Matte involucra coating adhesive for textile and preparation method thereof

A textile and coating glue technology, which is applied in textiles, papermaking, fiber processing, etc., can solve the problems of no public information, affect usability, and weak film feeling, etc., achieve good elasticity, increase stability, and soft vision effect of effect

Active Publication Date: 2012-06-13
LIAONING FIXED STAR FINE CHEM
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Such coating adhesives on the market have shortcomings such as yellowing, poor fastness, and weak film feeling, which directly affect the usability
At present, there is no public information on related technologies in terms of water-based fog surface film coating glue

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Matte involucra coating adhesive for textile and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] 1. Lotion synthesis;

[0032] Pre -breasts: In the pre -milk tank, mixes 128 grams of removal water, 2.5 grams of fatty alcohol polyoxyethylene ether, 1.8 grams of sodium dulate sulfate, mix and add 104 grams of acrylate while stirring, methane of acrylic, methacryal oscopylene26 grams of cinnamone, 1.9 grams of methyl acrylic-2-hydroxyl ester, 3.9 grams of N-hydroxymethylene acrylamide, 1.5 grams of dioma acrylic triathol, 34 grams of lyeylene, and 4.5 grams of acrylic.Emulsion;

[0033] Treatment of polymerization reactions: 0.48 grams of ammonium sulfate and 0.48 grams of sodium sodium sulfate are dissolved in 10 grams of derived ionic water, respectively in the drip kettle, and add 32 grams of exfoliating water to the reaction kettle.The 25%pre-emulsion is used as a seed emulsion, and 40%of the dotter solution is added to 45-50 ° C, the reaction is 30-40 minutes, the control temperature is 70-75 ° C, and then adds the remaining pre-emulsion.Cainting agent solution, the ...

Embodiment 2

[0037] 1. Lotion synthesis;

[0038] Pre -breasts: In the pre -milk tank, wearing 135 grams of removal water, 2.3 grams of fatty alcohol polyoxyethylene ether, sodium dulate sodium sulfate 1.6 grams are mixed with each other, 101 grams of acrylate is added while stirring28 grams of cinnamone, 2.0 grams of methyl acrylic-2-hydroxyl ester, 3.6 grams of N-hydroxymethylene acrylamide, 1.8 grams of dioma acrylic triathol, 33 grams of lyeylene, and 4.0 grams of acrylic.Emulsion;

[0039] Treatment of polymerization reactions: 0.43 grams of ammonium sulfate and 0.43 grams of sodium sodium sulfate are dissolved in 8 grams of derived ionic water, respectively in the drip kettle, and add 34 grams of exfoliating water to the reaction kettle.The 25%pre-emulsion is used as a seed emulsion, and 40%of the dotter solution is added to 45-50 ° C, the reaction is 30-40 minutes, the control temperature is 70-75 ° C, and then adds the remaining pre-emulsion.Cainting agent solution, the drip time is co...

Embodiment 3

[0043] 1. Lotion synthesis;

[0044]Pre -milk: In the pre -milk tank, the exfoliating water is 117 grams, the fattyol polyoxyethylene ether 2.4 grams, the sodium dulate sodium sulfate 2.0 grams is mixed with each other, and 105 grams of acrylic ethyl acrylic is added while stirringTwenty-grams of cinnamone, 1.8 grams of methyl acrylic-2-hydroxyl ester, 3.5 grams of N-hydroxymethylene acrylamide, 1.9 grams of dioma acrylic triathol, 34 grams of lyeylene, and 4.1 grams of acrylic, and 4.1 grams of acrylic.Emulsion;

[0045] Treatment of polymerization reactions: 0.41 grams of ammonium sulfate and 0.41 grams of sodium sodium sulfate are dissolved in 10 grams of derived ionic water, respectively in the drip kettle, and add 40 grams of exfoliating water to the reaction kettle.The 25%pre-emulsion is used as a seed emulsion, and 40%of the dotter solution is added to 45-50 ° C, the reaction is 30-40 minutes, the control temperature is 70-75 ° C, and then adds the remaining pre-emulsion.Ca...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a matte involucra coating adhesive for textile and a preparation method thereof. The matte involucra coating adhesive for textile is prepared from the following components in parts by weight: 2-2.5 parts of fatty alcohol-polyoxyethylene ether, 1.5-2 parts of sodium dodecyl sulfate, 100-105 parts of ethyl acrylate, 25-30 parts of iso-octyl methacrylate, 1.5-2 parts of 2-hydroxyethyl methacrylate, 3.5-4 parts of N-hydroxymethyl acrylamide, 1.5-2 parts of triethylene glycol dimethacrylate, 30-34 parts of styrene, 4-4.5 parts of acrylic acid, 0.4-0.5 part of ammonium persulfate, 0.4-0.5 part of sodium hydrosulfite, 270-340 parts of deionized water and a proper amount of ammonia water with weight percentage concentration of 20-22% by the steps of synthesizing into emulsion by pre-emulsification and initiated polymerization, and then adding 7-12 parts of thickener, 0.2-1.0 part of wetting dispersant and 10-50 parts of delustering agent. The product has mild gloss, soft handfeel, strong involucra feel and excellent firmness.

Description

Technical field [0001] The present invention involves fabric coating materials and preparation methods. It specially involves a water -based coating glue with a fog surface and strong cortex. It is used in textile coatings to make the fabric after the coating obtain the soft vision of the fog surfaceEffect, strong cortex, dry feel, at the same time have strong water resistance to washing the fastness. Background technique [0002] In recent years, consumers' aesthetic concepts have become increasingly inclined to leisure, fashion and personalization.The demand for low -gloss fabrics with a soft appearance has increased sharply, especially in the skin -sophisticated imitation leather fabric with fog -surface visual effects.While giving ordinary fabric fashion elements, it does not affect the comfort of wearing, and can greatly increase the added value of the fabric.The shortcomings such as yellow change, poor fastness, and poor cortex in the market have directly affected usability...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/29D06M11/79D06M15/227C08F220/18C08F220/28C08F220/58C08F222/20C08F212/08C08F220/06C08F2/30C08F2/26
Inventor 严欣宁杨青张迎春
Owner LIAONING FIXED STAR FINE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com