B component:
[0076] Waterborne epoxy curing agent 100
[0077] A: B = 100:13, the effective period of construction is 6 hours.
[0078] Process preparation method:
[0079] Add water, additive wetting and dispersing agent, defoamer I, defoamer II, and flash rust inhibitor into the stock pot in sequence, stir evenly at low speed, then add pigments and fillers, disperse at ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a water-based epoxy anti-corrosive coating and a preparation method thereof, and relates to a ship antirust and cabin inside and outside antirust fireproof paint. The invention provides a water-based epoxy coating with the VOC lower than 10g/l, and the coating belongs to an environment-friendly coating, which not only has the antirust performance of anti-corrosive coating,but also has low flame propagation of cabin inside finish paint, meets the requirement of cabin inside smoke and toxin, resists aging, and is a multifunctional water-based coating, and the bottom andthe surface are combined. Zhejiang Ampang AB-EP-20 is used as the epoxy resin, Zhejiang Ampang AD-HGF is used as the curing agent, and fluorocarbon emulsion (the model of which is Beijing Baowei PF-1) is used as the base material. Wetting dispersant, defoamer I, defoamer II, flash rust inhibitor, thickener, defoamer and substrate wetting agent are used as additives, rutile titanium white powder, compound zinc phosphate, ferrotitanium powder, talcum powder, ultra-fine aluminum hydroxide, precipitated barium sulfate, mica powder and aluminum tripolyphosphate are used as pigment fillers.
Description
technical field [0001] The invention relates to a water-based epoxy anti-corrosion coating and a preparation method thereof, belonging to the fields of metal protection and flame retardancy, and in particular to anti-rust and fire-proof paints for ships, interiors and exteriors of cabins. Background technique [0002] At present, most of the anti-corrosion coatings in my country's submarines and various ship cabins use traditional solvent-based coatings, which contain heavy metal compounds such as chromium or lead, which are highly toxic and cause great harm to the marine environment and human health. The research and development of environmentally friendly water-based cabin coatings has very important practical significance for eliminating the hidden dangers of fire and poisoning incidents during the construction of interior cabin coatings and improving the living environment of interior cabins. [0003] At present, there are few water-based paints used for the interior of ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more